Compositions and methods to improve the setting properties and rub resistance of printing inks

ABSTRACT

Provided are high viscosity essentially non-aqueous dispersions containing acrylic core/shell polymer particles in a non-aqueous solvent; sheetfed, heatset and coldset lithographic ink compositions containing the dispersions; and methods of printing with ink containing the dispersions to improve the setting and drying properties and rub resistance of sheet fed offset, heatset and coldset lithographic inks. The lithographic inks containing the dispersions set quickly enough to allow processing of printed sheets soon after printing.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is the United States national phase filing of thecorresponding international application number PCT/US2011/060845, filedon Nov. 15, 2011, which claims priority to and benefit of U.S.Provisional Application No. 61/413,611, filed on Nov. 15, 2010, whichapplication is hereby incorporated by reference in their entirety.

Where permitted, the subject matter of the above-referenced applicationis incorporated by reference in its entirety.

FIELD OF THE INVENTION

Lithographic printing inks that allow processing of lithographic inkprinted sheets soon after printing are provided. The invention relatesto lithographic sheetfed printing inks containing a high viscosityessentially non-aqueous dispersion made of acrylic core/shell polymersin a non-aqueous organic solvent (NAD); heatset and coldset lithographicinks containing NAD; and to methods of printing with lithographic inkscontaining NAD to improve the setting and drying properties and rubresistance of sheetfed offset, heatset and coldset lithographic inks.

BACKGROUND

Lithographic printing processes often are used to prepare printedarticles such as papers, magazines, films and labels. For lithographicprinting processes, all types of lithographic printing inks known in theart can be used, depending on the selected process. These include, e.g.,sheetfed, heatset and coldset lithographic printing inks.

Sheetfed printing inks normally dry as a result of anoxido-polymerization process. The oxygen surrounding the ink film reactswith the free C═C double bonds present in the ink system, which allowsthe formation of a high molecular weight polymer. The kinetics of thisprocess are very slow and oxidative drying could last anywhere fromseveral days to weeks depending on the ink formulation. Thus, in orderto expedite further processing, such as cutting, folding and/or binding,the printed substrate often is overprinted with varnish. This is anadded step that adds to the cost of the process.

The kinetics of oxidative drying can be increased by including metaldrier or metal catalyst, which allows the ink film to be dried anywherefrom several hours to 1 or 2 days. However, printing inks containingmetal catalysts or metal driers have two major drawbacks. Firstly, thesheetfed printing inks are prone to premature polymerization on thepress, which can necessitate time consuming and costly frequent presscleaning, or premature polymerization in storage containers, usually inthe form of skin formation, which leads to sheetfed printing ink wastageand possible contamination. Secondly, the metal driers or metalcatalysts are generally not user-friendly due to associated toxicityissues. Cobalt salts are the most widely used metal driers or metalcatalysts in sheetfed offset printing but are regarded as toxic tohandlers.

In the literature, there is no description of sheetfed offset inks thatcan polymerize (dry) quickly enough for further processing without theneed for overprinting or including metal driers or metal catalysts.Thus, a need exists to improve the setting and drying properties and rubresistance of sheetfed lithographic inks while minimizing or eliminatingmetal driers or metal catalysts in the printing inks and the associatedhealth risks and/or eliminating the need to overprint with varnish priorto further processing.

Lithographic printing inks used in heatset printing processes dry underthe influence of heat, generally via solvent evaporation. Theevaporation of solvent can be a major factor in the drying speed of theheatset printing ink. Heatset printing inks often include oils, such as,for example, mineral oils, which oils evaporate under the influence ofheat, thereby allowing the printing ink film on the printed substrate todry. The oils, e.g., mineral oils, can have a boiling range above 200°C. For example, some heatset printing inks often include oils have aboiling range of 220° C. to 320° C. Because the heatset printing inkdoes not need to have its components absorbed by the substrate, e.g.,paper, in order to dry, substrates having smaller pores and/or having acoated surface can be printed.

Solvent evaporation as a drying mechanism can be accomplished at roomtemperature given enough time. Stacking of fresh prints in order toconserve space, which is typical during long printing runs, frequentlylimits the amount of oxygen available to the printed sheets and thusreduces the oxido-polymerization mechanism for drying, thereby limitingthe efficacy of room temperature drying of stacked prints. To meet theefficacy requirements of the modern printer, a thermal process toaccelerate solvent drying is required in heatset printing applications.The requirement that heatset printing inks be dried, such as by using athermal process or other drying devices, means that the printing processcan be energy intensive. Additionally, the incorporation of somesolvents in lithographic printing inks can result in undesirabledistortion, e.g., capillary spread prior to the ink drying, impactingprint resolution. Thus, a need exists to improve the setting propertiesand drying properties and rub resistance of heatset printing inks whilereducing the temperature needed to cure the heatset printing inks oreliminating the need to heat the heatset printing ink altogether.

Printing inks used in coldset printing processes dry by absorption ofink components into the substrate, such as paper. Coldset printing inkscan include special auxiliary substances, e.g., surfactants, waxes,gelating agents and mineral fillers, which enhance or enable the inkfilm on the printed substrate surface to dry by causing ink componentsto be absorbed into the substrate. The printed ink film generally doesnot have the same strength as the film produced from a heatset printingink formulation. Rub off can be a problem for some coldset printing inkformulations. Thus, a need exists to improve the setting properties andrub resistance of coldset printing inks.

SUMMARY OF THE INVENTION

It now has been found that the setting and drying rates, as measured byrub resistance, of most printing inks, particularly lithographicprinting inks, including sheetfed, heatset and coldset lithographicprinting inks, is advantageously enhanced by the inclusion of anessentially non-aqueous dispersion containing acrylic core/shellpolymers in a continuous phase of an essentially non-aqueous organicsolvent (NAD). Incorporation of NAD in lithographic printing inksresults in printing inks that set dry dramatically faster thanconventional lithographic printing inks.

Provided herein are lithographic printing inks and methods for improvedprocessability of a lithographic printed substrate. In particular,provided are sheetfed offset printing inks containing NAD that exhibitfast setting and drying speeds while preferably eliminating metal driersor metal catalysts and the associated health risks. For the purposes ofthis application, drying speed is assessed by rub resistance testing,which indicates the degree of drying in a printed ink film. Better rubresistance indicates faster drying. Worse rub resistance indicatesslower drying.

Provided herein are sheetfed printing inks that contain NAD butpreferably do not contain metal drier or metal catalyst and that stilldry quickly enough to allow processing of sheetfed printed sheets soonafter printing without requiring overprinting. Also provided are methodsof sheetfed offset lithographic printing of a substrate that minimize orobviate the need to include a metal drier or metal catalyst in order toproduce a printed substrate that rapidly exhibits sufficient rubresistance to allow further processing of the printed substrate soonafter printing. The methods include applying to a substrate a heatsetprinting ink that includes a NAD.

Also provided are heatset lithographic printing inks that contain a NADand exhibit fast setting and drying speeds at reduced applied thermalconditions. Also provided are heatset lithographic printing inks thatcontain NAD and exhibit fast drying speeds at ambient drying conditions.Also provided are methods of heatset offset lithographic printing of asubstrate that allows formation of a printed ink film on the substrate,the printed ink film rapidly exhibiting rub resistance. The methodincludes providing a heatset lithographic printing ink containing a NAD,which reduces the thermal energy required to set and dry the printingink or eliminates the need to apply an external energy source, such asusing a thermal process or other drying devices, such as, e.g., UV or IRdryers, in order to form a printed heatset printing ink film exhibitingrub resistance on the substrate.

Provided herein are coldset offset lithographic printing inks, whichcontain a NAD, and that exhibit fast setting and drying speeds comparedto comparable coldset printing inks that do not contain a NAD. Alsoprovided are methods of coldset offset lithographic printing of asubstrate that results in a printed coldset printing ink film thatexhibits enhanced rub resistance. The methods include applying to thesubstrate a coldset lithographic printing ink that includes a NAD.

DETAILED DESCRIPTION OF THE INVENTION

It is to be understood that the foregoing general description and thefollowing detailed description are exemplary and explanatory only andare not restrictive of any subject matter claimed.

The section headings used herein are for organizational purposes onlyand are not to be construed as limiting the subject matter described.

A. Definitions

Unless defined otherwise, all technical and scientific terms used hereinhave the same meaning as is commonly understood by one of skill in theart to which the inventions belong. All patents, patent applications,published applications and publications, websites and other publishedmaterials referred to throughout the entire disclosure herein, unlessnoted otherwise, are incorporated by reference in their entirety for anypurpose.

In this application, the use of the singular includes the plural unlessspecifically stated otherwise.

In this application, the use of “or” means “and/or” unless statedotherwise. As used herein, use of the term “including” as well as otherforms, such as “includes,” and “included,” is not limiting.

As used herein, ranges and amounts can be expressed as “about” aparticular value or range. “About” is intended to also include the exactamount. Hence “about 5 percent” means “about 5 percent” and also “5percent.” “About” means within typical experimental error for theapplication or purpose intended.

As used herein, “improved rub resistance” refers to achieving a rubresistance of a printed ink in a certain amount of time after printingthat is better that the rub resistance achieved with a comparablecontrol printed ink in the same amount of time. As an example, inksexhibiting improved rub resistance exhibit improved processability, inwhich the printed substrate can be subjected to further processingwithout detrimental effect to the printed ink. In some instances, an inkdemonstrating improved rub resistance has a rub resistance in 15 minutesor less that is equal to the rub resistance achieved in a standard inkafter 1 hour.

As used herein, “setting” refers to ink film formation and apparentdrying of the ink. Although the ink chemically may not be dried, the inkis set and exhibits rub resistance.

As used here, “NAD” refers to an essentially non-aqueous dispersioncontaining acrylic core/shell polymers, which can be in the form ofparticles, in an essentially non-aqueous solvent. While the continuousphase of the dispersion is a non-aqueous solvent, such as a non-aqueousorganic solvent, the dispersion can contain up to 1 wt % water, such as0.001 wt % to 1 wt % water based on the weight of the composition.

As used herein, “essentially non-aqueous” refers to a composition thatcontains minimal to no water. In some instances, an essentiallynon-aqueous composition can contain up to 1.0 wt % water based on theweight of the composition.

As used herein, a “rheology adjusting component” refers to a compound ormixture of two or more compounds that when added to a dispersionmodifies the rheology of the dispersion. The modification to therheology can result in an increase in the viscosity of the dispersion.

As used herein, “core-to-shell ratio” or “core/shell ratio” refers tothe value obtained when the amount of acrylic core polymer in acore/shell polymer particle is divided by the amount of acrylic shellpolymer in a core/shell polymer particle.

B. Improved Lithographic Printing Inks

It now has been found that the setting and drying rates, as measured byrub resistance, of most printing inks, such as lithographic printinginks, including sheetfed, heatset and coldset lithographic printinginks, can be advantageously enhanced by the inclusion of a NAD asdescribed herein. Incorporation of a NAD in a lithographic printing inkresults in a lithographic printing ink that sets and dries dramaticallyfaster than conventional lithographic printing inks that do not includea NAD.

Sheetfed lithographic printing inks are designed to run on sheetfedpresses and are formulated to print on appropriate substrates that areprinted using a sheetfed lithographic process. The NADs provided hereincan be used in conventional and waterless printing sheetfed lithographicprinting inks. Conventional sheetfed lithographic printing inkstypically have a viscosity (measured using a Laray falling rodviscometer) of between at or about 150 dPa·s to at or about 250 dPa·sand a tack (measured using a Tack-o-Scope device at 200 rpm, e.g., fromTestprint, Inc., Cherry Hill, N.J.) of at or about 130 to at or about220. Waterless printing sheetfed lithographic printing inks typicallyhave a viscosity (measured using a Laray falling rod viscometer) ofbetween at or about 220 dPa·s to at or about 400 dPa·s and a tack(measured using a Tack-o-Scope device at 200 rpm) of at or about 120 toat or about 180.

Heatset lithographic printing inks are designed to run on heatsetpresses and are formulated to print on appropriate substrates that areprinted using a heatset lithographic process. The NADs provided hereincan be used in heatset lithographic printing inks. Heatset lithographicprinting inks typically have a viscosity (measured using a Laray fallingrod viscometer) of between at or about 70 dPa·s to at or about 150 dPa·sand a tack (measured using a Tack-o-Scope device at 300 rpm) of at orabout 100 to at or about 200.

Coldset lithographic printing inks are designed to run on coldsetpresses and are formulated to print on appropriate substrates that areprinted using a coldset lithographic process. The NADs provided hereincan be used in coldset lithographic printing inks. Coldset lithographicprinting inks typically have a viscosity (measured using a Laray fallingrod viscometer) of between at or about 40 dPa·s to at or about 100 dPa·sand a tack (measured using a Tack-o-Scope device at 300 rpm) of at orabout 80 to at or about 130.

C. Essentially Non-Aqueous Dispersions of Acrylic Core/Shell Polymer(NADS)

Dispersions of polymers are known in the art (for example, see U.S. Pat.Nos. 6,638,995 and 5,331,025, U.S. Patent Application Publ. No.US2005/0244736 and International patent publications WO 2009/155201 andWO2011/014826). U.S. Pat. No. 6,638,995 describes lithographic printinginks that include a polyol phase dispersed or emulsified in a branchedvinyl resin vehicle phase. The patent states that the inks have improvedmisting and slinging properties and when used in news inks are purportedto improved rub-off properties. The vinyl resins are prepared by chainreaction polymerization, or addition polymerization, throughcarbon-carbon double bonds, using vinyl monomers, such as acrylic andmethacrylic monomers. The inks can also include other resins and one ormore solvents, including water and aliphatic hydrocarbons (lithographicinks) or soybean or other vegetable oils (gravure and flexographicinks). The inks purportedly can be formulated having an oil-basedcontinuous phase that contains the branched vinyl vehicle and a polyoldiscontinuous (dispersion) phase that contains a liquid polyol.

U.S. Pat. No. 5,331,025 describes methods for reducing the drying timeof paints that contain composite polymer particles having a softer,insoluble first stage and a hard second stage. The composite polymerparticles are described as being made of at least two mutuallyincompatible polymer stages that can be present as core/shell polymers.

U.S. Published Patent Appl. US 2005/0244736 describes liquid toners forelectro-photographic image forming apparatuses, e.g., copiers, laserprinters, and fax machines.

The patent application describes the toners as containing an organosoland dispersion assistant agent that has an unsaturated double bond thatphoto-polymerizes in the presence of a photoreactive catalyst. Theorganosol purportedly contains particles of a thermoplastic co-polymercore that is insoluble in the carrier liquid (aliphatic hydrocarbon),and a shell containing co-polymer graft stabilizer that is covalentlybonded to the thermoplastic co-polymer core. The patent applicationdescribes a function of the organosol as maintaining dispersionstability of the toner for an extended period of time.

In the international patent publication WO09155201, the use of anon-aqueous dispersion (NAD) polymer is described in order to increasethe drying speed of a sheetfed offset ink. The specification mentionsthat the amount of NAD present in the sheet fed offset ink is at leastfrom about 1% to about 15%, more preferably about 5% and most preferablyabout 10%. The examples, however, are limited to an amount of NAD of 10wt % based on the weight of the ink, which necessitates the use of ametal drier or metal catalyst to polymerize the ink.

Core/shell polymer technology is well known in the polymer arts. Forexample, see U.S. Pat. Nos. 3,985,703; 4,264,678; 4,375,532; 4,419,471;4,888,395; 4,916,171; 4,994,524; 5,006,592; 5,087,663; 5,186,993;5,324,780; 6,203,973; 6,309,739; 6,605,404 and 7,939,103; and Kazemi etal., Small 4(10): 1756-1762 (2008). Any of the core/shell polymers knownin the art that are compatible with the ink components can be used inthe present invention.

Core/shell polymers have been used successfully in paint to controlbody, encapsulate pigment, and to provide emulsion-like dispersions inwater-free environments. Preferred NADs for lithographic printing inkscontain insoluble acrylic polymer particles dispersed in an essentiallynon-aqueous organic medium. These dispersions are attractive additivesfor lithographic printing inks due to their controlled particle size.

The preferred NAD used in the present lithographic printing inks can beformed by generating an acrylic core-shell polymer where the shellpolymer is soluble in the continuous phase solvent while the acryliccore polymer is insoluble in the solvent, but soluble in the shellpolymer. This structure can be obtained through a 2-step polymerizationwhere the shell polymer is formed first and then the acrylic corepolymer is “filled in,” generating a dispersion. This process isdescribed in WO09155201A, which is incorporated herein in its entiretyby reference.

In the preparation of the NAD, the acrylic monomers used to make theacrylic shell polymer and/or the acrylic core polymer can include afunctional group selected from among a carboxyl group, a hydroxyl groupand a vinyl group.

The acrylic core polymer and/or the acrylic shell polymer of the NAD caninclude monomers that include a carboxyl functional group. Exemplarymonomers that include a carboxyl functional group include acrylic acid,methacrylic acid, itaconic acid and maleic acid.

The acrylic core polymer and/or the acrylic shell polymer of the NAD caninclude monomers that include a hydroxyl functional group. Exemplarymonomers that include a hydroxyl functional group include 2-hydroxyethyl acrylates, 2-hydroxy ethyl methacrylates, 2-hydroxy propylacrylates and 2-hydroxy propyl methacrylates.

The acrylic core polymer and/or the acrylic shell polymer of the NAD caninclude monomers that include a vinyl functional group. Exemplarymonomers that include a hydroxyl functional group include glycidylacrylate; glycidyl methacrylates and dimethyl amino methacrylate.

The NAD can be prepared by selecting a pre-formed acrylic shell polymerthat is soluble in the continuous phase essentially non-aqueous solventand then generating an acrylic core polymer from monomers selected toform an acrylic core polymer that is insoluble in the essentiallynon-aqueous solvent, but soluble in the shell polymer. By reacting thepre-formed acrylic shell polymer with the acrylic core polymer in theessentially non-aqueous solvent at elevated temperature, such as between85° C.-140° C., the acrylic core polymer preferentially interacts withthe acrylic shell polymer to form core/shell polymers, particularlycore/shell polymer particles, generating a dispersion of core/shellpolymer in the continuous phase essentially non-aqueous solvent.

The NAD also can be prepared by selecting a pre-formed acrylic shellpolymer that is soluble in the continuous phase essentially non-aqueoussolvent and selecting a pre-formed acrylic core polymer that isinsoluble in the essentially non-aqueous solvent, but soluble in theshell polymer. By reacting the pre-formed acrylic shell polymer with thepre-formed acrylic core polymer in the essentially non-aqueous solventat elevated temperature, such as between 85° C.-140° C., the acryliccore polymer preferentially interacts with the acrylic shell polymer toform core/shell polymers, particularly core/shell polymer particles,generating a dispersion of core/shell polymer in the continuous phaseessentially non-aqueous solvent.

D. Acrylic Core/Shell Polymer NAD Formation

NAD Synthesis

The non-aqueous dispersions provided herein can be formed by generatingan acrylic core/shell polymer where the shell polymer is soluble in anessentially non-aqueous organic solvent continuous phase while theacrylic core polymer is insoluble in the solvent, but soluble in theshell polymer. The acrylic core/shell polymer can be formed in atwo-step polymerization process in which the shell polymer is formedfirst and then the acrylic core polymer is “filled in,” generating adispersion.

1. Acrylic Shell Polymer

The shell polymer can be formed using any method known in the art. Forexample, the acrylic shell polymer of the acrylic core/shell polymer canbe formed by first heating a continuous phase essentially non-aqueoussolvent to 120° C. or to about 120° C., under an inert gas, such asnitrogen gas, in a reaction vessel. The continuous phase essentiallynon-aqueous solvent can be an organic medium, such as a vegetable oil ora hydrocarbon solvent, for example a hydrocarbon oil. The oil shouldhave good solubility, preferably with an aniline point between from orbetween about from 45° C. to 90° C., or 50° C. to 80° C., such as at orabout 45° C., 50° C., 55° C., 60° C., 65° C., 70° C., 75° C., 80° C.,85° C. or 90° C. Examples of vegetable oils include almond oil, cacaooil, candlenut oil, castor oil, dehydrated castor oil, coconut oil, cornoil, cottonseed oil, grape seed oil, hempseed oil, linseed oil, oliveoil, palm kernel oil, peanut oil, rapeseed oil, rice bran oil, saffloweroil, sunflower oil, sesame oil, soybean oil, tall oil, tung oil andwalnut oil, including combinations and fatty acid esters, such as fattyacid alkyl esters, thereof. Exemplary vegetable oils include, forexample, ethyl hexyl palmitate. Suitable hydrocarbon solvents includeparaffinic oils, such as white mineral oils (CAS No. 8042-47-5), e.g.,Magie N-40 oil; naphthenic oils and distillates, such as hydrotreatedlight naphthenic distillates (CAS No. 64742-53-6), e.g., Nytex 5130, andhydrotreated heavy naphthenic distillates (CAS No. 64742-52-5), e.g.,Nytex 510 and Nytex 810); and aromatic oils. The hydrocarbon solventoptionally can be a process oil containing bitumen (CAS No. 64742-93-4),such as Nyprint 863.

The vegetable oil or hydrocarbon solvent preferably has a sulfur contentat or below 1000 ppm. Generally, it is preferred that the vegetable oilor hydrocarbon solvent has a sulfur content at or below 750 ppm, andmore preferably below 500 ppm. For example, the sulfur content is at orabout 1 ppm, 10 ppm, 25 ppm, 50 ppm, 75 ppm, 100 ppm, 125 ppm, 150 ppm,175 ppm, 200 ppm, 225 ppm, 250 ppm, 275 ppm, 300 ppm, 325 ppm, 350 ppm,375 ppm, 400 ppm, 425 ppm, 450 ppm or 475 ppm, but less than 500 ppmsulfur. Exemplary continuous phase solvents that can be used tosynthesize the shell polymers provided herein are hydrotreated lightnaphthenic distillates, e.g., Nytex 5130, and white mineral oils, e.g.,Magie N-40 oil.

The total amount of continuous phase essentially non-aqueous solventused in the synthesis of the shell polymers provided herein, as apercentage (%) by weight of the total reaction mixture (wt %), can be,e.g., between from or about from 1 wt % to 60 wt %, such as 1 wt % to 10wt %, 1 wt % to 15 wt %, 1 wt % to 25 wt %, 1 wt % to 30 wt %, 1 wt % to40 wt %, 1 wt % to 50 wt %, 5 wt % to 10 wt %, 5 wt % to 15 wt %, 5 wt %to 25 wt %, 5 wt % to 30 wt %, 5 wt % to 40 wt %, 5 wt % to 50 wt %, 10wt % to 20 wt %, 10 wt % to 30 wt %, 10 wt % to 40 wt %, 10 wt % to 50wt %, 15 wt % to 25 wt %, 15 wt % to 30 wt %, 15 wt % to 35 wt %, 15 wt% to 40 wt %, 15 wt % to 45 wt %, 15 wt % to 50 wt %, 20 wt % to 30 wt%, 20 wt % to 40 wt %, 20 wt % to 50 wt %, 25 wt % to 30 wt %, 25 wt %to 35 wt %, 25 wt % to 40 wt %, 25 wt % to 45 wt %, 25 wt % to 50 wt %,25 wt % to 60 wt %, 30 wt % to 40 wt %, 30 wt % to 50 wt %, 30 wt % to60 wt %, 40 wt % to 50 wt %, 40 wt % to 55 wt %, 40 wt % to 60 wt %, 45wt % to 50 wt %, 45 wt % to 55 wt %, 45 wt % to 60 wt %, 50 wt % to 60wt %, 50 wt % to 55 wt %, and 55 wt % to 60 wt %, based on the weight ofthe total reaction mixture. Generally, the total reaction mixturecontains less than 60 wt % solvent. For example, the reaction mixturesprovided herein can contain at least or about at least 1 wt %, 3 wt %, 5wt %, 7 wt %, 10 wt %, 12 wt %, 15 wt %, 17 wt %, 19 wt %, 20 wt %, 21wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27 wt %, 28 wt %, 29wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35 wt %, 40 wt %, 42wt %, 45 wt %, 48 wt %, 50 wt %, 55 wt %, but less than 60 wt % totalsolvent based on the weight of the total reaction mixture.

Over a period of time, a mixture of acrylic monomers and a catalyst or amixture of catalysts can be added to the reaction vessel containing thecontinuous phase essentially non-aqueous solvent. The period of time canbe, for example, 1 to 5 hours, or 1, 2, 3, 4 or 5 hours, such as 4 hoursor about 4 hours. The temperature of the first reaction vessel can bebetween 85° C. to 140° C., or 90° C. to 130° C., for example at or about85° C., 90° C., 95° C., 100° C., 105° C., 110° C., 115° C., 120° C.,125° C., 130° C., 135° C. or 140° C., such as 120° C. or about 120° C.The mixture of monomers and mixture of catalysts can be addedconcurrently to the first reaction vessel from separate reactionvessels.

The mixture of monomers can be pre-mixed in a separate mixing vessel andcan include monomers that are soluble in the continuous phase solvent.Such monomers can contain hydrocarbon chains. The hydrocarbon chains onthe monomers can make the resulting polymer readily soluble in thecontinuous phase solvent. The monomers can contain one or morefunctional groups, such as carboxyl groups. Exemplary monomers that cancontain carboxyl groups are acrylic acid and substituted acrylic acids(e.g., n-butyl acrylate), methacrylic acid and substituted methacrylicacids (e.g., isobutyl methacrylate, dodecyl methacrylate, methylmethacrylate and n-butyl methacrylate), itaconic acid and substituteditaconic acids, and maleic acid and substituted maleic acids. Themonomers can contain hydroxyl groups. Exemplary monomers that cancontain hydroxyl groups include 2-hydroxy ethyl acrylates, 2-hydroxyethyl methacrylates, 2-hydroxy propyl acrylates and 2-hydroxy propylmethacrylates. The monomers can contain vinyl functional groups.Exemplary vinyl functional groups include glycidyl acrylates, glycidylmethacrylates and dimethyl amino methacrylates. Monomers that containepoxy functional groups, such as glycidyl acrylates, can be added to themonomer mixture to increase the attraction between the acrylic shell andacrylic core polymers. The monomers can contain one or more than onefunctional group or a combination of functional groups such as carboxyl,hydroxyl and vinyl.

In the shell polymers provided herein, the monomer mixture can containtwo or more monomers. For example, the mixture of monomers can be amixture of substituted methacrylic acids. The methacrylic acids can beC₁-C₁₂ alkyl methacrylates. Exemplary C₁-C₁₂ alkyl methacrylates thatcan be used in the shell polymers provided herein are isobutylmethacrylate and dodecyl methacrylate. The ratio of isobutylmethacrylate to dodecyl methacrylate can be or can be about 10:1, 9:1,8:1, 7:1, 6:1, 5:1, 4:1, 3:1, 2:1, 1.5:1, 1.3:1, 1.1:1 or 1:1 or less.

To aid in efficient polymer formation, a polymerization promotor can beadded to the monomer mixture. The polymerization promoters areco-polymerizable with the acrylate monomers (and other co-monomers, ifpresent) of the acrylic core/shell polymers. The promoters can promotepolymerization or cross-linking, and/or introduce pendant groups, e.g.,cross-linkable pendant carboxylic groups, cross-linkable pendanthydroxyl groups and/or cross-linkable pendant amide groups, into thecopolymer backbone. Exemplary polymerization promoters include acrylicacid or C₁-C₆-substituted acrylic acid, e.g., methacrylic acid (tointroduce cross-linkable pendant carboxylic groups into the copolymerbackbone), hydroxyalkyl esters of acrylic acid orC₁-C₆-alkyl-substituted acrylic acid, such as 2-hydroxyethyl acrylate,2-hydroxypropyl acrylate and 3-hydroxy-propyl methacrylate (to introducecross-linkable pendant hydroxyl groups into the copolymer backbone), andan acrylic acid amide or C₁-C₆-alkyl-substituted acrylic acid amide,such as hydroxymethylene diacetone acrylamide (to introducecross-linkable pendant amide groups into the copolymer backbone). Apreferred polymerization promoter contains acrylic acid. An exemplarypolymerization promoter is acrylic acid. The amount of polymerizationpromoter that can be used can be from 0.5 wt % to 5 wt % based on theweight of the reaction mixture. In an exemplary monomer mixture, 1 wt %or about 1 wt % acrylic acid based on the weight of the reaction mixturecan be present.

In the acrylic shell polymers provided herein, the total weight ofmonomer or monomer mixture as a percentage (%) by weight of the reactionmixture (wt %) can be, for example, between from or about from 1 wt % to60 wt %, such as 1 wt % to 10 wt %, 1 wt % to 15 wt %, 1 wt % to 25 wt%, 1 wt % to 30 wt %, 1 wt % to 40 wt %, 1 wt % to 50 wt %, 5 wt % to 10wt %, 5 wt % to 15 wt %, 5 wt % to 25 wt %, 5 wt % to 30 wt %, 5 wt % to40 wt %, 5 wt % to 50 wt %, 10 wt % to 20 wt %, 10 wt % to 30 wt %, 10wt % to 40 wt %, 10 wt % to 50 wt %, 15 wt % to 25 wt %, 15 wt % to 30wt %, 15 wt % to 35 wt %, 15 wt % to 40 wt %, 15 wt % to 45 wt %, 15 wt% to 50 wt %, 20 wt % to 30 wt %, 20 wt % to 40 wt %, 20 wt % to 50 wt%, 25 wt % to 30 wt %, 25 wt % to 35 wt %, 25 wt % to 40 wt %, 25 wt %to 45 wt %, 25 wt % to 50 wt %, 25 wt % to 60 wt %, 30 wt % to 40 wt %,30 wt % to 50 wt %, 30 wt % to 60 wt %, 40 wt % to 50 wt %, 40 wt % to55 wt %, 40 wt % to 60 wt %, 45 wt % to 50 wt %, 45 wt % to 55 wt %, 45wt % to 60 wt %, 50 wt % to 60 wt %, 50 wt % to 55 wt %, and 55 wt % to60 wt %, by weight of the reaction mixture, which contains anessentially non-aqueous solvent, acrylic monomer or mixture of acrylicmonomers and other reactants. Generally, the reaction mixture generallycontains less than 60 wt % acrylic monomer or acrylic monomer mixture.For example, the reaction mixtures provided herein can contain at leastor about at least 1 wt %, 3 wt %, 5 wt %, 7 wt %, 10 wt %, 12 wt %, 15wt %, 17 wt %, 19 wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25wt %, 26 wt %, 27 wt %, 28 wt %, 29 wt %, 30 wt %, 35 wt %, 40 wt %, 42wt %, 45 wt %, 48 wt %, 50 wt %, 55 wt %, or 60 wt % total monomermixture based on the total weight of the reaction mixture.

The catalyst or mixture of catalysts can be pre-mixed in a separatevessel before adding to the reaction vessel containing the reactionmixture. The catalyst pre-mix can include one or more polymerizationinitiators. The polymerization initiators can be, for example, organicperoxide catalysts. Exemplary organic peroxide catalysts include dialkylperoxides, di-tert-alkyl peroxides, diacyl peroxides, dialkylperoxydicarbamates, tert-alkyl peroxyesters and di-tert-alkylperoxy-ketals. Preferred polymerization initiators are the dialkylperoxides, such as tert-butyl peroctoate and tert-butyl peroxybenzoate.The polymerization initiators can be free radical initiators. Exemplaryfree radical initiators include azo initiators. A preferred azoinitiator is, for example, Vazo® 67 (DuPont, Wilmington, Del.). Thecatalyst mixture can contain two or more polymerization initiators. Forexample, the mixture of catalysts can be a mixture of organic peroxidecatalysts. Exemplary organic peroxide catalysts that can be used in theshell polymers provided herein are tort-butyl peroctoate and tert-butylperoxybenzoate. The ratio of tert-butyl peroctoate to tert-butylperoxybenzoate can be or can be about 10:1, 9:1, 8:1, 7:1, 6:1, 5:1,4:1, 3:1, 2:1, 1.5:1, 1.3:1, 1.1:1 or 1:1 or less.

The catalysts can be pre-mixed in a continuous phase solvent, forexample the same continuous phase solvent present in the reaction vessel(e.g., Nytex 5130 or Magie N-40 oil).

After the mixture of monomers and mixture of catalysts are added to thereaction vessel, and after mixing at a temperature between 85° C. to140° C., or 90° C. to 130° C., for example at or about 85° C., 90° C.,95° C., 100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130° C.,135° C. or 140° C., such as 120° C. or about 120° C. for a period oftime between, for example, 1 to 5 hours, or 1, 2, 3, 4 or 5 hours, suchas 4 hours or about 4 hours, the inert gas can be changed to air. Amixture of glycidyl methacrylate, triphenyl-phosphine andp-methoxyphenol can be added to the reaction mixture in the reactionvessel. For example, up to 1 wt % or about 1 wt %, or between 0.05 wt %to 0.5 wt %, such as 0.1 wt %, 0.2 wt %, 0.3 wt %, 0.4 wt %, 0.5 wt %,0.6 wt %, 0.7 wt %, 0.8 wt %, 0.9 wt % or 1 wt % glycidyl methacrylateby weight of the reaction mixture. The amount of triphenyl-phosphinethat can be added to the reaction mixture can be in the range of at orabout 0.001 wt % to 0.1 wt %, or 0.005 wt % to 0.05 wt %, such as 0.001wt %, 0.002 wt %, 0.003 wt %, 0.004 wt %, 0.005 wt %, 0.006 wt %, 0.007wt %, 0.008 wt %, 0.009 wt %, 0.010 wt %, 0.011 wt %, 0.012 wt %, 0.013wt %, 0.014 wt %, 0.015 wt %, 0.016 wt %, 0.017 wt %, 0.018 wt %, 0.019wt %, 0.020 wt %, 0.021 wt %, 0.022 wt %, 0.023 wt %, 0.024 wt %, 0.025wt %, 0.026 wt %, 0.027 wt %, 0.028 wt %, 0.029 wt %, 0.030 wt %, 0.040wt %, 0.050 wt %, 0.060 wt %, 0.070 wt %, 0.080 wt %, 0.090 wt % or 0.1wt % triphenyl-phosphine based on the weight of the reaction mixture.The amount of p-methoxyphenol that can be added to the reaction mixturecan be in the range of at or about 0.0005 wt % to 0.01 wt %, or 0.001 wt% to 0.009 wt %, such as 0.001 wt %, 0.002 wt %, 0.003 wt %, 0.004 wt %,0.005 wt %, 0.006 wt %, 0.007 wt %, 0.008 wt %, 0.009 wt % or 0.001 wt %p-methoxyphenol based on the weight of the reaction mixture. In anexemplary reaction, the reaction mixture contains 0.33 wt % glycidylmethacrylate, 0.02 wt % triphenyl phosphine and 0.003 wt %p-methoxyphenol based on the weight of the reaction mixture.

After addition of the glycidyl methacrylate, triphenylphosphine andp-methoxyphenol mixture, the reaction vessel can be held at the sametemperature, for example at 85° C. to 140° C., or 90° C. to 130° C., forexample at or about 85° C., 90° C., 95° C., 100° C., 105° C., 110° C.,115° C., 120° C., 125° C., 130° C., 135° C. or 140° C., such as 120° C.or about 120° C., for a period of time between, for example, 1 to 5hours, or 1, 2, 3, 4 or 5 hours, such as 4 hours or about 4 hours. Theair in the reaction vessel then be removed, such as by subjecting thereaction mixture vessel to vacuum for 30 minutes or about 30 minutes.The reaction vessel then can be cooled down to allow discharge of theresulting shell polymer. The reaction vessel can be cooled down to atemperature of 100° C. or about 100° C. or less.

The inert gas can be changed to air after the mixture of monomers andmixture of catalysts are added to the reaction vessel and mixed at 85°C. to 140° C., or 90° C. to 130° C., for example at or about 85° C., 90°C., 95° C., 100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130°C., 135° C. or 140° C., such as 120° C. or about 120° C., for a periodof time between, for example, 1 to 5 hours, or 1, 2, 3, 4 or 5 hours,such as 4 hours or about 4 hours. Additional polymerization initiator,for example the same polymerization initiator used in the catalystmixture (e.g., t-butyl peroctoate), can be added to the reaction vessel.For example, additional polymerization initiator can be added in anamount of up to 1 wt % or about 1 wt %, such as 0.1 wt %, 0.2 wt %, 0.3wt %, 0.4 wt %, 0.5 wt %, 0.6 wt %, 0.7 wt %, 0.8 wt %, 0.9 wt % or 1 wt% based on the weight of the reaction mixture. The reaction vessel thencan be held at the same temperature, for example at 120° C. or about120° C., for a time from 1-4 hours, such as 1, 1.5, 2, 2.5, 3, 3.5 or 4hours, for example, 2 hours or about 2 hours.

The viscosity of the composition can be modified by slowly adding arheology adjusting component, such as, for example, water, an alcohol,an alkali compound, an amine or a combination thereof, to the reactionvessel. Addition of the rheology adjusting component increases theviscosity of the resulting NAD such that addition of a relatively largeamount of the NAD, such as 15 wt % to 60 wt % based on the weight of theink, to an ink will not adversely affect the desired viscosity range ofthe ink.

The alcohol that can be used as or in the rheology adjusting componentcan be, for example, a C₁-C₆ alcohol, such as isopropanol (isopropylalcohol), butanol, ethanol and methanol. Suitable alkali compounds thatcan used as or in the rheology adjusting component include metalhydroxides. Exemplary metal hydroxides include potassium hydroxide,sodium hydroxide and calcium hydroxide. Exemplary amines that can beused as or in the rheology adjusting component can be a primary amine(e.g., ethyl amine), secondary amine (e.g., diethylamine) or tertiaryamine (e.g., triethylamine). For example, a rheology adjusting componentcan contain a mixture of water, an alcohol, an alkali compound and anamine. An exemplary rheology adjusting component contains water,potassium hydroxide, such as 85 wt % potassium hydroxide, isopropanoland diethylamine.

In the acrylic shell polymers provided herein, the total amount ofrheology adjusting component as a percentage (%) by weight of thereaction mixture (wt %) can be, for example, between from or about from0.01 wt % to 2 wt %, such as 0.01 wt % to 0.1 wt %, 0.01 wt % to 0.2 wt%, 0.01 wt % to 0.3 wt %, 0.01 wt % to 0.4 wt %, 0.01 wt % to 0.5 wt %,0.01 wt % to 0.6 wt %, 0.01 wt % to 0.7 wt %, 0.01 wt % to 0.8 wt %,0.01 wt % to 0.9 wt %, 0.01 wt % to 1.0 wt %, 0.01 wt % to 1.1 wt %,0.01 wt % to 1.2 wt %, 0.01 wt % to 1.3 wt %, 0.01 wt % to 1.4 wt %,0.01 wt % to 1.5 wt %, 0.01 wt % to 1.6 wt %, 0.01 wt % to 1.7 wt %,0.01 wt % to 1.8 wt %, 0.01 wt % to 1.9 wt %, 0.1 wt % to 0.2 wt %, 0.1wt % to 0.3 wt %, 0.1 wt % to 0.4 wt %, 0.1 wt % to 0.5 wt %, 0.1 wt %to 1.0 wt %, 0.1 wt % to 1.5 wt %, 0.1 wt % to 2.0 wt %, 0.5 wt % to 1.0wt %, 0.5 wt % to 1.1 wt %, 0.5 wt % to 1.2 wt %, 0.5 wt % to 1.3 wt %,0.5 wt % to 1.4 wt %, 0.5 wt % to 1.5 wt %, 0.5 wt % to 1.6 wt %, 0.5 wt% to 1.7 wt %, 0.5 wt % to 1.8 wt %, 0.5 wt % to 1.9 wt %, 0.5 wt % to2.0 wt %, 1.0 wt % to 1.1 wt %, 1.0 wt % to 1.2 wt %, 1.0 wt % to 1.3 wt%, 1.0 wt % to 1.4 wt %, 1.0 wt % to 1.5 wt %, 1.0 wt % to 1.6 wt %, 1.0wt % to 1.7 wt %, 1.0 wt % to 1.8 wt %, 1.0 wt % to 1.9 wt %, 1.0 wt %to 2.0 wt %, 1.2 wt % to 1.3 wt %, 1.2 wt % to 1.4 wt %, 1.2 wt % to 1.5wt %, 1.2 wt % to 1.6 wt %, 1.2 wt % to 1.7 wt %, 1.2 wt % to 1.8 wt %,1.2 wt % to 1.9 wt %, 1.2 wt % to 2.0 wt %, 1.5 wt % to 1.6 wt %, 1.5 wt% to 1.7 wt %, 1.5 wt % to 1.8 wt %, 1.5 wt % to 1.9 wt %, 1.5 wt % to2.0 wt %, 1.7 wt % to 1.8 wt %, 1.7 wt % to 1.9 wt %, 1.7 wt % to 2.0 wt%, 1.8 wt % to 2.0 wt %, and 1.9 wt % to 2.0 wt %, based on the weightof the reaction mixture.

Generally, the reaction mixture contains less than 2.0 wt % water. Forexample, the reaction mixtures provided herein can contain water in anamount of up to 0.001 wt %, 0.01 wt %, 0.05 wt %, 0.1 wt %, 0.2 wt %,0.25 wt %, 0.3 wt %, 0.4 wt %, 0.5 wt %, 0.6 wt %, 0.7 wt %, 0.75 wt %,0.8 wt %, 0. wt %, 1.0 wt %, 1.1 wt %, 1.2 wt %, 1.25 wt %, 1.3 wt %,1.4 wt %, 1.5 wt %, 1.6 wt %, 1.7 wt %, 1.75 wt %, 1.8 wt %, 1.9 wt % or2.0 wt % based on the weight of the reaction mixture. Because therheology adjusting component, which includes water, can be added to thereaction vessel at high temperatures, such as at 120° C. or about 120°C., a large part of the water from the rheology adjusting component canbe distilled off, thus reducing the total amount of water present in theshell polymer and/or the NAD.

The constituents of the rheology adjusting component can be pre-mixed ina separate vessel and slowly added to the reaction vessel in order tocontrol any foaming that can occur. After addition of the rheologyadjusting component, the reaction vessel can be held at the sametemperature, for example at 120° C. or about 120° C., for 1 hour orabout 1 hour. The reaction vessel then can be cooled to allow dischargeof the resulting acrylic shell polymer. The reaction vessel can becooled down to a temperature of 90° C. or about 90° C. The reactionvessel can be cooled down to a temperature of less than or equal to 85°C. or less than or equal to about 85° C.

2. Acrylic Core Polymer

The acrylic core polymer of the acrylic core/shell polymer of the NADdescribed herein can be formed by heating in a reaction vessel acontinuous phase essentially non-aqueous solvent and the acrylic shellpolymer provided herein (and as described above) to 85° C.-140° C., suchas at or about 85° C., 90° C., 95° C., 100° C., 105° C., 110° C., 115°C., 120° C., 125° C., 130° C., 135° C. or 140° C. The reaction vesselcan be heated under an inert gas, such as nitrogen gas. The total amountof acrylic shell polymer added to the reaction mixture as a percentage(%) by weight of the reaction mixture (wt %) can be, for example,between from or about from 1 wt % to 60 wt %, such as 1 wt % to 10 wt %,1 wt % to 15 wt %, 1 wt % to 25 wt %, 1 wt % to 30 wt %, 1 wt % to 40 wt%, 1 wt % to 50 wt %, 5 wt % to 10 wt %, 5 wt % to 15 wt %, 5 wt % to 25wt %, 5 wt % to 30 wt %, 5 wt % to 40 wt %, 5 wt % to 50 wt %, 10 wt %to 20 wt %, 10 wt % to 30 wt %, 10 wt % to 40 wt %, 10 wt % to 50 wt %,15 wt % to 25 wt %, 15 wt % to 30 wt %, 15 wt % to 35 wt %, 15 wt % to40 wt %, 15 wt % to 45 wt %, 15 wt % to 50 wt %, 20 wt % to 30 wt %, 20wt % to 40 wt %, 20 wt % to 50 wt %, 25 wt % to 30 wt %, 25 wt % to 35wt %, 25 wt % to 40 wt %, 25 wt % to 45 wt %, 25 wt % to 50 wt %, 25 wt% to 60 wt %, 30 wt % to 40 wt %, 30 wt % to 50 wt %, 30 wt % to 60 wt%, 40 wt % to 50 wt %, 40 wt % to 55 wt %, 40 wt % to 60 wt %, 45 wt %to 50 wt %, 45 wt % to 55 wt %, 45 wt % to 60 wt %, 50 wt % to 60 wt %,50 wt % to 55 wt %, and 55 wt % to 60 wt %, based on the weight of thereaction mixture. Generally, the reaction mixture contains less than 60wt % acrylic shell polymer. For example, the reaction mixture cancontain acrylic shell polymer in an amount that is at least or about atleast 1 wt %, 3 wt %, 5 wt %, 7 wt %, 10 wt %, 12 wt %, 15 wt %, 17 wt%, 19 wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt%, 27 wt %, 28 wt %, 29 wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt%, 35 wt %, 40 wt %, 42 wt %, 45 wt %, 48 wt %, 50 wt %, 55 wt %, butless than 60 wt % based on the weight of the reaction mixture.

The continuous phase essentially non-aqueous solvent can be an organicmedium, such as a vegetable oil or a hydrocarbon solvent, for example ahydrocarbon oil. The vegetable oil or hydrocarbon solvent should havegood solubility, preferably with an aniline point between from orbetween about from 45° C. to 90° C., or 50° C. to 80° C., such as at orabout 45° C., 50° C., 55° C., 60° C., 65° C., 70° C., 75° C., 80° C.,85° C. or 90° C. Suitable vegetable oils include, for example, ethylhexyl palmitate. Suitable hydrocarbon solvents include paraffinic oils,such as white mineral oils, e.g., mineral oils of CAS number 64742-47-8,such as Magic N-40 oil; naphthenic oils and distillates, such ashydrotreated light naphthenic distillates (e.g., process oils of CAS No.64742-53-6, such as Nytex 5130) and hydrotreated heavy naphthenicdistillates (e.g., process oils of CAS No. 64742-52-5, such as Nytex 510and Nytex 810); and aromatic oils. The hydrocarbon solvent optionallycan contain bitumen (CAS No. 64742-93-4), such as Nyprint 863.

The hydrocarbon solvent can have a sulfur content at or below 1000 ppm.Generally, the hydrocarbon solvent has a sulfur content at or below 500ppm. Generally, the hydrocarbon solvent has a sulfur content at or below500 ppm. For example, the sulfur content is at or about 1 ppm, 10 ppm,25 ppm, 50 ppm, 75 ppm, 100 ppm, 125 ppm, 150 ppm, 175 ppm, 200 ppm, 225ppm, 250 ppm, 275 ppm, 300 ppm, 325 ppm, 350 ppm, 375 ppm, 400 ppm, 425ppm, 450 ppm, or 475 ppm, but less than 500 ppm sulfur. Exemplarycontinuous phase solvents that can be used to synthesize the acryliccore polymers provided herein are hydrotreated light naphthenicdistillate, particularly Nytex 5130, and white mineral oils,particularly Magie N-40 oil.

The total amount of continuous phase essentially non-aqueous solventused in the synthesis of the acrylic core polymers provided herein, as apercentage (%) by weight of the total reaction mixture (wt %) can be,for example, between from or about from 1 wt % to 60 wt %, such as 1 wt% to 10 wt %, 1 wt % to 15 wt %, 1 wt % to 25 wt %, 1 wt % to 30 wt %, 1wt % to 40 wt %, 1 wt % to 50 wt %, 5 wt % to 10 wt %, 5 wt % to 15 wt%, 5 wt % to 25 wt %, 5 wt % to 30 wt %, 5 wt % to 40 wt %, 5 wt % to 50wt %, 10 wt % to 20 wt %, 10 wt % to 30 wt %, 10 wt % to 40 wt %, 10 wt% to 50 wt %, 15 wt % to 25 wt %, 15 wt % to 30 wt %, 15 wt % to 35 wt%, 15 wt % to 40 wt %, 15 wt % to 45 wt %, 15 wt % to 50 wt %, 20 wt %to 30 wt %, 20 wt % to 40 wt %, 20 wt % to 50 wt %, 25 wt % to 30 wt %,25 wt % to 35 wt %, 25 wt % to 40 wt %, 25 wt % to 45 wt %, 25 wt % to50 wt %, 25 wt % to 60 wt %, 30 wt % to 40 wt %, 30 wt % to 50 wt %, 30wt % to 60 wt %, 40 wt % to 50 wt %, 40 wt % to 55 wt %, 40 wt % to 60wt %, 45 wt % to 50 wt %, 45 wt % to 55 wt %, 45 wt % to 60 wt %, 50 wt% to 60 wt %, 50 wt % to 55 wt %, and 55 wt % to 60 wt %, based on theweight of the total reaction mixture. Generally, the total reactionmixture generally contains less than 60 wt % solvent. For example, thereaction mixtures provided herein can contain solvent in an amount thatis at least or about at least 1 wt %, 3 wt %, 5 wt %, 7 wt %, 10 wt %,12 wt %, 15 wt %, 17 wt %, 19 wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %,24 wt %, 25 wt %, 26 wt %, 27 wt %, 30 wt %, 35 wt %, 40 wt %, 42 wt %,45 wt %, 48 wt %, 50 wt %, 55 wt % or 60 wt % based on the weight of thereaction mixture.

Over a period of time a mixture of acrylic monomers and a mixture ofcatalysts can be added to the reaction vessel containing the continuousphase essentially non-aqueous solvent and acrylic shell polymer. Theperiod of time can be between 1 and 5 hours, e.g., 1, 2, 3, 4 or 5hours, for example, 3 hours or about 3 hours, or 4 hours or about 4hours. The temperature of the reaction vessel can be 85° C.-140° C.,such as at or about 85° C., 90° C., 95° C., 100° C., 105° C., 110° C.,115° C., 120° C., 125° C., 130° C., 135° C. or 140° C. The mixture ofacrylic monomers and mixture of catalysts can be added concurrently tothe reaction vessel from separate delivery vessels. The reaction vesselthen can be held at 85° C.-140° C., such as at or about 85° C., 90° C.,95° C., 100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130° C.,135° C. or 140° C. The reaction vessel can be held for between 1 and 5hours, e.g., 1, 2, 3, 4 or 5 hours, for example, 3 hours or about 3hours, or 4 hours or about 4 hours.

The mixture of acrylic monomers can be pre-mixed in a separate mixingvessel and can include monomers that are soluble in the continuous phaseessentially non-aqueous solvent. Such monomers can contain hydrocarbonchains. The hydrocarbon chains on the monomers can make the resultingpolymer readily soluble in the continuous phase essentially non-aqueoussolvent. The monomers can contain one or more functional groups, such ascarboxyl groups. Exemplary monomers that contain carboxyl groups areacrylic acid and substituted acrylic acids (e.g., n-butyl acrylate),methacrylic acid and substituted methacrylic acids (e.g., isobutylmethacrylate, dodecyl methacrylate, methyl methacrylate and n-butylmethacrylate), itaconic acid and substituted itaconic acids, and maleicacid and substituted maleic acids. The monomers can contain hydroxylgroups. Exemplary monomers that can contain hydroxyl groups include2-hydroxy ethyl acrylates, 2-hydroxy ethyl methacrylates, 2-hydroxypropyl acrylates and 2-hydroxy propyl methacrylates. The monomers cancontain vinyl functional groups. Exemplary vinyl functional groupsinclude glycidyl acrylates, glycidyl methacrylates and dimethyl aminomethacrylates. Monomers that contain epoxy functional groups, such asglycidyl acrylates, can be added to the monomer mixture to increase theattraction between the acrylic shell and acrylic core polymers. Themonomers can contain one or more than one functional group or acombination of functional groups such as carboxyl, hydroxyl and vinyl.

In the acrylic core polymers provided herein, the monomer mixture addedto the reaction vessel can contain two or more monomers. For example,the mixture of monomers can be a mixture of substituted acrylic andmethacrylic acids. The acrylic and methacrylic acids can be C₁-C₁₂ alkylacrylates and methacrylates. Exemplary C₁-C₁₂ alkyl acrylic andmethacrylic acids that can be used in the acrylic core polymers providedherein are n-butyl acrylate, methyl methacrylate and n-butylmethacrylate. The ratio of methyl methacrylate to n-butyl methacrylatecan be or can be about 10:1, 9:1, 8:1, 7:1, 6:1, 5:1, 4:1, 3:1, 2:1,1.5:1, 1.3:1, 1.1:1 or 1:1 or less. The ratio of methyl methacrylate ton-butyl acrylate can be or can be about 10:1, 9:1, 8:1, 7:1, 6:1, 5:1,4:1, 3:1, 2:1, 1.5:1, 1.3:1, 1.1:1 or 1:1 or less. The ratio of n-butylacrylate to n-butyl methacrylate can be or can be about 10:1, 9:1, 8:1,7:1, 6:1, 5:1, 4:1, 3:1, 2:1, 1.7:1, 1.5:1, 1.4:1, 1.3:1, 1.2:1, 1.1:1or 1:1 or less.

In the acrylic core polymers provided herein, the total amount ofmonomer mixture as a percentage (%) by weight of the reaction mixture(wt %) can be, for example, between from or about from 1 wt % to 60 wt%, such as 1 wt % to 10 wt %, 1 wt % to 15 wt %, 1 wt % to 25 wt %, 1 wt% to 30 wt %, 1 wt % to 40 wt %, 1 wt % to 50 wt %, 5 wt % to 10 wt %, 5wt % to 15 wt %, 5 wt % to 25 wt %, 5 wt % to 30 wt %, 5 wt % to 40 wt%, 5 wt % to 50 wt %, 10 wt % to 20 wt %, 10 wt % to 30 wt %, 10 wt % to40 wt %, 10 wt % to 50 wt %, 15 wt % to 25 wt %, 15 wt % to 30 wt %, 15wt % to 35 wt %, 15 wt % to 40 wt %, 15 wt % to 45 wt %, 15 wt % to 50wt %, 20 wt % to 30 wt %, 20 wt % to 40 wt %, 20 wt % to 50 wt %, 25 wt% to 30 wt %, 25 wt % to 35 wt %, 25 wt % to 40 wt %, 25 wt % to 45 wt%, 25 wt % to 50 wt %, 25 wt % to 60 wt %, 30 wt % to 40 wt %, 30 wt %to 50 wt %, 30 wt % to 60 wt %, 40 wt % to 50 wt %, 40 wt % to 55 wt %,40 wt % to 60 wt %, 45 wt % to 50 wt %, 45 wt % to 55 wt %, 45 wt % to60 wt %, 50 wt % to 60 wt %, 50 wt % to 55 wt %, and 55 wt % to 60 wt %,based on the weight of the reaction mixture. Generally, the reactionmixture contains less than 60 wt % monomer mixture. For example, thereaction mixtures provided herein can contain an amount of monomermixture that is at least or about at least 1 wt %, 3 wt %, 5 wt %, 7 wt%, 10 wt %, 12 wt %, 15 wt %, 17 wt %, 19 wt %, 20 wt %, 21 wt %, 22 wt%, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27 wt %, 28 wt %, 29 wt %, 30 wt%, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35 wt %, 40 wt %, 42 wt %, 45 wt%, 48 wt %, 50 wt %, 55 wt % or 60 wt % based on the weight of thereaction mixture.

The mixture of catalysts can be pre-mixed in a separate mixing vesselbefore adding to the reaction vessel and can include polymerizationinitiators. The polymerization initiators can be, for example, organicperoxide catalysts. Exemplary organic peroxide catalysts include dialkylperoxides, di-t-alkyl peroxides, diacyl peroxides, dialkylperoxydicarbamates, t-alkyl peroxyesters and di-t-alkyl peroxyketals.Preferred polymerization initiators are the dialkyl peroxides, such ast-butyl peroctoate and t-butyl peroxybenzoate. The polymerizationinitiators can be free radical initiators. Exemplary free radicalinitiators include azo initiators. A preferred azo initiator is, forexample, Vazo® 67 (DuPont, Wilmington, Del.). The catalyst mixture cancontain one or more than one polymerization initiator. For example, themixture of catalysts can be a mixture of organic peroxide catalysts.Exemplary organic peroxide catalysts that can be used in the synthesisof acrylic core polymers provided herein are t-butyl peroctoate andt-butyl peroxybenzoate. The ratio of t-butyl peroctoate to t-butylperoxybenzoate can be or can be about 10:1, 9:1, 8:1, 7:1, 6:1, 5:1,4:1, 3:1, 2:1, 1.5:1, 1.3:1, 1.1:1 or 1:1 or less. The organic peroxidecatalysts can be used alone or in combination. An exemplary organicperoxide catalyst that can be used alone is t-butyl peroctoate.

The mixture of catalysts can be pre-mixed in a continuous phaseessentially non-aqueous solvent, for example, the same continuous phaseessentially non-aqueous solvent present in the reaction vessel used inthe synthesis of the acrylic core polymer, which is discussed above.Generally, the hydrocarbon solvent has a sulfur content at or below 500ppm. Exemplary continuous phase solvents that can be used to synthesizethe acrylic core polymers provided herein include hydrotreated lightnaphthenic distillate, particularly Nytex 5130, and white mineral oils,particularly Magie N-40 oil.

After the mixture of acrylic monomers and mixture of catalysts are addedto the reaction vessel, and after mixing at 85° C.-140° C., such as at85° C., 90° C., 95° C., 100° C., 105° C., 110° C., 115° C., 120° C.,125° C., 130° C., 135° C. or 140° C. for a period of time between 1 to 5hours, e.g. 1, 2, 3, 4, or 5 hours, such as for at or about 2 hours orat or about 3 hours, additional monomer can be added to the reactionvessel. The additional monomer can be one of the monomers present in theacrylic monomer mixture. For example, the additional monomer can bemethyl methacrylate. Any desired amount of additional monomer can beadded. For example, an additional amount of monomer that is up to 5 wt %or about 5 wt %, such as 0.1 wt %, 0.5 wt %, 0.7 wt %, 1 wt %, 1.5 wt %,2 wt %, 2.5 wt %, 3 wt %, 3.5 v, 4%, 4.5 wt % or 5 wt % based on theweight of reaction mixture can be added. The additional monomer can beadded to the reaction vessel at the same temperature, for examplebetween 85° C.-140° C., such as at 85° C. or at about 85° C.

In some instances, after the mixture of monomers and mixture ofcatalysts are added to the reaction vessel, the inert gas can be changedto air and the reaction vessel can be held at 120° C. or about 120° C.for 1 hour or about 1 hour.

A second or supplemental mixture of catalysts then can be added to thereaction vessel. The second mixture of catalysts can be pre-mixed in aseparate mixing vessel and can include additional polymerizationinitiators. For example, the additional polymerization initiators can bethe same polymerization initiators used in the first catalyst mixture.The additional polymerization initiators can be a single type ofcatalyst, such as t-butyl peroctoate. The additional polymerizationinitiators can be a mixture of catalysts, such as t-butyl peroctoate andt-butyl peroxybenzoate. The catalyst can be mixed with a continuousphase essentially non-aqueous solvent, e.g., the same continuous phasesolvent present in the first mixture of catalysts (e.g., Nytex 5130 orMagie N-40 oil). For example, a second mixture of catalysts can be addedin an amount of up to 5 wt % or about 5 wt %, such as 0.1 wt %, 0.25 wt%, 0.5 wt %, 0.75 wt %, 1 wt %, 1.5 wt %, 2 wt %, 2.5 wt %, 3 wt %, 3.5wt %, 4 wt %, 4.5 wt % or 5 wt % based on the weight of the reactionmixture.

If added, the supplemental mixture of catalysts can be added slowly, forexample the mixture can be added drop-wise to the reaction vessel. Thereaction vessel then can be held for a period of time at the sametemperature, for example at 85-140° C., such as at or about 85° C., 90°C., 95° C., 100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130°C., 135° C. or 140° C. The period of time that the first reaction vesselcan be held can vary from between 1 and 4 hours, such as 1, 2, 3 or 4hours. For example, the reaction can be allowed to proceed for 3 hoursor for about 3 hours.

After the supplemental mixture of catalysts is added and held in thefirst reaction vessel for the period of time, such as 3 hours, theviscosity of the composition in the reaction vessel can be adjusted. Forexample, the viscosity can be increased by slowly adding a rheologyadjusting component, such as, for example, water, an alcohol, an alkalicompound, an amine or a combination thereof, to the reaction vessel.Addition of the rheology adjusting component increases the viscosity ofthe resulting NAD such that addition of a relatively large amount of theNAD, such as 15 wt % to 60 wt % based on the weight of the ink, to anink will not adversely affect the desired viscosity range of the ink.

The alcohol that can be used as or in the rheology adjusting componentcan be, for example, a C₁-C₆ alcohol, such as isopropanol (isopropylalcohol), butanol, ethanol and methanol. Suitable alkali compounds thatcan used as or in the rheology adjusting component include metalhydroxides. Exemplary metal hydroxides include potassium hydroxide,sodium hydroxide and calcium hydroxide. Exemplary amines that can beused as or in the rheology adjusting component can be a primary amine(e.g., ethyl amine), secondary amine (e.g., diethylamine) or tertiaryamine (e.g., triethylamine). For example, a rheology adjusting componentcan contain a mixture of water, an alcohol, an alkali compound and anamine. An exemplary rheology adjusting component contains water,potassium hydroxide, such as 85 wt % potassium hydroxide, isopropanoland diethylamine.

The rheology adjusting component generally contains water. Because therheology adjusting component is added at a relatively high temperature,however, a large part of the water of the rheology adjusting componentcan be distilled off and removed, resulting in an essentiallynon-aqueous product. The resulting NAD product usually contains 2.0 wt %or less water, generally 1.0 wt % or less water, but also can contain0.5 wt % or less water, based on the weight of the NAD composition. Theresulting NAD product can contain an amount of water that is between0.001 wt % to 1 wt %, 0.005 wt % to 0.5 wt %, or 0.025 wt % to 0.25 wt%, or 0.01 wt % to 0.1 wt % based on the weight of the composition. Theresulting product also can be anhydrous.

A preferred mixture of constituents in the rheology adjusting componentthat can be used in the acrylic shell polymers and NAD provided hereininclude water, potassium hydroxide, such as 85 wt % potassium hydroxide,isopropanol and diethylamine.

In the synthesis of the acrylic core polymers provided herein, the totalamount of rheology adjusting component as a percentage (%) by weight ofthe reaction mixture (wt %) can be, for example, between from or aboutfrom 0.001 wt % to 2 wt %, such as 0.01 wt % to 0.1 wt %, 0.01 wt % to0.2 wt %, 0.01 wt % to 0.3 wt %, 0.01 wt % to 0.4 wt %, 0.01 wt % to 0.5wt %, 0.01 wt % to 0.6 wt %, 0.01 wt % to 0.7 wt %, 0.01 wt % to 0.8 wt%, 0.01 wt % to 0.9 wt %, 0.01 wt % to 1.0 wt %, 0.01 wt % to 1.1 wt %,0.01 wt % to 1.2 wt %, 0.01 wt % to 1.3 wt %, 0.01 wt % to 1.4 wt %,0.01 wt % to 1.5 wt %, 0.01 wt % to 1.6 wt %, 0.01 wt % to 1.7 wt %,0.01 wt % to 1.8 wt %, 0.01 wt % to 1.9 wt %, 0.1 wt % to 0.2 wt %, 0.1wt % to 0.3 wt %, 0.1 wt % to 0.4 wt %, 0.1 wt % to 0.5 wt %, 0.1 wt %to 1.0 wt %, 0.1 wt % to 1.5 wt %, 0.1 wt % to 2.0 wt %, 0.5 wt % to 1.0wt %, 0.5 wt % to 1.1 wt %, 0.5 wt % to 1.2 wt %, 0.5 wt % to 1.3 wt %,0.5 wt % to 1.4 wt %, 0.5 wt % to 1.5 wt %, 0.5 wt % to 1.6 wt %, 0.5 wt% to 1.7 wt %, 0.5 wt % to 1.8 wt %, 0.5 wt % to 1.9 wt %, 0.5 wt % to2.0 wt %, 1.0 wt % to 1.1 wt %, 1.0 wt % to 1.2 wt %, 1.0 wt % to 1.3 wt%, 1.0 wt % to 1.4 wt %, 1.0 wt % to 1.5 wt %, 1.0 wt % to 1.6 wt %, 1.0wt % to 1.7 wt %, 1.0 wt % to 1.8 wt %, 1.0 wt % to 1.9 wt %, 1.0 wt %to 2.0 wt %, 1.2 wt % to 1.3 wt %, 1.2 wt % to 1.4 wt %, 1.2 wt % to 1.5wt %, 1.2 wt % to 1.6 wt %, 1.2 wt % to 1.7 wt %, 1.2 wt % to 1.8 wt %,1.2 wt % to 1.9 wt %, 1.2 wt % to 2.0 wt %, 1.5 wt % to 1.6 wt %, 1.5 wt% to 1.7 wt %, 1.5 wt % to 1.8 wt %, 1.5 wt % to 1.9 wt %, 1.5 wt % to2.0 wt %, 1.7 wt % to 1.8 wt %, 1.7 wt % to 1.9 wt %, 1.7 wt % to 2.0 wt%, 1.8 wt % to 2.0 wt %, and 1.9 wt % to 2.0 wt %, by weight of thereaction mixture. Generally, the reaction mixture contains less than 2.0wt % rheology adjusting component. For example, the reaction mixturesprovided herein contain a rheology adjusting component in an amount thatis at or about 0.01 wt %, 0.05 wt %, 0.1 wt %, 0.2 wt %, 0.25 wt %, 0.3wt %, 0.4 wt %, 0.5 wt %, 0.6 wt %, 0.7 wt %, 0.75 wt %, 0.8 wt %, 0.9wt %, 1.0 wt %, 1.1 wt %, 1.2 wt %, 1.25 wt %, 1.3 wt %, 1.4 wt %, 1.5wt %, 1.6 wt %, 1.7 wt %, 1.75 wt %, 1.8 wt %, 1.9% or 2.0 wt % based onthe weight of the reaction mixture. Because the rheology adjustingcomponent, which generally contains water, can be added to the reactionvessel at high temperatures, e.g., 100° C. to 140° C., such as at orabove 120° C. or at or above about 120° C., water from the rheologyadjusting component can distill off during the reaction, thus reducingthe total residual amount of water present in the acrylic core polymerand/or reaction mixture.

The rheology adjusting component can be pre-mixed in a separate mixingvessel and slowly added to the reaction vessel to control any foamingthat can occur. After addition of the rheology adjusting component, thereaction vessel can be held at the same temperature, e.g., 100° C. to140° C., for example at 120° C. or about 120° C., for 1 to 4 hours,e.g., 1, 1.5, 2, 2.5, 3, 3.5 or 4 hours, such as 1 hour or about 1 hour.

The addition of the rheology adjusting component results in a NAD havingincreased viscosity when compared to an NAD prepared without theaddition of a rheology adjusting component. NADs prepared withoutaddition of the rheology adjusting component described herein have afairly low viscosity. For example, without addition of the rheologyadjusting component described herein, the viscosity of the resulting NADcan be less than 10 Pa·s at a shear rate of 50 sec⁻¹ (as measured on aTA Instruments AR 1000 rotational viscometer). Addition of the rheologyadjusting component as described herein results in a NAD having aviscosity of at or about 10 Pa·s to at or about 150 Pa·s at a shear rateof 50 sec⁻¹. The viscosity of the NAD can be greater than 10 Pa·s, 15Pa·s, 20 Pa·s, 25 Pa·s, 30 Pa·s, 35 Pa·s, 40 Pa·s, 45 Pa·s, 50 Pa·s, 55Pa·s, 60 Pa·s, 65 Pa·s, 70 Pa·s, 75 Pa·s, 80 Pa·s, 85 Pa·s, 90 Pa·s, 95Pa·s, 100 Pa·s, 110 Pa·s, 120 Pa·s, 130 Pa·s, 140 Pa·s or 150 Pa·s at ashear rate of 50 sec⁻¹. The viscosity of the NAD can be in a range of 10Pa·s to 40 Pa·s, or 20 Pa·s to 50 Pa·s, or 30 Pa·s to 60 Pa·s, 40 Pa·sto 80 Pa·s, or 50 Pa·s to 90 Pa·s, or 60 Pa·s to 100 Pa·s, or 70 Pa·s to120 Pa·s, or 80 Pa·s to 130 Pa·s, or 100 Pa·s to 150 Pa·s at a shearrate of 50 sec⁻¹.

The reaction mixture can be monitored for the presence of residualacrylic monomers or other co-monomers. The reaction mixture can bemonitored by any method known to those of skill in the art. The reactionmixture can be monitored by, for example, chromatography. An exemplarymethod of chromatography that can be used is gas chromatography. Thereaction is allowed to proceed until a desired level of residualmonomers is reached. The level can be less than 5 wt %, or lest than 1wt %, or less than 0.5 wt %, or less than 0.1 wt % of the initial valueof monomer present.

After a desired level of residual monomers is reached, the reactionvessel can be cooled down to allow discharge of the resulting acryliccore/shell polymer. For example, the reaction vessel can be cooled downto a temperature of between 30° C. to 90° C. The reaction vessel can becooled down to at or about room temperature. For example, the reactioncan be cooled down to 20° C. to 25° C.

The particle size of the acrylic core/shell polymer particles can impactthe final printing ink properties when the NAD is added to thelithographic printing ink. Acrylic core/shell polymer particles that aretoo large could lead to a low gloss level of the lithographic printedink whereas acrylic core/shell polymer particles that are too smallcould have a negative impact on the immediate rub resistance and fastconversion properties of the lithographic printed ink.

Reaction conditions and reactants can influence primary particle size ofthe acrylic core/shell polymer particles. For example, reactiontemperature during core/shell polymer formation has a measurable effecton core/shell polymer particle size. It has been observed that there isa correlation with increasing reaction temperature and decreasing theresulting core/shell polymer particle size. As the reaction temperatureincreases, the resulting acrylic core/shell polymer particle sizedecreases. It has be determined that reaction temperatures between 85°C. to 140° C., such as at or about 85° C., 90° C., 95° C., 100° C., 105°C., 110° C., 115° C., 120° C., 125° C., 130° C., 135° C. or 140° C., fora period of time of between 1 and 5 hours, such as 1, 1.5, 2, 2.5, 3,3.5, 4, 4.5 or 5 hours, such as 3 or 4 hours, generally results in anacrylic core/shell polymer where typically 90% of the particles of theacrylic core/shell polymer are less than 3 microns. Particularly, atreaction temperatures of at or about 120° C. or higher, about 50% ormore of the particles of the acrylic core/shell polymer are less than1.5 microns.

A direct correlation exists between the amount of alkyl methacrylatemonomer present in the acrylic core polymer and/or the acrylic shellpolymer and particle size. As the amount of alkyl methacrylate monomer,particularly methyl methacrylate, in the acrylic core polymer and/or theacrylic shell polymer increases, the average particle size of thecore/shell polymer particle increases, and thus higher methylmethacrylate levels favors larger particles.

The particle size and particle size distribution can be analyzed usingany method known in the art. For example, a volume average particle sizecan be measured by using a Coulter Counter™ particle size analyzer(manufactured by Beckman Coulter Inc.). The median particle size alsocan be measured using conventional laser diffraction techniques. Anexemplary laser diffraction technique uses a Mastersizer 2000 particlesize analyzer (Malvern Instruments LTD., Malvern, Worcestershire, UnitedKingdom), particularly a Hydro S small volume general-purpose automatedsample dispersion unit. All functions of the particle counting can becontrolled by the system software in either fully automatic operationvia standard operating procedure directions or by manual operation viaon-screen operating dialogues. In an exemplary method, the NAD sample tobe evaluated is diluted with cyclohexane to disperse the particles and arefractive index of 1.55 is used. The sample is stirred at up to 3500rpm after dilution of the sample to achieve an appropriate laserobscuration, particle size is measured using laser diffraction,generating a particle size distribution curve as well as data withrespect to the volume median diameter, D(v,0.5), which is the diameterwhere 50% of the distribution is above and 50% is below, the D(v,0.9)value, where 90% of the volume distribution is below this value, andD(v,0.1), where 10% of the volume distribution is below this value. Thespan of the particle size also can be determined, based on the width ofthe distribution based on the 10%, 50% and 90% quantile.

The mean particle size also can be measured using a Zetasizer Nano ZSdevice (Malvern Instruments LTD., Malvern, Worcestershire, UnitedKingdom) utilizing the Dynamic Light Scattering (DLS) method. The DLSmethod essentially consists of observing the scattering of laser lightfrom particles, determining the diffusion speed and deriving the sizefrom this scattering of laser light, using the Stokes-Einsteinrelationship.

An analysis of the particle size of the acrylic core/shell polymerparticles in the NAD shows that typically 90% of the particles of theacrylic core/shell polymer in the NAD are less than 3 microns.Particularly, 50% of the particles of the acrylic core/shell polymer inthe NAD are less than 1.5 microns or less than 1 micron. In someinstances, greater than 50% of the particles of the acrylic core/shellpolymer in the NAD are less than 1 micron. The average particle size ofthe acrylic core/shell polymer particles in the NAD can be in the rangeof at or about 300 nm to at or about 1300 nm. In particular, the averageparticle size of the acrylic core/shell polymer particles in the NAD canbe in the range of at or about 300 nm to at or about 600 nm, or at orabout 400 nm to at or about 800 nm, or at or about 500 nm to at or about900 nm, or at or about 600 nm to at or about 1200 nm.

The amounts of acrylic core polymer and acrylic shell polymer in theacrylic core/shell polymer were determined. Any method known in the artcan be used to determine the amounts of acrylic core polymer and acrylicshell polymer can be used. Spectrographic methods commonly are used inthe art. For example, Wang et al. (eXPRESS Polymer Letters 4(11):670-680 (2010)) describes methods of characterizing core/shell polymersusing Fourier transform infrared (IR) measurements. Fei et al.(Chalcogenide Letters 8(8): 499-504 (2011)) describes spectralcharacterization of core/shell polymers using IR spectroscopic analysis.Auguiar et al. (Macromolecules 32(20): 6767-6771 (1999) describescharacterization of core/shell polymers using transmission electronmicroscopy, dynamic mechanical thermal analysis light scattering, IRspectroscopy and differential scanning calorimetry. For IRspectrographic analysis, a Thermo Nicolet Magna 550 with a Golden Gatediamond crystal micro attenuated total reflection (ATR) device or animmersion transflectance probe can be used. For near IR spectroscopy(NIR), a Foss XDS NIR spectrometer can be used to analyze the polymerparticles to determine the amount of acrylic core polymer and acrylicshell polymer present. Analysis also can include software for automationor reaction monitoring, such as the FOSS XDS Interactance OptiProbe®Analyzer. Software known in the art can be used to assess thespectroscopic data. Exemplary software includes TQ Analyst (ThermoFisher Scientific, Waltham, Mass.), Unscrambler® X (CAMO Software AS,Woodbridge, N.J.) and irAnalyze software (LabCognition, Ft. Myers,Fla.).

The acrylic core/shell polymer particles in the NAD can contain from ator about 15 wt % to at or about 75 wt % or from at or about 20 wt % toat or about 60 wt % acrylic core polymer based on the weight of theacrylic core/shell polymer particle. The acrylic core/shell polymerparticles in the NAD can contain 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27wt %, 28 wt %, 29 wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35wt %, 36 wt %, 37 wt %, 38 wt %, 39 wt %, 40 wt %, 41 wt %, 42 wt %, 43wt %, 44 wt %, 45 wt %, 46 wt %, 47 wt %, 48 wt %, 49 wt %, 50 wt %, 51wt %, 52 wt %, 53 wt %, 54 wt %, 55 wt %, 56 wt %, 57 wt %, 58 wt %, 59wt %, 60 wt %, 61 wt %, 62 wt %, 63 wt %, 64 wt %, 65 wt %, 66 wt %, 67wt %, 68 wt %, 69 wt %, 70 wt %, 71 wt %, 72 wt %, 73 wt %, 74 wt % or75 wt % acrylic core polymer, based on the weight of the acryliccore/shell polymer.

The acrylic core/shell polymer particles in the NAD can contain from ator about 15 wt % to at or about 75 wt % or from at or about 20 wt % toat or about 60 wt % acrylic shell polymer based on the weight of theacrylic core/shell polymer particle. The acrylic core/shell polymerparticles in the NAD can contain 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27wt %, 28 wt %, 29 wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35wt %, 36 wt %, 37 wt %, 38 wt %, 39 wt %, 40 wt %, 41 wt %, 42 wt %, 43wt %, 44 wt %, 45 wt %, 46 wt %, 47 wt %, 48 wt %, 49 wt %, 50 wt %, 51wt %, 52 wt %, 53 wt %, 54 wt %, 55 wt %, 56 wt %, 57 wt %, 58 wt %, 59wt %, 60 wt %, 61 wt %, 62 wt %, 63 wt %, 64 wt %, 65 wt %, 66 wt %, 67wt %, 68 wt %, 69 wt %, 70 wt %, 71 wt %, 72 wt %, 73 wt %, 74 wt % or75 wt % acrylic shell polymer, based on the weight of the acryliccore/shell polymer.

The acrylic core/shell polymer particles can have an averagecore-to-shell ratio of from at or about 0.60 to at or about 2.0. Forexample, an acrylic core/shell polymer particle containing 62.2% acryliccore polymer and 37.8% acrylic shell polymer has a core/shell ratio ofabout 1.65. An acrylic core/shell polymer particle containing 40%acrylic core polymer and 60% acrylic shell polymer has a core/shellratio of about 0.67. The acrylic core/shell polymer particles can havean average core-to-shell ratio of from at or about 0.60 to at or about1.65 at or about 0.97 to at or about 1.24 or from at or about 1.00 to ator about 1.70 or from at or about 1.50 to at or about 1.90. Preferredcore/shell ratios include ratios between 1.20 and 1.80, or between 1.30and 1.70, or between 1.40 and 1.65 or between 1.55 and 1.75. The acryliccore/shell polymer particles of the NAD can have an averagecore-to-shell ratio of 1.0, 1.025, 1.05, 1.075, 1.1, 1.125, 1.15, 1.175,1.2, 1.225 1.25, 1.275, 1.3, 1.325, 1.35, 1.375, 1.4, 1.425, 1.45, 1.4751.5, 1.525, 1.55, 1.575, 1.6, 1.625, 1.65, 1.675 or 1.7.

The NAD composition can contain an essentially non-aqueous organicsolvent containing from at or about 15 wt % to at or about 35 wt %acrylic core polymer based on the weight of the NAD and from at or about15 wt % to at or about 35 wt % acrylic shell polymer based on the weightof the NAD. The acrylic core polymer and the acrylic shell polymer canmake up the acrylic core/shell polymer particles dispersed in the NAD.The NAD can contain from at or about 30 wt % to at or about 70 wt %acrylic core/shell polymer particles based on the weight of the NAD. TheNAD can contain from at or about 30 wt % to at or about 70 wt %essentially non-aqueous organic solvent based on the weight of the NAD.

The NAD composition can contain a rheology adjusting component. Anexemplary rheology adjusting component generally contains water, analcohol, an alkali compound, an amine or a mixture thereof. A preferredrheology adjusting component contains a mixture of water, potassiumhydroxide, isopropanol and diethylamine. The ratio of alkali compound toamine can be between 0.66 to 1.5 or between 0.75 to 1.25. The ratio ofwater to amine can be between 2 to 16 or between 3 to 9. The ratio ofwater to alcohol can between 3 to 15 or between 4 to 12.5.

The amount of rheology adjusting component can be present in the NADcomposition in an amount from or about from 0.001 wt % to 5 wt % basedon the weight of the NAD composition. The NAD composition can contain0.001 wt %, 0.005 wt %, 0.01 wt %, 0.025 wt %, 0.05 wt %, 0.075 wt %,0.1 wt %, 0.2 wt %, 0.3 wt %, 0.4 wt %, 0.5 wt %, 0.6 wt %, 0.7 wt %,0.8 wt %, 0.9 wt %, 1.0 wt %, 1.1 wt %, 1.2 wt %, 1.3 wt %, 1.4 wt %,1.5 wt %, 1.6 wt %, 1.7 wt %, 1.8 wt %, 1.9 wt %, 2.0 wt %, 2.1 wt %,2.2 wt %, 2.3 wt %, 2.4 wt %, 2.5 wt %, 2.6 wt %, 2.7 wt %, 2.8 wt %,2.9 wt %, 3.0 wt %, 3.1 wt %, 3.2 wt %, 3.3 wt %, 3.4 wt %, 3.5 wt %,3.6 wt %, 3.7 wt %, 3.8 wt %, 3.9 wt %, 3.0 wt %, 4.1 wt %, 4.2 wt %,4.3 wt %, 4.4 wt %, 4.5 wt %, 4.6 wt %, 4.7 wt %, 4.8 wt %, 4.9 wt % or5.0 wt % rheology adjusting component based on the weight of the NADcomposition.

Pre-Formed Polymers

The NAD can be prepared by selecting a pre-formed acrylic shell polymerthat is soluble in the continuous phase essentially non-aqueous solventand compatible with the acrylic core polymer to be synthesized, and thengenerating an acrylic core polymer from monomers selected to form anacrylic core polymer that is insoluble in the essentially non-aqueoussolvent, but soluble in the shell polymer. By reacting the pre-formedacrylic shell polymer with the acrylic core polymer in the essentiallynon-aqueous solvent at elevated temperature, such as between 85° C. to140° C., the acrylic core polymer preferentially interacts with theacrylic shell polymer to form core/shell polymers, particularlycore/shell polymer particles, generating a dispersion of core/shellpolymer in the continuous phase essentially non-aqueous solvent.

In selecting a pre-formed acrylic shell polymer, polymers that includeone or more monomer or comonomer units that contain hydrocarbon chainsand one or more monomer or comonomer units that contain one or morefunctional groups, such as carboxyl groups, hydroxyl groups or vinylgroups are preferred. Exemplary monomer units containing carboxyl groupsthat can be present in the pre-formed acrylic shell polymer are acrylicacid and substituted acrylic acids (e.g., n-butyl acrylate), methacrylicacid and substituted methacrylic acids (e.g., isobutyl methacrylate,dodecyl methacrylate, methyl methacrylate and n-butyl methacrylate),itaconic acid and substituted itaconic acids, and maleic acid andsubstituted maleic acids. The monomer units can contain hydroxyl groups.Exemplary monomer units containing hydroxyl groups that can be presentin the pre-formed acrylic shell polymer include 2-hydroxy ethylacrylates, 2-hydroxy ethyl methacrylates, 2-hydroxy propyl acrylates and2-hydroxy propyl methacrylates. Preferably, the pre-formed acrylic shellpolymer is selected to include one or more C₁-C₁₂ alkyl methacrylates asmonomer units. Exemplary C₁-C₁₂ alkyl methacrylates that can be presentin the shell polymers are isobutyl methacrylate and dodecylmethacrylate.

The selected pre-formed acrylic shell polymer can be added to acontinuous phase essentially non-aqueous solvent in a reaction vessel,heated to 85° C.-140° C., such as at or about 85° C., 90° C., 95° C.,100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130° C., 135° C.or 140° C., and the acrylic core polymer can be synthesized in situ overa period of time by addition to the reaction vessel a mixture of acrylicmonomers and a mixture of catalysts as described above, where thesynthesized acrylic core polymer, being insoluble in the continuousphase essentially non-aqueous solvent, migrates from the continuousphase into the acrylic shell polymer, “filling it in” and generating adispersion of core/shell polymer particles.

The viscosity of the composition can be modified by slowly adding to thereaction mixture a rheology adjusting component, such as, for example,water, an alcohol, an alkali compound, an amine or a combinationthereof. Addition of the rheology adjusting component increases theviscosity of the resulting NAD such that addition of a relatively largeamount of the NAD, such as 15 wt % to 60 wt % based on the weight of theink, to an ink will not adversely affect the desired viscosity range ofthe ink.

The alcohol that can be used as or in the rheology adjusting componentcan be, for example, a C₁-C₆ alcohol, such as isopropanol (isopropylalcohol), butanol, ethanol and methanol. Suitable alkali compounds thatcan used as or in the rheology adjusting component include metalhydroxides. Exemplary metal hydroxides include potassium hydroxide,sodium hydroxide and calcium hydroxide. Exemplary amines that can beused as or in the rheology adjusting component can be a primary amine(e.g., ethyl amine), secondary amine (e.g., diethylamine) or tertiaryamine (e.g., triethylamine). For example, a rheology adjusting componentcan contain a mixture of water, an alcohol, an alkali compound and anamine. An exemplary rheology adjusting component contains water,potassium hydroxide, such as 85 wt % potassium hydroxide, isopropanoland diethylamine.

The NAD also can be prepared by selecting a pre-formed acrylic shellpolymer that is soluble in the continuous phase essentially non-aqueoussolvent and selecting a pre-formed acrylic core polymer that isinsoluble in the essentially non-aqueous solvent, but soluble in theshell polymer. By reacting the pre-formed acrylic shell polymer with thepre-formed acrylic core polymer in the essentially non-aqueous solventat elevated temperature, such as between 85° C.-140° C., the acryliccore polymer preferentially interacts with the acrylic shell polymer,migrating from the continuous phase essentially non-aqueous solvent intothe acrylic shell polymer to form core/shell polymers, particularlycore/shell polymer particles, generating a dispersion of core/shellpolymer in the continuous phase essentially non-aqueous solvent.

In selecting a pre-formed acrylic shell polymer for this preparationmethod, acrylic polymers that include one or more monomer or comonomerunits that contain hydrocarbon chains and one or more monomer orcomonomer units that contain one or more functional groups, such ascarboxyl groups, hydroxyl groups or vinyl groups are preferred.Exemplary monomer units containing carboxyl groups that can be presentin the pre-formed acrylic shell polymer are acrylic acid and substitutedacrylic acids (e.g., n-butyl acrylate), methacrylic acid and substitutedmethacrylic acids (e.g., isobutyl methacrylate, dodecyl methacrylate,methyl methacrylate and n-butyl methacrylate), itaconic acid andsubstituted itaconic acids, and maleic acid and substituted maleicacids. The monomer units can contain hydroxyl groups. Exemplary monomerunits containing hydroxyl groups that can be present in the pre-formedacrylic shell polymer include 2-hydroxy ethyl acrylates, 2-hydroxy ethylmethacrylates, 2-hydroxy propyl acrylates and 2-hydroxy propylmethacrylates. Preferably, the pre-formed acrylic shell polymer isselected to include one or more C₁-C₁₂ alkyl methacrylates as monomerunits. Exemplary C₁-C₁₂ alkyl methacrylates that can be present in theshell polymers are isobutyl methacrylate and dodecyl methacrylate.

In selecting a pre-formed acrylic core polymer for this preparationmethod, acrylic polymers that include one or more monomer or comonomerunits that contain hydrocarbon chains, such as C₁-C₆ alkyl methacrylateand/or C₁-C₆ alkyl acrylate are preferred. The pre-formed acrylic corepolymer is selected so that it is insoluble in the continuous phase ofthe essentially non-aqueous solvent but is soluble in the acrylic shellpolymer selected above, which is soluble in the continuous phase of theessentially non-aqueous solvent and forms particles of acryliccore/shell polymer in the continuous phase of the essentiallynon-aqueous solvent. Exemplary monomer units containing C₁-C₆ alkylmethacrylate include methyl methacrylate, ethyl methacrylate, n-propylmethacrylate and n-butyl methacrylate. Exemplary monomer unitscontaining C₁-C₆ alkyl acrylate include methyl acrylate, ethyl acrylate,n-propyl acrylate and n-butyl acrylate.

The selected pre-formed acrylic shell polymer can be added to acontinuous phase essentially non-aqueous solvent in a reaction vessel,heated to 85° C.-140° C., such as at or about 85° C., 90° C., 95° C.,100° C., 105° C., 110° C., 115° C., 120° C., 125° C., 130° C., 135° C.or 140° C., and the selected pre-formed acrylic core polymer can beadded to the reaction mixture while maintaining or returning thetemperature of the reaction mixture to between 85° C.-140° C. Becausethe selected pre-formed acrylic core polymer is insoluble in thecontinuous phase essentially non-aqueous solvent but soluble in theacrylic shell polymer, the acrylic core polymer migrates from thecontinuous phase into the acrylic shell polymer, “filling it in” andgenerating a dispersion of core/shell polymer particles.

The viscosity of the NAD composition can be increased by adding arheology adjusting component, such as, e.g., water, an alcohol, analkali compound, an amine or a combination thereof. The alcohol that canbe used as or in the rheology adjusting component can be, for example, aC₁-C₆ alcohol, such as isopropanol (isopropyl alcohol), butanol, ethanoland methanol. Suitable alkali compounds that can used as or in therheology adjusting component include metal hydroxides. Exemplary metalhydroxides include potassium hydroxide, sodium hydroxide and calciumhydroxide. Exemplary amines that can be used as or in the rheologyadjusting component can be a primary amine (e.g., ethyl amine),secondary amine (e.g., diethylamine) or tertiary amine (e.g.,triethylamine). For example, a rheology adjusting component can containa mixture of water, an alcohol, an alkali compound and an amine. Anexemplary rheology adjusting component contains water, potassiumhydroxide, isopropanol and diethylamine.

It should be noted that the aforementioned NAD and its synthesis andpreparation represents a preferred embodiment in the present printingink formulations, but it is understood that other, other methods ofpreparing a NAD, and traditionally prepared NADs, could be used alone orin combination with the aforementioned NAD to produce printing inkcompositions having good printing, setting and drying properties.

E. Lithographic Printing Inks

The NADs can be incorporated into lithographic printing inks. Thelithographic printing inks containing one or more NADs of the presentinvention will usually include at least one pigment, the nature of whichis not critical to the present invention, and which can be chosen fromany of those pigments well known to those skilled in the art. In generalterms, a lithographic printing ink should have a low surface tension, bewater-repellent and be capable of emulsifying with a fount solution. Theformulation of printing inks for offset lithographic printing is verywell known, and is described in considerable detail, in the art. Forexample, see The Printing Ink Manual (5^(th) ed., Leach et al. eds.(2009), pages 342-452), and U.S. Pat. Nos. 5,382,282; 5,725,646 and6,489,375.

1. Sheetfed Printing Inks

One class of lithographic printing inks that can be formulated toinclude NADs are sheetfed printing inks. The NADs can be incorporatedinto conventional sheetfed printing inks and into waterless printingsheetfed printing inks. When printing substrates using a sheetfedlithography process, it is desirable to be able to further process thefreshly printed sheet as quickly as possible, while at the same timestill allowing the sheetfed printing inks to settle in and on thesubstrate in order for the desired print gloss and print resolution tobe achieved.

Lithographic printing inks formulated for sheetfed printingapplications, in both conventional and waterless printing sheetfedprinting inks, generally include one or more components that react withair to dry. Conventional off-set sheetfed printing inks usually containa resin and/or drying oil that reacts with oxygen in the air toinitially form a film on the surface of the ink film when the sheetfedprinting ink is printed on the substrate and to cure the final printedink over time.

Sheetfed printing inks normally set and dry as a result of anoxido-polymerization process. The oxygen surrounding the ink film reactswith the free C═C double bonds present in the ink system which allowsthe formation of a high molecular weight polymer. This chemical dryingprocess can be assisted by addition of a metal catalyst (metal drier).In the absence of metal catalyst, this process is very slow and couldlast anywhere from several days to weeks depending on the inkformulation. When drying is slow, the sheetfed printing ink does not setproperly on the printed substrate. In a sheetfed lithographic process,printed papers are laminated one after another, so that if the sheetfedprinting ink is not properly set, the printing ink from one sheet cantransfer to the back surface of the next paper.

The introduction of metal catalyst (metal drier) significantly increasesthe setting and drying process and allows the printing ink film to setand to be dried anywhere from several hours to 1 or 2 days. Sheetfedprinting inks containing metal catalysts, however, have two majordrawbacks. Firstly, the sheetfed printing inks are prone to prematurepolymerization on the printing press, which can necessitate timeconsuming and costly frequent press cleaning, or prematurepolymerization in storage containers, usually in the form of skinformation, which leads to printing ink wastage and possiblecontamination. Secondly, the metal catalysts generally are notuser-friendly due to associated toxicity issues. Accelerated drying maybe possible if electron beam curing or UV irradiation is used after theprinting step, but for both applications, special printing inks andspecial equipment is required, which introduces additional costs andpotential difficulties in the sheetfed printing process.

Provided are compositions and methods for improving the setting anddrying, as evidenced by improved rub resistance, of conventionalsheetfed printing ink compositions and waterless printing sheetfedprinting ink compositions containing NAD formulated for sheetfedapplications and printing using a sheetfed lithographic process.Including an amount of NAD that is at or about 11 wt % to 60 wt %, or 12wt % to 50 wt %, preferably 25 wt % to 35 wt % based on the weight ofthe ink composition, of NAD, particularly of a NAD provided herein, in asheetfed printing ink formulation, imparts sufficient setting drying andmechanical resistance of the printed ink film that metal catalysts canbe eliminated. It is possible to incorporate the NAD into a sheetfedprinting ink composition containing metal catalysts in order to impartimproved setting and drying and rub resistance properties, but thepreferred embodiment would be to introduce sufficient NAD in thesheetfed printing ink composition that it will set and dry in anacceptable time without the need for metal catalysts. In an alternateembodiment, the amount of NAD included in the sheetfed printing inkcomposition can be maintained at a level greater than 11 wt %, such asgreater than 15 wt % or greater than 20 wt %, or at a level between 25wt % to 60 wt %, based on the weight of the ink composition, or reducedto a lower level, and a reduced amount of metal drier could be usedrather than eliminating the drier altogether. As demonstrated in theExamples, sheetfed printing inks containing from 15 wt % to 60 wt % NADand no metal drier or anti-oxidant exhibit rub resistance values verysoon after printing, such as at 15 minutes, as well as after 1 hour, 2hours and 24 hours, that are equal to or better than comparativestandard sheetfed printing inks that contain drier and anti-oxidant.Sheetfed printing ink compositions without drier can be formulated tocontain between 15 wt % to 60 wt % NAD based on the weight of the inkcomposition and such sheetfed printing ink compositions exhibit goodsetting and drying properties, particularly as measured by rubresistance.

Also provided are conventional sheetfed printing ink compositions andwaterless printing sheetfed printing ink compositions containing NADthat do not require metal catalyst or its equivalent to properly set anddry, as exhibited by acceptable rub resistance values. The sheetfedprinting ink compositions can be characterized by having a viscosity of20 Pa·s to 150 Pa·s at a shear rate of 50 s⁻¹, or a viscosity of 40 Pa·sto 100 Pa·s at a shear rate of 50 s⁻¹. The viscosity can be measuredusing an AR 1000 rotational viscometer (TA Instruments, New Castle,Del., USA). The ink compositions also can be characterized by exhibitinga rub resistance rating of less than 2 after 24 hours, and/or a rubresistance rating of less than 2 after 2 hours, and/or a rub resistancerating of less than 2 after 15 minutes.

In the international patent publications WO2009/155201 andWO2011/014826, the use of a non-aqueous dispersion of core/shell polymerparticles is described. WO09155201 states that addition of NAD inconjunction with a metal drier can increase the drying speed of thesheetfed offset ink. Examples are limited, however, to an amount of NADup to 15 wt % based on the weight of the ink, and using a metal catalystto polymerize the ink. WO2011/014826 describes reducing the odor ofnon-aqueous dispersions and states that its non-aqueous dispersion ofcore/shell polymers can be incorporated into a standard sheetfedprinting ink at a 10 wt % level. WO2011/014826 provides no examples ofsuch sheetfed printing inks or their use.

NADs often exhibit a fairly low viscosity (for example about 10 Pa·s ata shear rate of 50 sec⁻¹ as measured on a TA Instruments AR 1000rotational viscometer). Introducing NADs having this low of a viscosityat increased levels into a sheetfed printing ink may be impracticalsince the resulting printing ink may not be viscous enough for goodperformance when used in a lithographic sheetfed printing process. In apreferred embodiment, the NAD used in the sheetfed printing inks of thepresent application are modified to have a higher viscosity (for exampleat or about 20 Pas to at or about 150 Pa·s at a shear rate of 50 sec⁻¹).By using a more viscous NAD, a greater amount of NAD can be included inthe sheetfed printing ink composition without significantly decreasingthe final viscosity of the sheetfed printing ink composition. Thisallows the formulator to increase the total NAD content in a finishedsheetfed printing ink to a level greater than 11 wt %, or 15 wt % basedon weight of the ink composition, such as at or about 16 wt % to 60 wt%, more preferably at or about 25 wt % to 35 wt % based on weight of theink composition, such that the resulting printing ink has a viscosityconducive for good sheetfed lithographic process performance, and thatwill quickly set and provide apparent dryness as evidenced by increasedrub resistance without the need for metal driers.

As discussed above, one method to increase the viscosity of the NAD isto introduce a rheology adjusting component, such as water, an alcohol,an alkali compound or an amine or a combination thereof, such as amixture of water, an alkali hydroxide, an alkylamine and an alcohol,during polymerization of or formation of the acrylic core/shell polymerparticles. Any other method for increasing the viscosity of anon-aqueous dispersion of polymer particles known in the art also can beused.

Conventional sheetfed printing ink compositions and waterless printingsheetfed printing ink compositions that incorporate NAD can be preparedby any method known in the art. For example, pigments, resins, such asalkyd resins, and varnishes can be pre-mixed using a mixer or vibrationshaker device. This mixture then can be milled and dispersed. Anycommercially available devices can be used to mix and disperse thecomponents. Examples of such equipment and devices include an agitatormill, an attritor grinding mil, a ball mill, a Cobol™ mill, a colloidmill, a Dyno® mill, a flow jet mill, a high-speed disperser, ahomogenizer, a Microfluidizer®, a pearl mill, a sand grinder, a sandmill, an ultrafine mill, a three-roll mill, a two-roll mill, and anultrasonic wave homogenizer, and these can be used alone or incombination of two or more. Preferably a two-roll or three-roll mill isused.

The milling can be repeated a number of times until a desired particlesize is achieved. For example, the mixture can be milled to obtain agrind not higher than 10 to form a printing ink concentrate. The millingcan be performed until about 90% of the particles are of a size lessthan 10 μm, or until about 90% of the particles are of a size less than5 μm, or until at least 50% of the particles are of a size of 2.5 μm orless.

Any additives to be added to the sheetfed printing ink composition, suchas wax paste, anti-set off paste, water fighter, emulsifier andanti-oxidants, and the NAD then can be added to this printing inkconcentrate and the mixture can be mixed to yield a homogeneous printingink composition. The mixing can be done using any standard mixing methodor instrument, such as a paddle mixer or paint shaker device to formfinished printing inks.

In general terms, a sheetfed lithographic printing ink should have a lowsurface tension, be water-repellent, be capable of emulsifying with afount solution, and, for conventional sheetfed offset lithography,usually be capable of drying without radiation. These very particularrequirements can be met by careful formulation and choice of the variouscomponents and is well known in the printing ink industry.

The sheetfed printing ink compositions containing NAD usually include apigment. The type of pigment included will depend upon the kind of inkbeing formulated. Lithographic printing inks are typically used in fourcolors—magenta, yellow, black, and cyan, which can be formulated toprovide a metallic or a pearlescent appearance. Any of the customaryinorganic and organic pigments can be used in the sheetfed printing inkcompositions of the present invention. Pigments suitable for use in thepresent invention include but are not limited to yellow of the AAA, AAOAand AAOT type, phthalo-cyanide Blue GS, green shade beta type, permanentred 2B calcium, lithol rubine (4B), rhodamine YS, carbon black metalmodified furnace type (with alkali blue toner) chrome yellow, ironblues, iron oxides, titanium dioxide, alumina hydrate, blanc fixe,calcium carbonate, lake pigments, PMTA colors, fluorescent pigments,metallic pigments, clays, naphthols, and other organic pigments. When ablack pigment is used, a blue toner can be included and it generallyreplaces a portion of the vehicle. The pigment can be added to thelithographic sheetfed printing ink composition either as a dry powder,flush, presscake or as a dispersion. When using a pigment flush, aportion of the vehicle can first be used to prepare the flushdispersion. The pigments can be used in an amount dispersable by theformulation. In general, it can be desirable to carry as much pigment inthe ink as possible. A typical range of typical pigment amounts used isapproximately 10 wt % to 50 wt % based on the weight of the printingink.

The sheetfed printing ink typically is dried by oxidative polymerizationof the resins and by incorporation of drying oils, e.g., linseed oil orcastor oil or derivatives thereof, which can pass into the paper in thecourse of printing. The proportion of drying oils in the sheetfed offsetprinting inks can be about 0 wt % to 50 wt %, or about 0.5% wt % to 30wt % based on the weight of the printing ink. The drying reactiontraditionally is accelerated further by addition of drying catalysts(metal driers), which are typically fatty acid salts, such as salts oforganic carboxylic acids, of heavy metals such as cobalt and manganese,e.g., cobalt/manganese linoleate, hexadeconate or octoate (e.g., seeU.S. Pat. Nos. 5,156,674; 6,899,756; 7,811,367). It has been found thataddition of the NAD compositions provided herein can significantlyreduce or eliminate the need for metal driers in the sheetfedlithographic printing ink formulation to improve the setting and dryingof the sheetfed ink composition, as exhibited by increased rubresistance. If not totally replaced by the NAD provided herein, a metaldrier can be included in the sheetfed printing ink composition. Thedrier can be any of the commercially available metal driers, such asthose based on cobalt or manganese or cobalt/manganese combinations. Anumber of cobalt/manganese driers are commercially available ascobalt/manganese linoleate, hexadeconate or octoate. Generally, thecommercial sheetfed printing inks contain metal drier in an amount thatis up to 3 wt %, or less than about 3 wt %, or less than about 2.5 wt %,preferably less than about 1.5 wt % based on the weight of the printingink. Addition of NAD to the sheetfed printing ink composition cansignificantly reduce or eliminate metal drier in the sheetfed printingink.

Additives can be introduced into the sheetfed printing ink in order tomodify the ink properties for specific applications. These additives caninclude, e.g., wax compounds, such as PE wax and/or PTFE wax, pour pointdepressants, surfactants, emulsifying agents, drying agents (e.g., forformulations containing vegetable oils), defoamers, anti-set off agents,lithographic additives, dispersants, solvents, flow agents, thickeners,anti-misting agents, lubricants, anti-settling agents, wetting agents,water fighters, gloss enhancers, UV absorbers, pigment fillers and/oranti-oxidants. These additives are well known to those skilled in theart. When included, additives typically are included in amounts of atleast about 0.001 wt % by weight of the ink, and can be included inamounts of about 5 wt % or more based on the weight of the ink,depending upon their nature. Many sheetfed printing inks are formulatedto use vegetable oils in combination with, or instead of, mineral oils.When mineral oils are present, they generally are selected to have aboiling range between at or about 260° C. to at or about 310° C. Furtherdetails regarding the fundamental characteristics of lithographicsheetfed printing inks can be found, e.g., in The Printing Ink Manual(5^(th) ed., Leach et al. eds. (2009), pages 387-431), the disclosure ofwhich is incorporated herein by reference.

Resins usable in the lithographic sheetfed printing inks of the presentinvention include, for example, natural or processed resins such asrosins, rosin esters, maleic modified resins, rosin modified fumaricresins, dimerized and polymerized rosins, phenolics, rosin modifiedphenolics, terpenes, polyamides, cyclized rubber, acrylics, hydrocarbonsand modified hydrocarbons. Also included among the available resins arethose identified in The Printing Ink Manual, supra.

Any conventional anti-oxidant that does not adversely react withcomponents of a sheetfed printing ink can be used. Exemplaryanti-oxidants include ascorbic acid, astaxanthin, carotene, chroman(3,4-dihydro-2H-1-benzopyran), hexamethylenebis(3,5-di-tert-butyl-4-hydroxyhydro-cinnamate), octadecyl3,5-di-tert-butyl-4-hydroxyhydro-cinnamate, vitamin E and vitamin Eanalogs, mono-tert-butylhydroquinone (MTBHQ) and butylated hydroxytoluene (BHT). Preferred anti-oxidants are MTBHQ and BHT. Generally, thesheetfed printing ink composition can contain less than about 5 wt %anti-oxidant based on the weight of the ink composition, preferably lessthan about 2.5 wt %, or less than about 1.5 wt % anti-oxidant based onthe weight of the ink composition.

The sheetfed printing ink composition can contain a heavy oil, such as amineral oil having a density between 0.85-0.91. An exemplary heavy oilis Printosol 30/40 AP85 from Haltermann (Channelview, Tex.). Generally,the composition can contain heavy oil in an amount that is less thanabout 10 wt %, preferably less than about 5 wt % or less than about 2.5wt % based on the weight of the ink composition.

The sheetfed printing ink includes a resin. Exemplary resins includenatural or modified resins such as rosin, copal, shellac, hardened rosinand rosin esters; synthetic resins such as phenol resin, rosin modifiedphenol resin, 100% phenol resin, maleic acid resin, alkyd resin, epoxymodified alkyd resin, soya/linseed oil alkyd resins, petroleum resin,vinyl resin, acrylic resin, polyamide resin, epoxy resin, aminoalkydresin, polyurethane resin and aminoplastic resin; cellulose derivativessuch as nitrocellulose and ethyl cellulose. Preferred resins includerosin resins, alkyd resins, epoxy modified alkyd resins and soya/linseedoil alkyd resins.

The amount of resin in the sheetfed printing ink composition and theproportion of resin to pigments in the sheetfed printing ink canroutinely be selected in order to adjust parameters that are importantfor the sheetfed printing process, such as, e.g., dispersability,tackiness and viscosity. For a given sheetfed printing ink, viscosityand tackiness usually are mutually dependent, but can also be modifiedindividually in a controlled manner through a specific printing inkformulation. Sheetfed printing inks having too high a degree oftackiness can give rise to picking or sections of the paper tearing.Sheetfed printing inks of low or inadequate tackiness are nottransferred in an appropriate manner in the course of the lithographicprinting process. If the viscosity of the printing ink is to low, it canreadily penetrate the paper, becoming visible on the opposite side ofthe paper. Low viscosity of the sheetfed printing ink also can causesmearing, blotchiness or loss of clarity in the reproduced image. Bycontrast, excessively viscous sheetfed printing inks will not flowappropriately from the filling sources to the rollers. The providedsheetfed printing ink compositions containing NAD are formulated toviscosities required for printing using a sheetfed lithographic printingprocess. Generally, the sheetfed printing ink composition containing NADcan contain a total amount of resin that is from at or about 5 wt % toat or about 50 wt % based on the weight of the ink composition. Thesheetfed printing ink composition containing NAD can contain a totalamount of resin that is from at or about 10 wt % to at or about 40 wt %based on the weight of the ink composition. The sheetfed printing inkcomposition containing NAD can contain resin in an amount that is lessthan about 40 wt % or less than about 35 wt % based on the weight of theink composition.

The sheetfed printing ink composition containing NAD can include a waxpaste, which can include one or more waxes. The waxes generally aredispersed in a vehicle based on a resin, such as rosin resin or alkydresin, to form a wax paste. The wax compound, or combinations of waxcompounds, can provide slip and rub resistance. Any wax known in the artcan be included in the sheetfed printing ink. Exemplary waxes includepolytetrafluoroethylene (PTFE), polyethylene (PE), micronized PE,Fischer Tropsch (FT), carnauba, and microcrystalline beeswax andcombinations thereof. The polyethylene wax can be of a low density,medium crystallinity and the form of a dispersion, such as Iovite XP 107or Lawter 697, in an alkyd resin is suitable for use in a sheet-fed ink.Exemplary PTFE waxes include Polyfluo® 535 and Polyfluo® 540. Anexemplary micronized PE wax is MicroMatte® 1011 UVW. The Fisher Tropsch(FT) waxes, generally available in aliphatic hydrocarbon solvents, suchas Texolon of Lawter Chemicals Company, also can be used. Preferredwaxes include PTFE, PE or micronized PE or combinations thereof.Generally, the sheetfed printing ink compositions containing NAD includean amount of wax that is less than about 10 wt %, preferably less thanabout 8 wt % based on the weight of the ink composition because the waxcompound can reduce the printing ink viscosity and gloss.

The sheetfed printing ink can include an anti-set off agent. Theanti-set off agent can include silicas or starches or combinationsthereof. The anti-set off agent generally is dispersed in a vehiclebased on a resin, such as rosin resin or alkyd resin. Generally, thesheetfed printing ink composition containing NAD can contain an anti-setoff agent in an amount that is less than about 10 wt %, preferably lessthan about 5% based on the weight of the ink composition.

The sheetfed printing ink containing NAD can include a water fighter.The water fighter can include one or more of the following: blown oils,including blown linseed oil, blown rapeseed oil, blown soybean oil andblown castor oil, such as oxidized castor oils (CAS No. 68187-84-8);isotridecyl alcohol such as is in Primalene AKC4918 (Akzo Nobel);polyalkylene oxide and hydrophobic polyoxyalkane compounds, such as arepresent in LithoTrol™ ink/water balance additives and polyglycols.Preferred water fighting agents are blown oils, polyglycols andpolyalkylene oxides. Generally, the sheetfed printing ink compositioncontaining NAD can contain a water fighter in an amount that is lessthan about 1.0 wt %, preferably between 0.1 wt % to 0.75 wt % based onthe weight of the ink composition. The amount of water fighter includedin the sheetfed printing ink composition containing NAD can be between0.2 wt % to 0.6 wt %, or between 0.3 wt % to 0.5 wt %, or at or about0.5 wt % based on the weight of the ink composition.

The sheetfed printing ink containing NAD can include an emulsifier. Anyemulsifier used routinely in the art for ink and ink-relatedapplications that is compatible with the components of the sheetfedprinting ink composition can be included. Generally, the emulsifier canbe selected to have an HLB (hydrophilic lipophilic balance) valuebetween at or about 2 to at or about 15. The emulsifier can include anamphoteric surfactant, a zwitterionic surfactant, an anionic surfactant,a nonionic surfactant, and mixtures thereof. The emulsifier can includeperfluoroalkyl surfactants, alkylphenyl surfactants, polysiloxanesurfactants and combinations thereof. The emulsifier can includealkoxylates, ethoxylates, block copolymers of ethylene oxide, copolymersof ethylene oxide, copolymers of propylene oxide, copolymers of butyleneoxide, alkyl phenol ethoxylate, alkyl phenol propoxylate,arylarylalkoxylates, amine alkoxylates, amine ethoxylates; fatty acidalkoxylates, fatty alcohol alkoxylates, alkyl sulfonates, alkyl benzenesulfonates, alkyl naphthalene sulfonates, sulfated fatty alcohols,sulfated fatty alcohols, sulfated fatty amines, sulfated fatty acidamides, acid esters of sodium isethionate, esters of sodiumsulfosuccinate, sulfated fatty acid esters, sulfonated fatty acidesters, petroleum sulfonates, N-acyl sarcosinates, alkyl polyglycosides,alkyl ethoxylated amines, alkyl acetylenic diols, pyrrilodone basedsurfactants, 2-ethyl hexyl sulfate, isodecyl alcohol ethoxylates,ethylene diamine alkoxylates, ethylene oxide/propylene oxide copolymers,diphenyl ether Gemini type surfactants, ethylene oxide/propylene oxidecopolymers, amine ethoxylates, alkyl polyglycosides, and oxo-tridecylalcohol ethoxylates and combinations thereof. The emulsifier can includelecithin, nonyl phenoxy polyethoxylated alcohols, acrylate-modifiedpolydimethyl-siloxanes, polyether-modified polydimethylsiloxanes,polyoxyalkylated ethers, anionic fluorothio alkyls, alkyl arylsulfonates, alkyl amine quaternary salts, polysorbates, alkyl ethers,aryl ethers, poloxamers, fatty alkanolamides, acetylenic glycols,ethoxylated glycols, ethoxylated acetylenic diols, sorbitan esters, andmixtures thereof. Generally, the sheetfed printing ink composition cancontain an emulsifier in an amount that is less than about 5 wt %,preferably less than about 2.5 wt %, based on the weight of the inkcomposition. The emulsifier can be present in the sheetfed printing inkcomposition containing NAD at a weight in the range of from at or about0.25 wt % to at or about 2.5 wt % based on the weight of the inkcomposition. The emulsifier can be present in an amount that is 0.25 wt%, 0.5 wt %, 0.75 wt %, 1 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2 wt %,2.25 wt % or 2.5 wt % based on the weight of the sheetfed printing inkcomposition.

The sheetfed printing ink containing NAD contains a varnish. The varnishcan contain a resin and a solvent. The varnish can contain resin, dryingoils, bodied drying oils, vegetable oils, naphthenic oils, paraffinicoils fatty acids and multifunctional unsaturated polyesters. Any resinsknown in the art can be included in the varnish. Exemplary resinsinclude rosin resin, alkyd resin, epoxy modified alkyd resins andsoya/linseed oil alkyd resins. The varnish also can contain a mineraloil, such as a light mineral oil or a heavy mineral oil or combinationsthereof. The varnish also can contain a vegetable oil, such as a linseedoil, castor oil, cottonseed oil, soya oil or combinations thereof. Anexemplary varnish contains 30 wt % to 40 wt % rosin resin, 30 wt % to 40wt % mineral oil, 15 wt % to 25 wt % linseed oil and 10 wt % to 20 wt %alkyd based on the weight of the varnish. Another exemplary varnish caninclude 40 wt % to 50 wt % rosin resin, 40 wt % to 50 wt % mineral oil,5 wt % to 15 wt % linseed oil and 1 wt % to 5 wt % soya oil based on theweight of the varnish. The varnish can be present in an amount that isbetween at or about 5 wt % to at or about 60 wt %, or 10 wt % to at orabout 50 wt %, such as 5 wt %, 6 wt %, 7 wt %, 8 wt %, 9 wt %, 10 wt %,11 wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %,19 wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %,27 wt %, 28 wt %, 29 wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %,35 wt %, 36 wt %, 37 wt %, 38 wt %, 39 wt %, 40 wt %, 41 wt %, 42 wt %,43 wt %, 44 wt %, 45 wt %, 46 wt %, 47 wt %, 48 wt %, 49 wt % or 50 wt %based on the weight of the sheetfed printing ink composition.

An exemplary conventional sheetfed printing ink composition contains,based on the weight of the ink composition, 1 wt % to 10 wt % resin, 10wt % to 45 wt % varnish, 15 wt % to 45 wt % pigment, 15 wt % to 60 wt %NAD, 1 wt % to 10 wt % waxes, 0.5 wt % to 5 wt % heavy oil, 0.5 wt % to5 wt % emulsifier, 1 wt % to 5 wt % anti-set off agents, 0.25 wt % to2.5 wt % anti-oxidant, 0.1 wt % to 1 wt % water fighter agent and, ifpresent, 0.25 wt % to 2 wt % metal drier.

It has been found that sheetfed printing ink compositions containingNAD, particularly containing 11 wt % to 60 wt %, or 15 wt % to 60 wt %NAD based on the weight of the ink composition, exhibit faster settingand drying, as exhibited by increased rub resistance 1 minute afterprinting without oven drying. As demonstrated in the Examples, sheetfedprinting ink compositions containing NAD set quickly and have improvedshort term rub resistance when compared to a sheetfed printing ink thatdoes not include a drier or anti-oxidant. Increasing the amount of NADin the sheetfed printing ink composition results in increasingimprovements in the set time and rub resistance. Accordingly, providedare methods for improving rub resistance of a sheetfed printing inkcomposition by including in the sheetfed printing ink composition an NADin an amount that provides rub resistance without the need to include ametal drier. As shown in the Examples, including NAD in the sheetfedprinting ink composition without metal drier yields a printed ink thatexhibits a rub resistance value at 15 minutes that is the same as orbetter than rub resistance value achieved in 24 hours.

Also provided are sheetfed printing ink formulations containing NAD andmethods of sheetfed lithographic printing that obviate the need formetal driers and anti-oxidants in the sheetfed printing ink. The methodincludes preparation of a sheetfed printing ink composition thatcontains from 11 wt % to 60 wt % NAD, such as 15 wt % to 55 wt % NAD,preferably between 20 wt % to 35 wt % NAD based on the weight of the inkcomposition, and does not contain a metal drier. As demonstrated in theExamples, sheetfed printing ink compositions that contain from 15 wt %to 60 wt % NAD based on the weight of the ink composition will set anddry properly and exhibit good rub resistance without the need for metaldriers or anti-oxidant. Such sheetfed printing ink compositions yieldprinted inks that have rub resistance values 2 hours and 24 hours afterprinting that are equal or better than ink compositions containing metaldriers.

Also provided are sheetfed lithographic printed substrates printed witha sheetfed printing ink, where the sheetfed printing ink contains from11 wt % to 60 wt % NAD, such as 15 wt % to 55 wt % NAD, preferablybetween 20 wt % to 35 wt % NAD, based on the weight of the inkcomposition, where the sheetfed printing ink composition does notinclude a metal drier.

Also provided are methods of lithographic printing using a sheetfedlithographic printing process, comprising printing a substrate with asheetfed printing ink that contains from 11 wt % to 60 wt % NAD, such as15 wt % to 55 wt % NAD, preferably between 20 wt % to 35% NAD based onthe weight of the ink composition, where the sheetfed printing inkcomposition does not include a metal drier.

2. Heatset Printing Ink Compositions

Another class of lithographic inks that can be formulated to includeNADs are heatset printing inks. Standard heatset printing inks are usedmainly to print magazines and normally set and dry by solventevaporation while the printed substrate goes through a heatingapparatus, such as an oven or IR or UV dryer. A printed substratetemperature between 100° C. and 130° C. normally is required at the endof the heating process in order to dry the printed ink film. Althoughprogress has been made within the last few years to improve the outputsof the heating process, the heatset printing process remains relativelyunfriendly to the environment due to the energy necessary to dry theheatset printing ink film. A heatset printing ink that would allow areduction in energy consumption would make the heatset printing processmore environmental-friendly. A reduction in energy consumption could beachieved by reducing the temperature required to dry the heatsetprinting ink. A significant reduction in energy consumption could beachieved by eliminating the need to heat the heatset printing inkaltogether in order to dry the heatset printing ink. Such a heatsetprinting ink would make the heatset printing process moreenvironmental-friendly as well as more economical for the print shops.

The present invention provides heatset printing ink compositions thatcontain a non-aqueous dispersion (NAD). The inclusion of NAD in heatsetprinting inks provides a heatset printing ink composition that exhibitsexcellent setting and drying and immediate rub resistance without theneed for the printed heatset printing ink to be exposed to thermalenergy, such as in an oven or via IR or UV heaters. Heatset printing inkcompositions containing NAD can be printed using a conventional heatsetlithographic process while reducing the temperature of the externalenergy source, e.g., an oven, or even turning off the oven typicallyused with conventional heatset printing. It is impossible to by-pass oreliminate the oven in a heatset lithographic printing process usingconventional heatset printing inks because doing so would immediatelylead to severe rub off issues in the downstream folding and cuttingunits, yielding printed jobs with very poor appearance.

The amount of NAD that can be included into a heatset printing ink canvary between 5 wt % to 50 wt % based on the weight of the inkcomposition. The NAD can be incorporated into the heatset printing inkcomposition in a range of from at or about 10 wt % to at or about 45 wt%, or at or about 15 wt % to at or about 40 wt %, or at or about 20 wt %to at or about 35 wt %, based on the weight of the ink composition. TheNAD can be present in the heatset printing ink composition in an amountthat is at or about 5 wt %, 6 wt %, 7 wt %, 8 wt %, 9 wt %, 10 wt %, 11wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19wt %, 20 wt %, 21 wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27wt %, 28 wt %, 29 wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35wt %, 36 wt %, 37 wt %, 38 wt %, 39 wt %, 40 wt %, 41 wt %, 42 wt %, 43wt %, 44 wt %, 45 wt %, 46 wt %, 47 wt %, 48 wt %, 49 wt % or 50 wt %based on the weight of the ink composition.

Heatset offset printing inks can include a resin or modified resin, suchas hydrocarbon resin, rosin resin, phenolic modified rosin resin, alkydresin, oxidized alkyd resin or rosin resin, including modified rosinesters and modified alkyd resins and combinations thereof, one or morepigments, and solvents such as mineral solvents or petroleumderivatives, generally high boiling point solvents, and additives suchas waxes and rheology control agents. U.S. Pat. Nos. 6,489,375 and6,451,873 describe resin-based rheological additives for web offsetheatset printing inks.

Exemplary resins that can be included in the heatset printing inksinclude rosins, rosin esters, phenolic modified rosins, maleic modifiedresins, rosin modified fumaric resins, dimerized and polymerized rosins,phenolics, rosin modified phenolics, terpenes, polyamides, cyclizedrubber, acrylics, hydrocarbons and modified hydrocarbons andcombinations thereof. Preferred resins are alkyd resins, phenolicmodified rosin resins and hydrocarbon resins and combinations thereof,particularly phenolic modified rosin resins combined with hydrocarbonresins. In the heatset printing ink compositions containing NAD providedherein, the total resin content of the ink composition can be in a rangeof from at or about 1 wt % to at or about 40 wt %, or in a range of fromat or about 1 wt % to at or about 10 wt %, or in a range of from at orabout 5 wt % to at or about 15 wt %, or in a range of from at or about10 wt % to at or about 30 wt %, based on the weight of the inkcomposition. The heatset printing inks can include a clay base, avarnish, one or a combination of waxes, emulsifier(s) andanti-oxidant(s). Further details regarding the fundamentalcharacteristics of heatset printing inks can be found, e.g., in ThePrinting Ink Manual (5^(th) ed., Leach et al. eds. (2009), pages360-387), the disclosure of which is incorporated herein by reference.

The heatset printing ink compositions usually include a pigment, thenature of which is not critical to the present invention, and which canbe chosen from any of those pigments well known to those skilled in theart. Heatset printing inks generally are prepared in fourcolors—magenta, yellow, black, and cyan. Any of the customary inorganicand organic pigments can be used in the ink compositions of the presentinvention. The pigment can be added to the heatset printing inkcomposition either as a dry powder, flush, presscake or as a dispersion.When using a pigment flush, a portion of the vehicle can first be usedto prepare the flush dispersion. The pigments can be used in an amountdispersable by the formulation. In general, it can be desirable to carryas much pigment in the heatset printing ink as possible. A range oftypical pigment amounts used is approximately 10 wt % to 50 wt % basedon the weight of the heatset printing ink.

Typical heatset printing ink compositions can be characterized, e.g., ascontaining an oil, such as, e.g., a mineral oil, that evaporates underthe influence of application of an external energy, such as heat,thereby allowing the printed ink to dry on the substrate. Inconventional heatset printing inks, the mineral oils generally have aboiling range of 220° C. to 320° C., and typical conventional heatsetprinting inks contain mineral oils having a boiling range between 240°C. and 270° C. The boiling range of the oil for a conventional heatsetprinting ink typically is selected to provide good evaporation whenexposed to a thermal energy source, such as in an oven or when exposedto an IR or UV dryer. Because the heatset printing inks containing NADprovided herein do not require an external energy source, such as anoven or IR or UV drier, to properly set and dry, mineral oils and/orvegetable oils having a lower boiling point range, such as a boilingpoint range between 210° C. and 250° C., or a boiling point rangebetween 160° C. and 220° C., can be used. A heatset printing inkcomposition can contain an oil in an amount of from at or about 15 wt %to at or about 60 wt % based on the weight of the ink composition. Theoils in the heatset printing ink composition can be present in an amountfrom at or about 20 wt % to at or about 50 wt %, or at or about 25 wt %to at or about 45 wt %, or at or about 30 wt % to at or about 40 wt %based on the weight of the heatset ink composition.

The heatset printing ink composition also can include a clay and/ororganoclays. Clays and organoclays are used widely as viscositymodifiers and also can serve as anti-misting agents. Organoclays soldunder the trademark Bentone® can be included in the ink compositionscontaining NAD described herein. The clays often are included as a claybase, which can include a clay in a resin solution vehicle. In someinstances, the amount of clay in a clay base can be as high at 60 wt %based on the weight of the ink composition. In exemplary heatsetprinting ink compositions containing NAD provided herein, a clay ororganoclay, if present, can be present in the heatset printing ink in anamount that is in a range of from at or about 0.25 wt % to at or about 5wt %, or in a range of from at or about 0.5 wt % to at or about 3 wt %based on the weight of the ink composition. The clay/organoclay can bepresent in an amount that is at or about 0.25 wt %, 0.5 wt %, 0.75 wt %,1 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2 wt %, 2.25 wt %, 2.5 wt % or2.75 wt % based on the weight of the ink composition.

The heatset printing inks containing NAD include a varnish. The varnishcan contain a resin and a solvent. Any resin and any solvent that candissolve or solvate the selected resin can be used. Exemplary resinsinclude rosin resin, modified rosin resins, alkyd resin, modified alkydresins, such as epoxy modified alkyd resins and soya/linseed oil alkydresins. The varnish also can contain, as a solvent, a mineral oil, suchas a light mineral oil or a heavy mineral oil, a naphthenic oil, aparaffinic oil, a vegetable oil or combinations thereof. The varnishalso can include a gelling agent. Exemplary gelling agents includechelates, such as an aluminum chelate, and alcoholates, such as aluminumalcoholate. An exemplary aluminum chelate is oxy aluminum octoate. Inthe heatset printing ink compositions containing NAD provided herein,the varnish can be present in an amount that is in a range of from at orabout 5 wt % to at or about 55 wt %, or in a range of from at or about10 wt % to at or about 50 wt %, or in a range of from at or about 15 wt% to at or about 45 wt %, based on the weight of the ink composition. Anexemplary varnish contains, based on the weight of the varnish, 40 wt %to 50 wt % mineral oil, 40 wt % to 60 wt % resin, such as rosin resin ormodified rosin resin, lwt % to 1 Owt % vegetable oil, such as linseedoil, and 0.1 wt % to 1.5 wt % gelling agent, such as oxy aluminumoctoate.

The heatset printing ink containing NAD also can include a wax, whichcan be incorporated into the printing ink composition as a wax paste.The wax paste can include a wax dispersed in a vehicle based on a resin,such as rosin resin or alkyd resin. Any wax known in the art can beincluded in the heatset printing ink composition containing NAD.Exemplary waxes include polytetra-fluoroethylene (PTFE), polyethylene(PE), micronized PE, Fischer Tropsch (FT), carnauba, andmicrocrystalline beeswax and combinations thereof. Preferred waxesinclude PTFE, PE or micronized PE or combinations thereof. Generally,the heatset printing ink composition containing NAD can include wax inan amount that is less than about 10 wt %, preferably less than about 5wt % based on the weight of the ink composition.

The heatset printing ink containing NAD also can include an emulsifier.Any emulsifier used routinely in the art for ink and ink-relatedapplications that is compatible with the components of the heatsetprinting ink composition can be included. The emulsifier can include anamphoteric surfactant, a zwitterionic surfactant, an anionic surfactant,a nonionic surfactant, and mixtures thereof. The emulsifier can includeperfluoroalkyl surfactants, alkylphenyl surfactants, polysiloxanesurfactants and combinations thereof. The emulsifier can includealkoxylates, ethoxylates, block copolymers of ethylene oxide, copolymersof ethylene oxide, copolymers of propylene oxide, copolymers of butyleneoxide, alkyl phenol ethoxylate, alkyl phenol propoxylate,arylarylalkoxylates, amine alkoxylates, amine ethoxylates; fatty acidalkoxylates, fatty alcohol alkoxylates, alkyl sulfonates, alkyl benzenesulfonates, alkyl naphthalene sulfonates, sulfated fatty alcohols,sulfated fatty alcohols, sulfated fatty amines, sulfated fatty acidamides, acid esters of sodium isethionate, esters of sodiumsulfosuccinate, sulfated fatty acid esters, sulfonated fatty acidesters, petroleum sulfonates, N-acyl sarcosinates, alkyl polyglycosides,alkyl ethoxylated amines, alkyl acetylenic diols, pyrrilodone basedsurfactants, 2-ethyl hexyl sulfate, isodecyl alcohol ethoxylates,ethylene diamine alkoxylates, ethylene oxide/propylene oxide copolymers,diphenyl ether Gemini type surfactants, ethylene oxide/propylene oxidecopolymers, amine ethoxylates, alkyl polyglycosides, and oxo-tridecylalcohol ethoxylates, and combinations thereof. The emulsifier caninclude lecithin, nonyl phenoxy polyethoxylated alcohols,acrylate-modified polydimethyl-siloxanes, polyether-modifiedpolydimethylsiloxanes, polyoxyalkylated ethers, anionic fluorothioalkyls, alkyl aryl sulfonates, alkyl amine quaternary salts,polysorbates, alkyl ethers, aryl ethers, poloxamers, fattyalkanolamides, acetylenic glycols, ethoxylated glycols, ethoxylatedacetylenic diols, sorbitan esters, and mixtures thereof. Generally, theheatset printing ink composition can contain an emulsifier in an amountthat is less than about 7.5 wt %, preferably less than about 5 wt % or2.5 wt %, based on the weight of the ink composition. The emulsifier canbe present in the heatset printing ink in a range of from at or about0.25 wt % to at or about 5 wt % based on the weight of the inkcomposition.

The heatset printing ink composition containing NAD can include ananti-oxidant. Anti-oxidant additives are known in the art and arecommercially available. Any conventional anti-oxidant that does notadversely react with other components of the heatset printing ink can beused. Exemplary anti-oxidants include ascorbic acid, astaxanthin,carotene, chroman (3,4-dihydro-2H-1-benzopyran), hexamethylenebis(3,5-di-tert-butyl-4-hydroxyhydro-cinnamate), octadecyl3,5-di-tert-butyl-4-hydroxyhydro-cinnamate, vitamin E and vitamin Eanalogs, mono-tert-butylhydroquinone (MTBHQ) and butylated hydroxytoluene (BHT). Preferred anti-oxidants are MTBHQ and BHT. Generally, theheatset printing ink composition containing NAD can contain an amount ofanti-oxidant that is less than about 5 wt %, preferably less than about2.5 wt % or less than about 1.5 wt % or less than about 1 wt % based onthe weight of the ink composition.

An exemplary heatset printing ink composition can, e.g., containexemplary ranges of components that include, for example, 10 wt % to 50wt % pigment, 10 wt % to 55 wt % rosin resin varnish (which contains 30wt % to 50 wt % rosin resin, 30 wt % to 50 wt % mineral oil, 5 wt % to35 wt % linseed oil, 0 wt % to 5 wt % soya oil and 0 wt % to 20 wt %alkyd based on the weight of the varnish), 1 wt % to 15 wt % mineral oilor mineral solvent, 0.1 wt % to 2 wt % anti-oxidant, 1 wt % to 5 wt %wax paste, 10 wt % to 50 wt % NAD, 0 wt % to 10 wt % clay or organoclay,0 wt % to 5 wt % alkyd resin, and 0 wt % to 5 wt % emulsifier based onthe weight of the ink composition.

Because the heatset printing ink does not need to be absorbed by thesubstrate in order to set and dry, substrate surfaces having smallerpores can be printed using the heatset printing ink compositions. Inaddition, coated substrates can be printed using the heatset printingink compositions. The substrate can include heavily coated paper,typically having a coating weight of more than 10 g/m², and for example,of at least 15 g/m². The substrate also can be a paper having a baseweight range of greater than 40 g/m², such as, for example, having abase weight greater than 50 g/m², such as a base weight in the range of55-120 g/m². The substrate also can be a super calendered paper.

In traditional heatset lithographic printing operations, the printedheatset printing ink on a substrate is dried using a dryer, such as anoven, hot air, a UV drier or an IR dryer. During the setting and dryingprocess, the oil in the heatset printing ink evaporates, the resin inthe heatset printing ink becomes insoluble and precipitates causing theink to set. In some processes, after the substrate is heated in a dryer,the substrate can be cooled by passing the printed substrate through acooling device. Thus, the traditional heatset printing process can beenergy intensive.

As demonstrated in the Examples, the rub resistance of prints made usingheatset printing ink compositions containing NAD is improved, and thegeneral trend it that rub resistance is continuously improved as agreater amount (wt %) of NAD is included in the heatset printing inkcomposition. Heatset printing ink compositions containing NAD yield aprinted ink having a rub resistance at 1 minute without any externalenergy treatment, such as thermal treatment, that is the same or betterthan its rub resistance at 24 hours without external energy treatment.Heatset printing ink compositions containing 5 wt % to 50 wt % NAD ormore based on the weight of the ink composition set quickly and provideoptimum rub resistance 1 minute after printing when the oven is turnedoff in the tested formulations. When the same heatset printing inkscontaining NAD are exposed to an external energy source, such as to athermal energy, such as heating in an oven, the dried heatset printinginks containing NAD generally exhibit a similar rub resistance.Including NAD in a heatset printing ink composition yields a heatsetprinting ink that when printed on a substrate exhibits very fast settingand improved rub resistance when compared to conventional heatsetprinting inks that do not contain NAD. Thus, heatset printing inkcompositions containing NAD exhibit fast setting times and significantlyimproved rub resistance whether or not the sheet is subjected toexposure to an external energy source, such as thermal energy, such asheating in an oven. In exemplary compositions, heatset printing inkcompositions containing NAD exhibit rub resistance after 1 minutewithout going through an oven that is equal to the rub resistance of aconventional ink containing no NAD after the conventional ink has gonethrough an oven. In contrast, conventional heatset printing inkcompositions that do not include NAD have, shortly after printingwithout the input of external energy, very poor rub resistance thatslowly improves with time at the solvent in the ink slowly evaporates.Thus, a heatset printing ink composition containing NAD can be providedthat can eliminate the need for exposing a substrate printed with theheatset printing ink to an external energy, such thermal energy. Alsoprovided are methods for rapidly or immediately upon substrateapplication improving rub resistance of a heatset printing inkcomposition by including in the ink composition an NAD in an amount thatprovides rub resistance without having to be exposed to an energysource, such as an oven, IR drier or UV drier.

Addition of 5 wt % to 60 wt % NAD, or 15 wt % to 55 wt % NAD to aheatset printing ink composition, e.g., at levels of 30 wt % or less inexemplary compositions, allows the ink press operator to reduce theenergy required to set and dry the ink formulation, such as by reducingthe temperature of the oven used to set and dry the printed ink. Such areduction in energy can result in a printed product that is lessexpensive to produce. In addition, including NAD in the heatset printingink compositions produces an ink demonstrating improved setting andimmediate rub resistance, such as, e.g., when measured 1 minute afterprinting.

Provided are methods of heatset printing that reduce the energyconsumption during setting and drying of a heatset printed substrate.The methods include preparation of a heatset printing ink compositionthat contains from 5 wt % to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15wt % to 40 wt % NAD based on the weight of the ink composition, andprinting the ink onto a substrate. Because the ink containing NADrequires little to no exposure to external energy in order to set andproperly dry, the amount of energy necessary for printing with such inkscan be reduced. As demonstrated in the Examples, heatset printing inkcompositions that contains NAD in the range of from 15 wt % to 60 wt %NAD based on the weight of the ink composition set quickly and dryproperly and exhibit good rub resistance without the need for exposureto external energy, such as heating in an over or via IR or UV dryers.

Also provided are methods for reducing the amount of energy required toprovide rub resistance of a heatset printing ink by including in the inkformulation an NAD in an amount that provides rub resistance, such as inthe range of from 5 wt % to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15wt % to 40 wt % NAD, based on the weight of the ink composition, atlower exposures to an energy source, such as an oven, IR drier or UVdrier, than conventionally used.

Also provided are methods for reducing the time necessary for a heatsetprinting ink printed on a substrate to set and dry without heating,where the methods include preparation of a heatset printing inkcomposition that contains from 5 wt % to 60 wt % NAD or 10 wt % to 50 wt% NAD or 15 wt % to 40 wt % NAD or 30 wt % to 60 wt % based on theweight of the ink composition, and printing the ink onto a substrate.Such heatset printing ink compositions yield printed inks that have rubresistance values after 1 minute without heating that are equal to orbetter than heatset printing ink compositions containing no NAD after 24hours without heating.

Also provided are methods for generally improving the rub resistance ofa heatset printing ink printed on a substrate, where the methods includepreparation of a heatset printing ink composition that contains from 5wt % to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15 wt % to 40 wt % NADor 30 wt % to 60 wt % based on the weight of the ink composition, andprinting the ink onto a substrate. Such heatset printing inkcompositions yield printed inks that have rub resistance values,particularly Prüfbau rub mark values, that continue to improve whenincreasing amounts of NAD are added to the heatset printing inkcomposition.

Also provided are heatset printed substrates that include an ink on atleast one surface thereof, where the heatset printing ink contains from5 wt % to 60 wt % NAD, preferably between 15 wt % to 35 wt % NAD or 30wt % to 60 wt % based on the weight of the ink composition and thesubstrate is printed using a heatset lithographic printing process.

Also provided are methods of printing a substrate using a heatsetlithographic printing process, comprising depositing on a substrate aheatset printing ink that contains from 5 wt % to 60 wt % NAD,preferably between 15 wt % to 35 wt % NAD or 30 wt % to 60 wt % NADbased on the weight of the ink composition, where the ink is depositedon the substrate using a heatset lithographic printing process.

The heatset printing ink compositions also can be characterized byexhibiting an increase of at least 10%-50%, or between 10%-100%, such as10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%,80%, 85%, 90%, 95% or 100% in a rub resistance rating when compared to acomparable ink composition that does not contain NAD. For example, asdemonstrated in the Examples, an exemplary heatset printing inkcomposition containing 40 wt % NAD based on the weight of the inkcomposition without heat treatment exhibited an average rub resistancemark value of 4, while a comparative ink containing no NAD without heattreatment had an average ink mark value of 8, which represents a 100%improvement in the average rub resistance mark value for the inkcontaining the NAD. Other exemplary ink compositions containing NADexhibited increases in rub resistance ratings of, e.g., 33%, 50% and66%.

3. Coldset Printing Ink Compositions

Another class of lithographic inks that can be formulated to includeNADs are coldset printing ink compositions. Coldset printing inksprimarily are used to print porous paper, particularly newspaper.Coldset printing ink compositions basically contain a pigment dispersedin a mineral/vegetable oil and binder, and often a resin. Coldsetprinting inks generally dry by penetration of the solvent in the inkcomposition into the fibers of the paper, which allows the resin in theink composition to set and thereby provide rub-fastness to the ink. Rubresistance of coldset ink, however, is very poor and ink easily cantransfer to the fingers of the person who is handling or reading thenewspaper. Other problems experienced with the coldset printing processinclude inter-page set off, where ink from one page marks an adjacentpage.

In addition, conventional coldset printing inks generally are used forprinting on uncoated stock used for newspaper since drying requires openpores through which the solvent in the ink can be absorbed andtransported away from the ink film. The substrate typically is uncoated,although lightly coated paper can be used. For coldset lithographicprinting applications, the paper can be structured in a base weightrange of generally less than 50 g/m², and especially less than 40 g/m².Due to this limitation, other types of paper, such as coated or supercalendared papers, typically cannot be printed using a conventionalcoldset lithographic printing process. In addition, because mostnewspapers are printed at night, some printshops cannot run theirprinting machines during the day. Providing a coldest printing ink thatwould allow printing with a coldset printing ink on other paper typesand qualities could lead to a significant increase in coldsetlithographic press productivity and substrate versatility.

Provided herein are coldset printing inks that contain non-aqueousdispersions containing acrylic core/shell polymers (NAD). Theintroduction of this polymeric dispersion in coldset printing inksprovides a coldset printing ink that demonstrates improved immediate andlong-term rub resistance on different substrates, including papers ofdifferent types and qualities, e.g., uncoated paper, super calenderedpaper and/or low weight coated paper.

As mentioned above, coldset printing inks basically contain a pigmentdispersed in a mineral/vegetable oil and binder, and often a resin.Because of cost restrictions, additives generally are not included inmany coldset printing inks. Any modified coldset printing ink must beeasy to insert into a current printing process, must not add excessivelyto the cost, and must not unduly slow the overall printing process. Someconventional coldset printing inks include binders. Binders generallyinclude ingredients that modify the absorption characteristics of theink into the substrate, such as extenders, clays, e.g., organoclays,smectic clays and Kaolin clays and carbonates. In some instances, thecoldset printing ink can include surfactants, waxes, gelling agents andmineral fillers. A skilled artisan will readily recognize thatadditional additives, such as dispersing agents, wetting agents, waxesand other agents, can be included in the coldset printing inkcompositions. Due to cost constraints, however, many ink compositionscontain few if any additional additives. Further details regarding thefundamental characteristics of coldset printing inks can be found, e.g.,in The Printing Ink Manual (5^(th) ed., Leach et al. eds. (2009), pages353-360), the disclosure of which is incorporated herein by reference.

The coldset printing ink compositions typically include a pigment.Coldset printing inks typically are black inks for printing newspapers,although inks of other colors, such as magenta, yellow and cyan, alsocan be formulated. Any of the customary inorganic and organic pigmentscan be used in the ink compositions of the present invention. In thecase of black ink, carbon black (such as Elftex carbon black from CabotCorp.) can be used. In the coldset printing ink compositions containingNAD provided herein, the pigment can be present in an amount that isfrom at or about 10 wt % to at or about 40 wt % based on the weight ofthe ink composition.

The oil used in the composition can be a hydrocarbon oil or a vegetableoil or a combination thereof. Suitable hydrocarbon oils includeparaffinic oils, such as white mineral oils (CAS No. 8042-47-5), e.g.,Magie N-40 oil; naphthenic oils and distillates, such as hydrotreatedlight naphthenic distillates (CAS No. 64742-53-6), e.g., Nytex 5130, andhydrotreated heavy naphthenic distillates (CAS No. 64742-55-5), e.g.,Nytex 510). The vegetable oils can be drying oils, semidrying oils andnondrying oils. Examples include almond oil, cacao oil, candlenut oil,castor oil, dehydrated castor oil, coconut oil, corn oil, cottonseedoil, grape seed oil, hempseed oil, linseed oil, olive oil, palm kerneloil, peanut oil, rapeseed oil, rice bran oil, safflower oil, sunfloweroil, sesame oil, soybean oil, tall oil, tung oil and walnut oil,including combinations and fatty acid esters, such as fatty acid alkylesters, thereof. Modified vegetable oils, such as epoxy-modified orsilicone-modified or epoxidized oils, such as epoxidized soybean orlinseed oils, also can be used. Coldset printing ink compositionsgenerally include oils having less volatility. For example, in somecompositions, the oil can be selected to have a boiling range between300° C. to 400° C. In the coldset printing ink compositions containingNAD provided herein, the oil can be present in an amount that is from ator about 2 wt % to at or about 30 wt % based on the weight of the inkcomposition.

When present, any resin known in the art can be used. Exemplary resinsinclude, e.g., natural or processed resins such as rosins, rosin esters,maleic modified resins, rosin modified fumaric resins, dimerized andpolymerized rosins, phenolics, rosin modified phenolics, alkyd resins,modified alkyd resins, terpenes, polyamides, cyclized rubber, acrylics,hydrocarbons and modified hydrocarbons. In the coldset printing inkcompositions provided herein containing NAD, the resin, when present,can be in an amount that is from at or about 0.5 wt % to at or about 30wt % based on the weight of the ink composition.

The coldset printing ink composition containing NAD can includeviscosity modifying agents and/or mineral fillers. Many such additivesare known in the art and are commercially available. Organoclays can beused as a viscosity modifying agent as well as a mineral filler.Organoclays generally contain bentonite, hectorite or attapulgite claysor combinations thereof. Organoclays sold under the trademark Benton®can be included in the coldset ink compositions containing NAD describedherein. In the coldset printing ink compositions containing NAD providedherein, a viscosity modifying agent, such as an organoclay, whenpresent, can be in an amount that is from at or about 0.5 wt % to at orabout 5 wt % based on the weight of the ink composition.

The coldset printing ink composition containing NAD can include anextender paste. Extender paste can be used to increase the solid contentof the printing ink and to improve the solid lay of the coldset printingink on the printed substrate. The extender paste can contain extenderpigments, such as kaolin, kaolin derivatives, alumina hydrate, blancfixe (CAS No. 7727-43-7), calcium carbonate (coated or uncoated) or zincwhite. The extender paste also can include resins and solvents. Anexemplary resin is vegetable oil hybrid resin. The solvent can be ahydrocarbon solvent, such as a white mineral oil (CAS No. 8042-47-5) ora hydrotreated light naphthenic distillates (CAS No. 64742-53-6). Anexemplary extender paste includes 60 wt % coated calcium carbonate, 4.5wt % vegetable oil hybrid resin, and 35.5 wt % mineral oil based on theweight of the extender paste. In the coldset printing ink compositionscontaining NAD provided herein, an extender paste, when present, can beincluded in an amount that is from at or about 1 wt % to at or about 25wt % based on the weight of the ink composition.

The coldset printing ink composition containing NAD includes a varnish.The varnishes can contain a resin and a solvent. Any resin and anysolvent that can dissolve or solvate the selected resin can be used.Exemplary resins include rosin resin, modified rosin resin, alkyd resin,and modified alkyd resin, such as epoxy modified alkyd resins andsoya/linseed oil alkyd resins. The varnish also can contain, as asolvent, a mineral oil, such as a light mineral oil or a heavy mineraloil, a naphthenic oil, a paraffinic oil, a vegetable oil, hydrocarbons,such as C₁₂-C₁₄ or C₁₁-C₁₄ or C₁₂-C₁₆ or C₁₄₋₁₈ n-alkanes, isoalkanes,cyclics or aromatics, or combinations of these solvents thereof.Exemplary hydrocarbon solvents include white mineral oil (CAS No.8042-47-5) and Exx-Print solvents (ExxonMobile Chemical, Houston, Tex.),such as Exx-Print T82A and T84D. Exemplary vegetable oils includesoybean, cottonseed and linseed oils.

In the coldset printing ink compositions containing NAD provided herein,the varnish can be present in a range of from at or about 5 wt % to ator about 55 wt %, or in a range of from at or about 10 wt % to at orabout 50 wt %, or in a range of from at or about 15 wt % to at or about45 wt % based on the weight of the ink composition. An exemplary wettingvarnish can include 15 wt % to 30 wt % vegetable oil, such as soybeanoil, 25 wt % to 40 wt % mineral oil, 30 wt % to 60 wt % resin, such asrosin resin or modified rosin resin, and 0.001 wt % to 0.5 wt %anti-oxidant, such as BHT, based on the weight of the wetting varnish.An exemplary letdown varnish can include 10 wt % to 30 wt % vegetableoil, such as soybean oil, 30 wt % to 60 wt % hydrocarbon solvent, suchas mineral oil or Exx-Print T82A, 30 wt % to 60 wt % resin, such asrosin resin or modified rosin resin, and 0.001 wt % to 0.5 wt %anti-oxidant, such as BHT, based on the weight of the letdown varnish.

The coldset printing ink compositions containing NAD can contain ananti-oxidant. Any conventional anti-oxidant compatible with thecomponents in the coldset printing ink composition can be used.Exemplary anti-oxidants include ascorbic acid, chroman(3,4-dihydro-2H-1-benzopyran), hexamethylenebis(3,5-di-tert-butyl-4-hydroxyhydro-cinnamate), octadecyl3,5-di-tert-butyl-4-hydroxyhydrocinnamate, vitamin E and vitamin Eanalogs, mono-tert-butylhydroquinone (MTBHQ) and butylated hydroxytoluene (BHT). Preferred anti-oxidants are MTBHQ and BHT. Generally, thecoldset printing ink composition containing NAD can contain ananti-oxidant in an amount that is less than about 5 wt %, preferablyless than about 2.5 wt % or less than about 1.5 wt % based on the weightof the ink composition.

The amount of NAD introduced into a coldset printing ink composition canvary between at or about 5 wt % to at or about 60 wt %. A coldsetprinting ink composition can contain NAD in an amount between 5 wt % to25 wt % or 10 wt % to 50 wt % or 15 wt % to 40 wt % or 20 wt % to 35 wt% by weight of the ink composition. In the coldset printing inkcompositions provided herein, the NAD can be present in an amount thatis 5 wt %, 6 wt %, 7 wt %, 8 wt %, 9 wt %, 10 wt %, 11 wt %, 12 wt %, 13wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19 wt %, 20 wt %, 21wt %, 22 wt %, 23 wt %, 24 wt %, 25 wt %, 26 wt %, 27 wt %, 28 wt %, 29wt %, 30 wt %, 31 wt %, 32 wt %, 33 wt %, 34 wt %, 35 wt %, 36 wt %, 37wt %, 38 wt %, 39 wt %, 40 wt %, 41 wt %, 42 wt %, 43 wt %, 44 wt %, 45wt %, 46 wt %, 47 wt %, 48 wt %, 49 wt %, 50 wt %, 51 wt %, 52 wt %, 53wt %, 54 wt %, 55 wt %, 56 wt %, 57 wt %, 58 wt %, 59 wt % or 60 wt %based on the weight of the ink composition.

Addition of NAD to a coldset printing ink, particularly when added in anamount of 5 wt % or greater, such as between 10% to 60% by weight of theink composition, improves the set and rub resistance of the printedproduct. Exemplary coldset printing ink formulations containing aslittle as 10 wt % NAD based on the weight of the ink composition, whenprinted on uncoated paper, exhibited a significant decrease of the DeltaE CMC values in rub tests, which can be directly correlated to a betterrub resistance. A Delta E CMC value of 4 generally is accepted asindicative of an ink that exhibits good rub resistance.

Including NAD in coldset printing ink compositions can improve thekinetics at which acceptable rub resistance is achieved on a papersubstrate. The improvements in rub resistance can be observed in samplesprinted with inks containing NAD shortly after printing. For example, 15minutes after printing on uncoated paper, exemplary samples printed withcoldset printing ink compositions containing 10 wt % NAD based on theweight of the ink composition exhibited rub resistance values half thatof control inks containing no NAD, demonstrating significant improvementin rub resistance of coldset inks when NAD is included. Increasing theamount of NAD in the coldset printing ink composition resulted inconcurrent improvements in the short term rub resistance values. Thus,coldset printing ink compositions containing NAD in an amount that its 5wt % to 60 wt % based on the weight of the ink composition, andparticularly exemplary in compositions containing 10 wt % to 50 wt % NADbased on the weight of the ink composition, exhibit improvements in inksetting and drying properties, as exhibited by improved rub resistancevalues obtained by standard testing methods. Coldset printing inkcompositions containing NAD also exhibit rub resistance values at 15minutes that are similar to the rub resistance values obtained at 24hours.

Adding NAD to coldset printing ink compositions also allows the coldsetprinting ink to be used on diverse substrates other than uncoatednewsprint. Coldset printing ink compositions containing NAD can beprinted on super calendered and coated paper, paper substrates thattypically cannot be printed with conventional coldset printing inks thatdo not contain NAD. Exemplary coldset printing inks containing 10 wt %NAD based on the weight of the ink composition exhibited improvement inrub resistance when compared to conventional coldset printing inkwithout NAD on super calendered paper. As the amount of NAD in thecoldset printing ink composition is increased, the rub resistance of theresulting coldset printing ink composition increases. For example, anexemplary coldset printing ink composition containing 25 wt % NAD basedon the weight of the ink composition exhibited a rub resistance betterthan an exemplary coldset printing ink compositions containing 10 wt %NAD based on the weight of the ink composition, and exhibited asignificant improvement in rub resistance compared to conventionalcoldset printing ink compositions that do not contain NAD. Coldsetprinting ink compositions containing NAD that were printed on supercalendared paper produced a printed substrate that had rub resistancetest values, measured by Delta E CMC, that were below the critical valueof 4. Hence, coldset printing ink compositions containing NAD,particularly compositions containing 5 wt % to 60 wt % NAD based on theweight of the ink composition, can be used to print on super calenderedpaper using a coldset lithographic process.

Similar results were obtained for coldset printing inks containing NADwhen printed on low weight coated paper. Control comparative coldsetprinting ink samples without NAD exhibited a very poor rub resistance 15minutes after printing when printed on low weight coated paper. Coldsetprinting ink compositions containing between 5 wt % to 60 wt % NAD basedon the weight of the ink composition, exhibited improvement in rubresistance when printed on low weight coated paper in comparison tocomparative coldset printing ink without NAD. Increasing the amount ofNAD in the ink composition increased the improvement observed in rubresistance. Exemplary compositions containing greater than 5 wt % NADbased on the weight of the ink composition exhibit enhanced rubresistance on low weight coated paper. Hence, coldset printing inkcompositions containing NAD, such as between 5 wt % to 60 wt % NAD basedon the weight of the ink composition, exhibit enhanced rub resistance onlow weight coated paper and thus can be used to print on low weightcoated paper using a coldset lithographic process.

Provided are methods of improving rub resistance of a substrate printedusing a coldset lithographic process. The methods include preparation ofa coldset printing ink composition that contains from 5 wt % to 60 wt %NAD or 10 wt % to 50 wt % NAD or 15 wt % to 40 wt % NAD or 25 wt % to 50wt % NAD based on the weight of the ink composition, and printing theink onto a substrate using a coldset lithographic process. Asdemonstrated in the Examples, coldset printing ink compositions thatcontain NAD in the range of from 5 wt % to 60 wt % NAD based on theweight of the ink composition, set faster and exhibit improved rubresistance when compared to coldset ink compositions without NAD. Insome methods, a rub resistance value less than 4 can be achieved within15 minutes after printing using a coldset printing ink compositioncontaining NAD.

Also provided are methods for printing on super calendered paper using acoldset lithographic printing process by using a coldset printing inkformulation that includes an NAD in an amount that provides rubresistance on super calendered paper, such as in the range of from 5 wt% to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15 wt % to 40 wt % NADbased on the weight of the ink composition.

Also provided are methods for printing on light weight coated paperusing a coldset lithographic printing process by using a coldsetprinting ink formulation that includes an NAD in an amount that providesrub resistance on light weight coated paper, such as in the range offrom 5 wt % to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15 wt % to 40 wt% NAD based on the weight of the ink composition.

Also provided are methods for reducing the time necessary for a coldsetprinting ink printed on a substrate to set and dry, where the methodsinclude preparation of a coldset printing ink composition that containsfrom 5 wt % to 60 wt % NAD or 10 wt % to 50 wt % NAD or 15 wt % to 40 wt% NAD or 30 wt % to 60 wt % NAD based on the weight of the inkcomposition, and printing the coldset printing ink onto a substrate.Such coldset printing ink compositions containing NAD yield printed inksthat have rub resistance values after 15 minutes that are equal orbetter than ink compositions containing no NAD after 24 hours.

Also provided are substrates printed using a coldset lithographicprocess that include a coldset printing ink film on at least one surfacethereof, where the coldset printing ink that formed the film containsfrom 5 wt % to 60 wt % NAD, preferably between 10 wt % to 40 wt % or 15wt % to 35 wt % NAD or 30 wt % to 60 wt % NAD based on the weight of theink composition.

Also provided are methods of printing a substrate using a coldsetlithographic process, comprising depositing on a substrate a coldsetprinting ink composition that contains from 5 wt % to 60 wt % NAD,preferably between 10 wt % to 40 wt % or 15 wt % to 35 wt % NAD or 30 wt% to 60 wt % NAD based on the weight of the ink composition.

EXAMPLES

The following examples illustrate specific aspects of the presentinvention and are not intended to limit the scope thereof in any respectand should not be so construed.

Example 1

An exemplary non-aqueous dispersion of an acrylic core/shell polymer(NAD) was prepared. The acrylic shell polymer was synthesized containingthe ingredients in Table 1.

TABLE 1 Acrylic shell polymer ingredients. Material wt % A Magie N-40ink oil 34.05 MP B Isobutyl methacrylate 39.58 C Dodecyl methacrylate13.56 D Acrylic acid 1.08 CP E Magie N-40 ink oil 10.837 F t-butylperoctoate 0.43 G t-butyl peroxybenzoate 0.11 H Glycidyl methacrylate0.33 I Triphenylphosphine 0.02 J p-Methoxyphenol 20.003 TOTAL (wt %)100.00

The following protocol was used to synthesize the shell polymer.

Ingredient A was charged to a reactor and heated to 120° C. and held innitrogen gas. Ingredients B, C and D were pre-mixed to form a monomerpre-mixture (MP). Ingredients E, F and G were pre-mixed to form acatalyst pre-mixture (CP). Thereafter, pre-mixtures MP and CP wereconcurrently added to the reactor from separate feeds over 4 hours andheld at 120° C. for 4 hours. Then, the nitrogen gas was changed to airand ingredients H, I and J were charged to the reactor and thetemperature was held at 120° C. for 4 hours. The air was then vacuumedfor 30 minutes and the temperature cooled to 100° C. followed bydischarging the resulting product (shell polymer).

The formation of the acrylic core polymer and NAD was carried out usingthe materials described in Table 2.

TABLE 2 Acrylic Core polymer and NAD ingredients. Material wt % A Magie#N-40 ink oil 32.64 B Shell polymer (Table 1) 31.47 MP CMethylmethacrylate 13.30 D N-butyl methacrylate 5.36 E N-butyl acrylate6.57 CP1 F Magie #N-40 ink oil 5.24 G t-butyl peroctoate 0.26 H t-butylperoctoate 0.14 I Methylmethacrylate 2.56 CP3 J t-butyl peroctoate 0.13K Magie #N-40 ink oil 2.33 100.00

The components for synthesis of the acrylic core polymer include themonomer pre-mixture (MP), the catalyst pre-mixture 1 (CP1), catalystpre-mixture 3 (CP3), additional monomer (Component H) and additionalcatalyst (Component I). The acrylic core polymer is formed in thepresence of the acrylic shell polymer (Component B, from Table 1) in thecontinuous phase containing the essentially non-aqueous organic solvent(Component A, Magie #N-40 ink oil). The acrylic core polymer isinsoluble in the continuous phase of the essentially non-aqueous solventbut is soluble in the acrylic shell polymer and the acrylic shellpolymer is soluble in the continuous phase of the essentiallynon-aqueous solvent and forms particles of acrylic core/shell polymer inthe continuous phase of the essentially non-aqueous solvent. The NADcontains the dispersion of the acrylic core/shell polymer particles inthe continuous phase of the essentially non-aqueous solvent and residualrheology adjusting component.

The formation of the acrylic core polymer and the final NAD were carriedout according to the following protocol. Ingredients A and B werecharged to a reactor and heated to 85° C. and held in nitrogen gas.Ingredients C and D and E were pre-mixed to form a monomer pre-mixture(MP). Ingredients F and G were pre-mixed to form a catalyst pre-mixture1 (CP1). Ingredients J and K were pre-mixed to form a catalystpre-mixture 3 (CP3). Thereafter, pre-mixtures MP and CP1 wereconcurrently added from separate feeds to the reactor over 4 hours andheld at 85° C. for 3 hours. Then, ingredient I was charged followed bypre-mixture CP3 drip-wise and the mixture was held for 3 hours. Thepresence of residual monomers was checked with gas chromatography andthe resultant product (NAD) was brought to room temperature anddischarged.

In this Example, the continuous phase of essentially non-aqueous solventused was a common hydrocarbon solvent, Magie N-40 oil. The shell polymerwas made up of a copolymer of isobutyl methacrylate and dodecylmethacrylate in a ratio of approximately 3:1. The long hydrocarbonchains on these monomers make the resulting polymer readily soluble inthe mineral oil. Approximately 1 wt % acrylic acid based on the weightof the reaction mixture was added to aid in efficient polymer formation.A small amount of glycidyl methacrylate was added because the epoxygroups in this monomer increase the attraction between the acrylic shelland acrylic core polymers.

Example 2

An exemplary non-aqueous dispersion of an acrylic core/shell polymer(NAD) was prepared. The shell polymer was synthesized containing theingredients in Table 3.

TABLE 3 Shell polymer ingredients. Material wt % A Nytex 5130 34.03 MP BIsobutyl methacrylate 39.25 C Dodecyl methacrylate 13.50 D Acrylic acid1.07 CP E Nytex 5130 9.79 F t-butyl peroctoate (50% conc.) 0.83 Gt-butyl peroxybenzoate 0.11 H t-butyl peroctoate (50% conc.) 0.42 WT IWater 0.75 J KOH [85%] 0.09 K Isopropyl alcohol 0.06 L Diethylamine 0.1TOTAL (wt %) 100.00

A shell polymer was synthesized according to the following protocol.Ingredient A was charged to a reactor and heated to 120° C. and held innitrogen gas. Ingredients B, C and D were pre-mixed to form a monomerpre-mixture (MP). Ingredients E, F and G were pre-mixed to form acatalyst pre-mixture (CP). Thereafter, pre-mixtures MP and CP wereconcurrently added from separate feeds to the reactor over 4 hours andheld at 120° C. for 4 hours. Then, the nitrogen gas was changed to airand the reaction was held for an hour at 120° C. Ingredient H then wasadded to the reaction vessel and the temperature was held at 120° C. foran additional 2 hours. Ingredients I, J, K and L were premixed in aseparate addition vessel and were then slowly added to the reactionmixture under reflux conditions. Foaming that occurred was controlled byadjusting the addition rate. After addition of the ingredients to thevessel was complete, the reaction vessel was held for an hour at 120° C.and then cooled down to 90° C. to allow discharging the resultingproduct (shell polymer).

The formation of the acrylic core polymer and final NAD were carried outusing the materials described in Table 4.

TABLE 4 Acrylic core polymer and NAD ingredients. Material wt % A Nytex5130 32.00 B Shell polymer (Table 3) 32.04 MP C Methylmethacrylate 15.73D N-butyl methacrylate 5.32 E N-butyl acrylate 6.23 CP1 F Nytex 51306.50 G t-butyl peroctoate (50% conc.) 0.51 H t-butyl peroxybenzoate 0.25CP2 I t-butyl peroctoate (50% conc.) 0.28 J t-butyl peroxybenzoate 0.14WT K Water 0.75 L KOH [85%] 0.09 M Isopropyl alcohol 0.06 N Diethylamine0.1 TOTAL (wt %) 100.00

The components for synthesis of the acrylic core polymer include themonomer pre-mixture (MP), the catalyst pre-mixture 1 (CP1) and catalystpre-mixture 2 (CP2). The acrylic core polymer is formed in the presenceof the acrylic shell polymer (Component B, from Table 3) in thecontinuous phase containing the essentially non-aqueous organic solvent(Component A, Nytex 5130). The acrylic core polymer is insoluble in thecontinuous phase of the essentially non-aqueous solvent but is solublein the acrylic shell polymer and the acrylic shell polymer is soluble inthe continuous phase of the essentially non-aqueous solvent and formsparticles of acrylic core/shell polymer in the continuous phase of theessentially non-aqueous solvent. The rheology adjusting componentincludes water, KOH, isopropyl alcohol and diethyl amine (Components Kthrough N), which is added to modify the rheology of the dispersion,e.g., to increase the apparent viscosity. The NAD contains thedispersion of the acrylic core/shell polymer particles in the continuousphase of the essentially non-aqueous solvent and residual rheologyadjusting component.

The formation of the acrylic core polymer and NAD was carried out usingthe following protocol.

Ingredients A and B were charged to a reactor and heated to 120° C. andheld in nitrogen gas. Ingredients C and D and E were pre-mixed to form amonomer pre-mixture (MP). Ingredients F, G and H were pre-mixed to forma catalyst pre-mixture 1 (CP1). Ingredients I and J were pre-mixed toform a catalyst pre-mixture 2 (CP2). Thereafter, pre-mixtures MP and CP1were concurrently added from separate feeds to the reactor over 3 hoursand held at 120° C. for 3 hours. Then, the nitrogen gas was changed toair and the reaction was held for an hour at 120° C. Then, thepre-mixture CP2 was charged drip-wise and the mixture was held for 3hours. Finally the ingredients K, L, M, and N were premixed and addedslowly to the reaction vessel under reflux conditions. The foaming thatoccurred was controlled by adjusting the addition rate. The reactionvessel was held for an hour at 120° C. and then cooled down to 90° C. toallow discharging the resulting product (NAD).

The continuous phase of essentially non-aqueous solvent used in thisExample is the common hydrocarbon solvent Nytex 5130. The shell polymeris made up of a copolymer of isobutyl methacrylate and dodecylmethacrylate in a ratio of approximately 3:1. The long hydrocarbonchains on these monomers make the resulting polymer readily soluble inthe mineral oil. Approximately 1% of acrylic acid based on the weight ofthe reaction mixture was added to aid in efficient polymer formation.The viscosity of the composition was modified by adding a mixture ofwater, isopropyl alcohol, KOH and diethylamine (shown in Table 4 asitems K through N).

Example 3

Typical commercially available sheetfed printing inks require drier andanti-oxidant in order to properly polymerize to dry the ink. A printtrial was performed to demonstrate that commercially available sheetfedprinting inks without NAD will not polymerize unless they contain drierand anti-oxidant. A commercial sheetfed printing inks, Sunlit Exact (SunChemical Corporation, Parsippany, N.J., USA) containing anti-oxidant anda combination cobalt/manganese drier in an amount that is from 1 wt % to4 wt % based on the weight of the ink composition was used and comparedto the same commercial sheetfed printing ink, Sunlit Exact, with thedrier and anti-oxidant removed.

The sheetfed printing inks were printed with an ink film weight of about1.5 g/m² using a Prüfbau printing machine. Rub resistance of theseprints was assessed with a Prüfbau Quartant abrasion testing instrument(100 strikes, P=0.05 bar). Rub test results were assessed visually andassigned a number from 0 to 5 based on the amount of ink that rubbed offduring the test. A rating of 0 indicates no visual rub off detected,while a rating of 5 indicates severe rub off. Depending on end useapplications and customer requirements, a rub rating of 2 or lower isconsidered a passing result. There may be applications, however, where arub rating of higher than 2 would be acceptable. Delta E CMC values canbe used for more quantitative values.

The rub resistance tests of the sheetfed printing ink Sunlit Exact withand without drier and anti-oxidant were performed after 30 minutes, 2hours and 24 hours of printing. The results are provided in Table 5.

TABLE 5 Rub Resistance comparison between a standard sheetfed offset inkwith drier and anti-oxidant vs. a standard ink without drier oranti-oxidant. Average Rub Resistane 30 min 2 hr 24 hr Sunlit Exact (SunChemical) 4.08 2.79 1.92 Sunlit Exact (Sun Chemical) w/o 4.38 3.04 3.25drier/anti-oxidant Rub resistance rated from 0 = no rub off; to 5 =severe rub off

From the data, it can be seen that the Sunlit Exact ink without drierand anti-oxidant has not sufficiently polymerized after 24 hours and asa consequence, exhibits poor rub resistance, while the standard SunlitExact ink containing drier and anti-oxidant exhibits progressivepolymerization at 2 hours and 24 hours and as a result exhibitsimproving rub resistance. Even after 24 hours to dry, however, theconventional sheetfed printing ink without drier and anti-oxidant had arub resistance value greater than 2.

Examples 4-15

Examples 4-15 describe the formulation and preparation of severalsheetfed printing ink compositions. The formulations for sheetfedprinting inks of Examples 4 to 8 are shown in Table 6. The inkcompositions were prepared by mixing together ingredients A, B, C, D andE for 2 minutes at 3000 rpm using a Speedmixer™ DAC 150 FVZ fromHauschild. The mill base (MB) obtained then was passed over a threeroller mill until obtaining a grain size measured on a NPIR1 grind gaugebelow 20 μm (preferably below 10 μm). Ingredients F, G, H, J, K, L and M(taken together, if present, the letdown ingredients) and the NAD (itemI) were added to the mill base. Each of the inks then was homogenized byagain mixing all the ingredients together for 2 minutes at 3000 rpm withthe Speedmixer™.

The sheetfed printing ink of Example 4 is a comparative ink—it containsno NAD but does contain drier and anti-oxidant. Thus, the comparativeink of Example 4 is similar to commercial sheetfed printing inks, whichusually contain a drier and an anti-oxidant. The sheetfed printing inkof Example 5 also is a comparative ink—it contains no NAD, and itcontains no drier and no anti-oxidant. Thus, the comparative ink ofExample 5 differs from commercial sheetfed printing inks in that itcontains no drier and no anti-oxidant. The amount of cyan pigment, alkydresin, heavy oil (Printosol 30/40 AP85 from Halternann Products,Channelview, Tex.), wax paste (containing 55 wt % microcrystalline PEwax, 5 wt % PTFE wax, 38 wt % mineral oil and 2 wt % wetting additivebased on the weight of the wax paste composition), anti-set off pasteand water fighter (blown linseed oil) was maintained constant in thesesheetfed printing inks. The sheetfed printing ink composition of Example6 contained 10 wt % NAD, 1.1 wt % anti-oxidant and 1.1 wt % drier basedon the weight of the ink composition. The sheetfed printing inkcomposition of Example 7 contained about 30 wt % NAD, 1.1 wt %anti-oxidant and 1.1 wt % drier based on the weight of the inkcomposition. The sheetfed printing ink composition of Example 8contained about 30 wt % NAD based on the weight of the ink composition,no anti-oxidant and no drier. To account for the addition of NAD and/orremoval of anti-oxidant and drier, the amount of mineral varnish 1 andmineral varnish 2 was varied in the sheetfed printing ink compositionsof Example 4 to 8.

For the sheetfed printing ink compositions of Example 4 to 8, viscositywas measured using an AR 1000 rotational viscometer (TA Instruments, NewCastle, Del., USA). All the samples were adjusted to have anapproximately similar high shear viscosity (±10 cP when measured at 50s⁻¹ at 23° C. Pa·s) so that differences observed on the examples cannotbe attributed to differences in high shear viscosity.

Tack was evaluated on a Tack-o-scope device (Testprint, Inc., CherryHill, N.J.). As shown in Table 5, inks of Examples 1 to 3 all exhibitedsimilar tack at 200 rpm.

TABLE 6 Exemplary sheetfed printing ink compositions. Example 4 Example5 Item Component (comparative) (comparative) Example 6 Example 7 Example8 A Cyan pigment 18.00 18.00 18.00 18.00 18.00 B ^(a)Mineral varnish 125.40 26.60 19.40 C ^(b)Mineral varnish 2 33.00 33.00 33.00 33.00 33.00D Alkyd resin 5.00 5.00 5.00 5.00 5.00 E ^(c)Heavy oil 2.50 2.50 2.502.50 2.50 MB Mill Base (total of 83.90 85.10 77.90 58.50 58.50 abovecomponents) F Mineral varnish 2 4.00 5.00 2.20 G Wax paste 5.40 5.405.40 5.40 5.40 H Anti set off paste 2.50 2.50 2.50 2.50 2.50 I NAD (fromTable 2) — 10.00 29.40 29.40 J Anti-oxidant 1.10 — 1.10 1.10 K Waterfighter 0.50 0.50 0.50 0.50 0.50 L Drier 1.10 — 1.10 1.10 M Emulsifier1.50 1.50 1.50 1.50 1.50 additive Total (wt %) 100.00 100.00 100.00100.00 100.00 Viscosity High shear 52 53 49 41 53 (50 s⁻¹, 23° C. Pa ·s) Low shear 70 67 86 170 208 (2 s⁻¹, 23° C. Pa · s) Tack (200 rpm) 9090 167 156 160 ^(a)Mineral varnish 1 consists of 30-40 wt % rosin resin,30-40 wt % mineral oil. 15-25 wt % linseed oil and 10-20 wt % alkydbased on the weight of the varnish. ^(b)Mineral varnish 2 consists of40-50 wt % rosin resin, 40-50 wt % mineral oil, 5-15 wt % linseed oiland 1-5% soya oil based on the weight of the varnish. ^(c)Heavy Oil:Printosol 30/40 AP85 (Haltermann).

The sheetfed printing ink compositions of Examples 4 to 8, shown inTable 6, were printed with an ink film weight of about 1.5 g/m² using aPrüfbau printing machine. Rub resistance of these prints was assessedwith a Prüfbau Quartant abrasion testing instrument (100 strikes, P=0.05bar). Table 7 provides rub test results for the inks described in Table5. Rub test results were assessed visually and assigned a number from 0to 5 based on the amount of ink that rubbed off during the test. Arating of 0 indicates no visual rub off detected, while a rating of 5indicates severe rub off. Delta E CMC values also can be used for morequantitative values.

TABLE 7 Influence on rub resistance of the addition of NAD to sheetfedprinting ink compositions containing drier and anti-oxidant. Example 4(comparative) Example 6 Example 7 wt % NAD (from Table 2) 0 10.00 29.40Rub resistance 2 hr 4 3 1.5 Rub resistance 24 hr 0.5 1 1.5 Rubresistance rated from 0 = no rub off; to 5 = severe rub off

The sheetfed printing ink composition of Example 6 is a sheetfedprinting ink composition similar to those described in the internationalpatent publication WO09155201A containing 10 wt % NAD based on theweight of the ink along with metal drier and anti-oxidant. The sheetfedprinting ink composition of Example 7 contains a higher amount of NADbut still contains drier and anti-oxidant. The increased amount of NADin the sheetfed printing ink composition of Example 7 leads to animprovement of the rub resistance in comparison to the rub resistance ofthe sheetfed printing ink composition of Example 6.

The sheetfed printing ink composition of Example 8 differs from thesheetfed printing ink composition of Example 7 in that it does notcontain drier or anti-oxidant. Table 8 provides rub test results for thesheetfed printing ink compositions of the comparative ink formulation ofExample 5 and inks of Examples 7 and 8, which contain NAD. As can beseen in Table 8, the rub resistance of the sheetfed printing inkcomposition ink composition of Example 8 (no drier or anti-oxidant)after 2 hours and after 24 hours is equal to or slightly better than thesheetfed printing ink composition of Example 7, which contains drier.This trial demonstrates that sheetfed printing ink compositionscontaining 15 wt % to 60 wt % NAD, preferably 25 wt % to 35 wt % NADbased on the weight of the ink composition, will set and dry properlyand exhibit good rub resistance without the need for driers andanti-oxidant.

TABLE 8 Influence on rub resistance of the addition of NAD to sheetfedprinting ink compositions that do not contain drier nor anti-oxidant.Example 5 (Comparative) Example 7 Example 8 wt % NAD (from Table 2) 029.40 29.40 wt % Drier 0 1.1 0 wt % Anti-oxidant 0 1.1 0 Rub resistance2 hr 4 1.5 1 Rub resistance 24 hr 1 1.5 1 Rub resistance rated from 0 =no rub off; to 5 = severe rub off

To confirm these results, two different sets of sheetfed printing inkcompositions were prepared using the protocol set forth above. The twosets of sheetfed printing ink compositions differ in that the sheetfedprinting ink compositions of Examples 9 to 12 contain drier/anti-oxidantand about 10 wt % NAD, based on the weight of the ink composition, whilethe sheetfed printing ink compositions of Examples 13 to 16 containabout 25 wt % to 30 wt % NAD based on the weight of the ink compositionbut contain no drier and no anti-oxidant. The formulations for sheetfedprinting ink compositions of Examples 9 to 12 are provided Tables 9 andthe formulations for sheetfed printing ink compositions of Examples 13to 16 are provided in Table 10.

TABLE 9 Four color process inks containing 10 wt % NAD, drier andanti-oxidant. Example Example Example 9 Example 10 11 12 Black pigment22.00 Cyan pigment 18.00 Magenta pigment 18.50 Yellow pigment 12.50 Clay2.00 ^(a)Mineral varnish 1 14.10 19.40 26.00 13.50 ^(b)Mineral varnish 226.00 33.00 26.00 29.60 Alkyd Resin 8.00 5.00 Heavy oil 3.00 2.50Mineral oil 3.00 Mill Base 73.10 77.90 73.50 57.60 (total of abovecomponents) Mineral varnish 1 18.50 Wax paste 5.50 5.40 5.90 6.00 Antiset off paste 2.50 2.50 2.50 3.00 NAD (from Table 2) 10.00 10.00 10.0010.00 Blue Toning 5.00 Drier 1.40 1.10 0.80 1.00 Anti-oxidant 0.70 1.201.20 1.00 Emulsifier 1.50 1.50 1.50 1.00 Mineral oil 3.00 3.00 6.00 3.00Total (% recipe) 102.70 102.60 101.40 101.10 High shear viscosity 33 4455 40 (50 s⁻¹, 23° C. Pa · s) Low shear viscosity 62 77 110 60 (2 s⁻¹,23° C. Pa · s) Tack (200 rpm) 141 149 119 165 ^(a)Mineral varnish 1contains 30-40 wt % rosin resin; 30-40 wt % mineral oil; 15-25 wt %linseed oil; and 10-20 wt % alkyd based on the weight of the varnish.^(b) Mineral varnish 2 contains 40-50 wt % rosin resin; 40-50 wt %mineral oil; 5-15 wt % linseed oil; and 1-5 wt % soya oil based on theweight of the varnish.

TABLE 10 Four color process inks containing 25 wt %-30 wt % NAD withoutdrier or anti-oxidant. Example Example Example Example 13 14 15 16 Blackpigment 22.00 Cyan pigment 18.00 Magenta pigment 18.50 Yellow pigment12.50 Clay 2.00 ^(a)Mineral varnish 1 13.00 ^(b)Mineral varnish 2 26.0033.00 32.00 29.60 Alkyd 10.00 7.00 7.00 Heavy oil 3.00 2.50 Mineral oil2.00 Mill Base (total of 61.00 60.50 59.50 57.10 above components) 1.001.00 1.00 1.00 Wax paste 5.50 5.40 5.90 6.00 Anti set off paste 2.502.50 2.50 3.00 NAD (from Table 2) 25.00 30.00 30.00 30.00 Blue Toning5.00 Emulsifier 1.50 1.50 1.50 1.00 Mineral oil 2.00 Water fighter 0.500.50 Total (% recipe) 101.00 100.40 99.40 99.10 High shear viscosity 2838 49 42 (50 s-1, 23° C. Pa · s) Low shear viscosity 68 98 139 234 (2s-1, 23° C. Pa · s) Tack (200 rpm) 158 164 174 174 ^(a)Mineral varnish 1contains 30-40 wt % rosin resin; 30-40 wt % mineral oil; 15-25 wt %linseed oil; and 10-20 wt % alkyd based on the weight of the varnish.^(b)Mineral varnish 2 contains 40-50 wt % rosin resin; 40-50 wt %mineral oil; 5-15 wt % linseed oil; and 1-5 wt % soya oil based on theweight of the varnish.

Sheetfed Lithographic Printing Press Trials

Prints using a sheetfed lithographic printing process were made usingthe sheetfed printing ink compositions of Examples 9 to 12 and Examples13 to 16. In the sheetfed lithographic printing press trials, thesheetfed printing ink compositions of Examples 9 to 12 of Table 9 andExamples 13 to 16 of Table 10 were printed using a sheetfed lithographicprinting process on a Heidelberg MO press with the following opticaldensities (Y=1.3; M=1.45; C=1.5; and K=1.9). Prints were prepared on twopaper substrates: Magnostar 115 g/m² (Sappi) and Maxigloss 200 g/m²(IGEPA).

Rub resistance of the printed substrates was assessed using a PrüfbauQuartant abrasion testing instrument and a Sutherland® ink rub tester.Rub resistance tests were performed 15 minutes, 1 hour, 2 hours and 24hours after printing. The results of the rub resistance tests are shownin Table 11.

TABLE 11 Comparison of the time evolution of the rub resistance ofcomparative sheetfed printing inks and increased NAD-containing inks.Average Rub Resistance Examples 9 to 12 Examples 13 to 16 Time afterprinting (10 wt % NAD) (25 wt %-30 wt % NAD) 15 minutes 1.75 0.55  1hour 1.45 0.4  2 hour 1.45 0.1 24 hour 0.75 0.75 Rub resistance ratedfrom 0 = no rub off; to 5 = severe rub off

The results in Table 11 demonstrate that the sheetfed printing inkcompositions provided herein containing a preferred amount of NAD and nodrier or anti-oxidant (sheetfed printing inks of Examples 13 to 16)exhibit rub resistance values equal to or better than comparative inksthat contain drier or anti-oxidant (sheetfed printing inks of Examples 9to 12) very soon after printing (15 minutes) as well as after 1, 2 and24 hours.

Since sheetfed printing inks of Examples 13 to 16 (containing from 25 wt% to 30 wt % NAD based on the weight of the ink composition but no driernor anti-oxidant) exhibit good rub resistance 15 minutes after printingusing a sheetfed lithographic printing process and at subsequent timeintervals, it is evident that sheetfed printing inks can be formulatedwithout drier while still quickly exhibiting good drying properties,provided sufficient NAD is incorporated into the formula. In theexemplary sheetfed printing ink compositions, sheetfed printing inkscontaining from 25 wt % to about 30 wt % NAD based on the weight of theink composition can be formulated without drier that quickly exhibitvery good drying properties.

Examples 17-24

Heatset Printing Ink Preparation

Examples 17 to 24 describe the formulation and preparation of severalheatset printing ink compositions. The formulations for heatset printinginks of Examples 17 to 22 are shown in Table 12. Example 17 is acomparative ink that contains no NAD. The heatset printing inkcompositions were prepared by weighing all the raw materials togetherand mixing them at 3000 rpm for 2 minutes with a Speedmixer™ DAC 150 FVZfrom Hauschild. A homogeneous mixture was obtained.

TABLE 12 Magenta ink formulations. Example 17 Example Example ExampleExample Example Component (comparative) 18 19 20 21 22 Magenta base34.00 34.00 34.00 34.00 34.00 34.00 ^(a)Rosin resin 49.50 42.50 35.0028.50 20.50 11.50 varnish Mineral oil 12.00 9.00 6.50 3.00 1.00^(b)Anti-oxidant 0.50 0.50 0.50 0.50 0.50 0.50 Wax paste 4.00 4.00 4.004.00 4.00 4.00 NAD (table 4) 0 10.00 20.00 30.00 40.00 50.00 wt % 100.00100.00 100.00 100.00 100.00 100.00 ^(a)Rosin resin varnish contains51.5% rosin resin; 45.6% mineral oil; 5% linseed oil; 0.9% aluminumchelate based on the weight of the varnish. ^(b)BHT.

The heatset printing ink compositions of Examples 17 to 22 used flushpigment although dry grind pigments also could have been used. In orderto introduce up to 50 wt % NAD based on the weight of the inkcomposition, the amounts of rosin resin varnish and mineral oil wereboth, in parallel, reduced in order to yield a comparable high shearviscosity for all of the different heatset printing inks. All theheatset printing ink compositions were adjusted to a similar high shearviscosity range so that differences observed amongst the heatsetprinting ink compositions cannot be attributed to any high shearviscosity difference.

Heatset Lithographic Printing Press Trials

Proof prints were printed in the lab using a Prüfbau device that wasequipped with a small heatset oven that simulates the drying using in aheatset lithographic printing process. The temperature of the printedsubstrate, such as paper, could be adjusted and controlled at the end ofthe oven by use of an IR thermometer that measured the papertemperature. Heatset printing inks were printed on a low weight coatedstock Bavaria 70 g/m² from Papier Union at 1.3 g/m².

Rub resistance testings of prints were performed on 2 different devices:the Sutherland® ink rub tester and a Prüfbau Quartant abrasion testinginstrument. For the Sutherland® ink rub resistance tests, the printedsheet was fixed to the moving device whereas the plain Maxigloss 200g/m² from IGEPA was fixed to the still surface. Fifty strikes wereperformed using a 910 g weight. For the Prübau Quartant tests, theprinted paper was fixed to the still surface whereas the plain paperAPCO II from Scheufelen was fixed to the moving device. Thirty strikeswere performed.

The testing on both devices was performed at room temperature andresults were evaluated visually on a scale of 0-10, with 0 representingno rub-off, 5 representing moderate rub-off, and 10 representing verysevere rub-off.

Rub resistance tests were performed at 1 minute after printing tosimulate the immediate rub resistance and at 24 hours after printing toevaluate the final rub resistance of the prints. In these tests, theprinted paper was not dried in an oven. The rub resistance results areshown in Table 13. An average rub resistance value of 4 is considered bymany print customers to be trouble-free.

TABLE 13 Influence of the introduction of 10% NAD on rub resistance 1minute after printing when printed sheets were not dried through theoven. Example 17 Example Rub Resistance Test (comparative) 18 wt % NAD 010 Sutherland rub mark 8 9 Prufbau rub mark 8 6 Average rub mark 8 7.5

The comparison of the rub resistance values 1 minute after printingwithout oven drying between the comparative heatset printing ink ofExample 17, a heatset printing ink containing no NAD, and the heatsetprinting ink composition of Example 18 containing 10 wt % NAD based onthe weight of the ink composition, demonstrated that NAD, at levels of10 wt % based on the weight of the ink composition, improves the shortterm rub resistances when a printed heatset printing ink is not dried bypassing through an oven.

The influence of increasing the amount of NAD in a heatset printing inkcomposition on the rub resistance of the printed ink is shown in Table14. Although the rub resistance improvement observed in Table 13 for aheatset printing ink composition containing 10 wt % NAD was somewhatlimited in comparison to the ink without NAD, the data in Table 14demonstrates that increasing the amount of NAD in the heatset printingink composition results in increasing improvements in the rub resistanceafter 1 minute when the printed substrate does not go through the oven.

TABLE 14 Influence of 0 wt % to 50 wt % NAD on rub resistance of heatsetprinting inks 1 minute after printing when printed sheets were not driedthrough the oven. Example 17 Example Example Example Example Example RubResistance Test (comparative) 18 19 20 21 22 wt % NAD 0 10 20 30 40 50Sutherland rub mark 8 9 8 7 5 5 Prufbau rub mark 8 6 5 5 3 3 Average rubmark 8 7.5 6.5 6 4 4

As the amount of NAD was increased from 10 wt % based on the weight ofthe ink composition in the heatset printing ink composition of Example18 to 50 wt % based on the weight of the ink composition in the heatsetprinting ink composition of Example 22, the rub resistance of theprinted substrate made using the heatset printing inks was continuouslyimproved. For the heatset printing ink compositions, little improvementin rub resistance was observed between the heatset printing inkcomposition of Example 21, containing 40 wt % NAD based on the weight ofthe ink composition, and the ink of Example 22, containing 50 wt % NADbased on the weight of the ink composition. From these results, it canbe concluded for the tested heatset printing ink compositions that 40 wt% NAD based on the weight of the ink composition provides an optimum rubresistance 1 minute after printing when the printed substrate is notsubjected to an external energy such as passing through an oven (orpassing through an oven that is turned off).

Samples printed with heatset printing ink compositions of Example 17 andExample 18 were thermally treated by passing the printed substratesthrough the oven under standard conditions (paper temperature=100° C. atthe exit of the oven). The results are shown in Table 15.

TABLE 15 Influence of 10 wt % NAD based on the weight of the inkcomposition on rub resistance 1 minute after printing when printedsheets achieved a temperature of 100° C. at the exit of the oven.Example 17 Example Rub Resistance Test (comparative) 18 wt % NAD 0 10Sutherland rub mark 4 5 Prufbau rub mark 4 3 Average rub mark 4 4The data in Table 15 demonstrate that the heatset printing ink ofExample 18 containing 10 wt % NAD based on the weight of the inkcomposition has a rub resistance similar to the comparative heatsetprinting ink of Example 14 containing no NAD when the printed samplesare heat treated in an oven using conventional processing conditions.

The effect of heat treatment on heatset printing ink compositionscontaining increasing amounts of NAD also was tested. Substrates printedwith heatset printing ink compositions of Examples 17 to 22 werethermally treated by passing the printed substrates through the ovenunder standard conditions (paper temperature=100° C. at the exit of theoven). The results are shown in Table 16.

TABLE 16 Influence of the introduction of 10 wt % to 50 wt % NAD basedon the weight of the ink composition on rub resistance 1 minute afterprinting when printed sheets achieved a temperature of 100° C. at theexit of the oven. Example 17 Example Example Example Example Example RubResistance Test (comparative) 18 19 20 21 22 wt % NAD 0 10 20 30 40 50Sutherland rub mark 4 5 5 5 5 3 Prufbau rub mark 4 3 4 3 2 2 Average rubmark 4 4 4.5 4 3.5 2.5The data in Table 16 demonstrate that when the heatset printing inkscontaining NAD are dried through the oven, heatset printing inkscontaining NAD below 30 wt % based on the weight of the ink compositionexhibit a very similar rub resistance. As the amount of NAD in theheatset printing ink is increased, for example, in amounts greater than30 wt % NAD based on the weight of the ink composition, the rubresistance of the heatset printing ink composition on the printedsubstrate after 1 minute is improved in comparison to the comparativeheatset printing ink of Example 17 containing no NAD.

For illustration, the importance of exposure of a traditional heatsetprinting ink composition to external energy to set and dry the ink wasdemonstrated. A printed substrate printed with a heatset printing inkcomposition containing no NAD (comparative heatset printing ink ofExample 17) and a substrate printed with a heatset printing inkcomposition containing NAD (heatset printing ink of Example 21,containing 40 wt % NAD based on the weight of the ink composition) werecompared before exposing the printed substrate to external energy (e.g.,passing through an oven) and after exposing the printed substrate toexternal energy. The results are shown in Table 17.

TABLE 17 Comparison of rub resistances 1 minute after printing of aconventional heatset printing ink containing no NAD (Example 17) and anNAD containing ink (Example 21, 40 wt % NAD). Both inks were driedeither without oven or by passing through an oven to achieve a papertemperature of 100° C. at the exit of the oven. Rub Resistance TestExample Paper T at Exit of (Performed at 17 Example the Oven (° C.) RoomTemp.) (comparative) 21 Without oven Sutherland rub mark 8 5 T = 23° C.Prufbau rub mark 8 3 Average rub mark 8 4 With oven Sutherland rub mark4 5 T = 100° C. Prufbau rub mark 4 3 Average rub mark 4 4

The data of Table 17 illustrate the dependence of conventional heatsetprinting inks to energy exposure, such as to heat in an oven, in orderto set and dry, as exhibited by rub resistance. For the comparativeheatset printing ink of Example 17, which contains no NAD, the rubresistance after 1 minute is significantly improved when the printedsheet is exposed to thermal energy by heating in the oven. Sheetsprinted with the heatset printing ink containing NAD (heatset printingink of Example 21), however, exhibit a similar rub resistance whether ornot the printed substrate is exposed to thermal energy by passingthrough the oven. For the tested heatset printing ink compositions, theaverage value of the rub resistance after 1 minute for the substrateprinted with the heatset printing ink composition of Example 21(containing NAD) without energy exposure (no oven treatment) is equal tothe rub resistance of the conventional heatset printing ink with energyexposure (with oven treatment).

The 1 minute rub resistance values obtained for substrates printed withheatset printing ink compositions of Examples 17 to 22 are provided inTable 18. As demonstrated by the data, a continuous improvement of therub resistance values without oven treatment is observed in the neatestprinting ink compositions of Examples 18 to 22. For the tested heatsetprinting ink compositions containing NAD, immediate rub resistancecomparable to that obtained in the comparative heatset printing ink ofExample 17 when dried through an oven can be achieved without heattreatment by including 30 wt % to 50 wt % NAD based on the weight of theink composition. Thus, exemplary heatset printing ink compositionscontaining at least 30 wt % NAD based on the weight of the inkcomposition can be formulated to eliminate the need for application ofexternal energy to set and dry the ink and thus to eliminate ovens or IRor UV dryers.

TABLE 18 Rub resistance measurements performed 1 minute after printing.Paper T at End of Rub Test Example the Oven (° C.) (performed at room T)17 18 19 20 21 22 Without oven Sutherland rub 8 9 8 7 5 5 T = 23° C.mark Prufbau rub mark 8 6 5 5 3 3 Average rub mark 8 7.5 6.5 6 4 4 Withoven Sutherland rub 4 5 5 5 5 3 T = 100° C. mark Prufbau rub mark 4 3 43 2 2 Average rub mark 4 4 4.5 4 3.5 2.5For the heatset printing ink compositions of Examples 18 to 20, theimprovement of rub resistance may not be sufficient to completely turnoff the oven. In view of the improvement in set and apparent dryness(improved rub resistance), the amount of external energy required to drythe heatset printing ink compositions of Examples 18 to 20 likely isreduced, and thus heatset printing ink compositions containing from 10wt % to 30 wt % NAD based on the weight of the ink composition couldallow the printer to reduce its oven temperature, thereby reducing theenergy consumption required to set and dry the printed substrate.

Heatset printing ink compositions containing NAD, particularlycontaining greater than 30 wt % NAD, such as at least 40 wt % NAD basedon the weight of the ink composition, when printed on a substrate understandard conditions (when dried using an oven) demonstrated improvedimmediate rub resistance when compared to a control heatset printing inkcontaining no NAD. These results are shown in Table 19.

TABLE 19 Comparison of the time evolution of the rub resistance of aconventional heatset printing ink and a heatset ink with NAD. The inksdid not go through the oven. Example Time After Rub Test 17 ExamplePrinting (Performed at Room T) (comparative) 21  1 minute Sutherland rubmark 8 5 Prufbau rub mark 8 3 Average rub mark 8 4 24 hours Sutherlandrub mark 4 4 Prufbau rub mark 2 3 Average rub mark 3 3.5

The data in Table 19 demonstrates that the printed ink of the heatsetprinting ink composition of Example 21 containing NAD quickly exhibitsan excellent rub resistance. As shown, in 1 minute after printing, theheatset printing ink composition of Example 21 already achieved almostthe same rub resistance value in 1 minute as is exhibited after 24 hourswithout application of external energy (e.g., drying in an oven).Without the oven treatment, the comparative ink that contains no NAD(Example 17) has at the very beginning (1 minute) a very poor rubresistance that slowly improves as the solvent evaporates and isabsorbed by the substrate. After 24 hours, the comparative ink thatcontains no NAD (Example 17) finally exhibits a good rub resistance.

In order to demonstrate that the improvements in setting and drying, asexhibited by improved rub resistance, was valid for heatset printinginks containing pigments other than magenta, additional trials wereperformed using heatset printing ink formulations containing cyanpigment. The comparative heatset printing ink composition of Example 23contains no NAD and the heatset printing ink composition of Example 24contains about 30 wt % NAD based on the weight of the ink composition.The formulations of the cyan heatset printing ink compositions are shownin Table 20.

TABLE 20 Cyan ink formulation. Example 23 Component (comparative)Example 24 Cyan base 27.60 27.60 Clay base 4.50 4.50 ^(a)Rosin resinvarnish 49.20 24.50 Alkyd resin 2.50 2.50 Wax paste 4.10 4.10 Emulsifier4.40 4.40 NAD 0.00 30.00 ^(b)Mineral solvent 7.20 0 ^(c)Anti-oxidant(BHT) 0.50 0.50 Total Weight (% Recipe) 100.00 98.10 ^(a)Rosin resinvarnish contains 51.5 wt % rosin resin; 45.6 wt % mineral oil; 5 wt %linseed oil; 0.9 wt % aluminum chelate based on the weight of thevarnish. ^(b)Mineral oil.

The heatset printing ink compositions of comparative Example 23 andExample 24 containing NAD were prepared by the same process as describedabove, replacing the magenta pigment with a cyan pigment. In order toinclude 30 wt % of NAD into the heatset printing ink composition ofExample 24, the amounts of rosin resin varnish and mineral oil in thecompositions were reduced in order to provide an ink with a comparablehigh shear viscosity.

Proof prints were printed in the lab using a Prüfbau device that wasequipped with a small heatset oven that simulates the drying using in aheatset lithographic printing process. The heatset printing inks wereprinted on a low weight coated stock Bavaria 70 g/m² from Papier Unionat 1.3 g/m². Rub resistance testings of prints were performed asdescribed above at 1 minute and 24 hours after printing. The 1 minuterub resistance values obtained for substrates printed with heatsetprinting ink compositions of Examples 23 and 24 are provided in Table21.

TABLE 21 Influence of 30 wt % NAD in a Cyan heatset printing ink on therub resistances after 1 minute. For both inks the oven was either turnedoff or set in order to get a paper Temperature of 100° C. at the exit ofthe oven. Rub Test Example 23 Paper T at the exit (performed 0% NADExample 24 of the oven (° C.) at room T) (comparative) 30% NAD Withoutoven Sutherland rub mark 8 6 T = 23° C. Prufbau rub mark 8 6 Average rubmark 8 6 With oven Sutherland rub mark 3 4 T = 100° C. Prufbau rub mark2 2 Average rub mark 2.5 3

The results presented in Table 21 are similar to the results observed inprints prepared using heatset printing inks containing magenta pigment.The ink of Example 24 containing 30 wt % NAD based on the weight of theink composition exhibits a similar rub resistance improvement incomparison to the comparative heatset printing ink of Example 23(containing no NAD) as was observed in similar inks containing magentapigment. Because the rub resistance values are similar for cyan inks andmagenta inks, it can be concluded that the color of the pigment selecteddoes not negatively impact the improvements observed when NAD is addedto a heatset printing ink composition. It also is expected thatincreasing the amount of NAD in the heatset printing ink compositions aswas done for ink compositions containing magenta pigment also woulddemonstrate a rub resistance similar to that exhibited by substratesprinted using the heatset printing ink composition of Example 24 whendried through the oven. Once dried through the oven, both heatsetprinting inks exhibited a similar rub resistance. Because the resultsfor cyan pigment-containing formulations were so similar to magentapigment-containing formulations, it is expected that the observedresults that adding NAD to a heatset printing ink increases rapidsetting and drying can be extrapolated to pigments of the other colors.

Examples 25-27

Coldset Lithographic Printing Ink Preparation

Examples 25 to 27 describe the formulation and preparation of severalcoldset printing ink compositions. The comparative coldset printing inkof Example 25 contains no NAD. The coldset printing ink composition ofExample 26 contains about 10 wt % NAD based on the weight of the inkcomposition. The coldset printing ink composition of Example 27 includesabout 25 wt % NAD based on the weight of the ink composition. Theformulations for coldset printing inks of Examples 25 to 27 are providedin Table 22.

TABLE 22 Coldset cyan ink formulation. Example 25 Example Example(comparative) 26 27 MB A Pigment Blue 15:3 12.00 12.00 12.00 B ^(a)Rosinresin varnish 30.50 30.50 30.50 C Alkyd 5.00 5.00 5.00 D Mineral oil5.00 5.00 5.00 E Kaolin 2.00 2.00 2.00 LD F ^(b)Rosin resin varnish11.50 6.50 G Mineral oil 12.00 8.50 2.00 H Organoclay 2.00 2.00 2.00 L^(c)Extender paste 16.50 16.50 16.50 I ^(d)Anti-oxidant 1.00 1.00 1.00solution (BHT) J NAD (table 4) 0 10.00 25.00 Total (% Recipe) 97.5099.00 101.00 ^(a)Varnish contains 47.5 wt % rosin resin; 31.5 wt %mineral oil; 20.8 wt % soybean oil and 0.2 wt % AO solution (BHT) basedon the weight of the varnish. ^(b)Varnish contains 39.5 wt % rosinresin; 46.5 wt % Exx-Print T82A; 13.8 wt % soybean oil and 0.2 wt % AOsolution (BHT) based on the weight of the varnish. ^(c)Extender pastecontains 60 wt % coated calcium carbonate, 4.5 wt % vegetable oil hybridresin and 35.5 wt % mineral oil based on the weight of the extenderpaste.

The coldset printing ink compositions were prepared by mixingingredients A, B, C, D and E altogether for 2 minutes at 3000 rpm with aSpeedmixer™ DAC 150 FVZ from Hauschild. The mill base (MB) obtained thenwas passed over a three roller mill until obtaining a grain sizemeasured on a NPIRI grind gauge below 20 μm or most preferably below 10μm. Finally the letdown ingredients (LD) F, G, H, I, J and optionally Lwere added to the mill base. The resulting mixture was homogenized bymixing all the ingredients together for 2 minutes at 3000 rpm with theSpeedmixer. Mineral oils optionally could be added in order to get asimilar high shear viscosity for all inks so that the differenceobserved during the following examples cannot be attributed to adifferent high shear viscosity.

Coldset Lithographic Printing Press Trials

Proof prints were performed in the lab using a Prüfbau device. Coldsetprinting inks were printed on 2 different stocks: an uncoated paper(Newsprint 45 g/m² from Stora Enso) and a low weight coated paper(Bavaria 70 g/m² from Papier Union). Both papers were printed at asimilar optical density of 1+/−0.05 measured with a spectrophotometerDatacolor/Sphere.

Rub resistance testings of the proof prints were performed on a PrüfbauQuartant abrasion testing instrument 15 minutes and 24 hours afterprinting. The printed paper was fixed to the still surface whereas thesimilar plain paper was fixed to the moving device. To evaluate the rubresistance of the different inks, 100 strikes were performed andassessed by measuring the Delta E CMC between the plain paper before andafter the 100 strikes. A correlation exists between the value observedfor Delta E CMC and rub resistance: the lower the Delta E CMC value, thebetter the rub resistance of the printed ink. A Delta E CMC value below4 could be considered as acceptable because coldset printing inks havinga Delta E CMC value below 4 generally are regarded by many customers asbeing trouble-free with respect to rub resistance.

The results of the rub resistance testing performed 15 minutes afterprinting the coldset printing ink composition on uncoated paper areprovided in Table 23.

TABLE 23 Results of the rub resistance performed after 15 minutes onuncoated paper Newsprint 45 g/m² from Stora Enso. Example 25 ExampleExample (comparative) 26 27 wt % NAD 0 10 25 Delta E CMC after 100strikes 6.4 3.12 3.18 on Prufbau Quartant Abrasion Testing Instrument

The coldset printing ink composition of Examples 26, which contain 10 wt% NAD based on the weight of the ink composition, and the coldsetprinting ink composition of Example 27, which contains 30 wt % NAD basedon the weight of the ink composition, exhibit a significant decrease ofthe Delta E CMC, which directly can be correlated to a better rubresistance. The substrates printed with the coldset printing inkcompositions of Examples 26 and 27 have a rub resistance value of lessthan 4, indicative that the coldset printing ink compositions would beexpected to be acceptable to most print customers. The comparativecoldset printing ink of Example 25 containing no NAD had a rubresistance value of greater than 4, indicative that the comparativecoldset printing ink without NAD would be expected to be rejected bymost print customers for poor rub resistance. The coldset printing inkcompositions of Examples 26 and 27 exhibit very similar acceptable rubresistance values shortly after printing using a coldset lithographicprinting process and demonstrate that set and rub resistance quickly isattained on uncoated paper using coldset printing ink compositionscontaining NAD.

After 24 hours, the print samples of the comparative coldset ink ofExample 25 and the coldset printing ink compositions of Examples 26 and27 containing NAD printed on uncoated paper were tested for rubresistance. The data is provided in Table 24.

TABLE 24 Results of the rub resistance performed after 24 hours onuncoated paper Newsprint 45 g/m² from Stora Enso. Example 25 ExampleExample (comparative) 26 27 wt % NAD 0 10 25 Delta E CMC after 100Strikes 3.13 3.84 2.39 on Prufbau Quartant Abrasion Testing Instrument

After 24 hours, the rub resistance value of the comparative coldsetprinting ink of Example 25, containing no NAD, is significantly improvedin comparison to the rub test performed 15 minutes after printing (seeTable 23). Although the coldset printing ink composition of Example 26exhibits a slightly worse rub resistance at 24 hours when compared tothe rub resistance value obtained 15 minutes after printing, the Delta ECMC remains below 4 and should, therefore, still be accepted bycustomers. The coldset printing ink composition of Example 27, whichcontains 30 wt % of NAD based on the weight of the ink composition,exhibits the best rub resistance after 24 hours on uncoated paper,yielding a rub resistance value of 2.39.

The kinetics in forming a rub resistant ink film using coldset printinginks was determined. The rub resistance of the comparative coldsetprinting ink of Example 25 (containing no NAD) and the rub resistance ofthe coldset printing ink composition of Example 27 (containing 25 wt %NAD based on the weight of the ink composition) was compared over time.It was observed that the speed at which a rub resistant ink film isproduced on a printed uncoated paper substrate is significantlyincreased by the introduction of NAD in a coldset printing ink.Exemplary data is provided in Table 25.

TABLE 25 Comparison of the rub resistance of a substrate printed withthe coldset printing ink of Example 25 (no NAD) after 24 hours to therub resistance after 15 minutes of a substrate printed with the coldsetprinting ink composition of Example 27 (25 wt % NAD based on the weightof the ink composition). Example 25 after 24 hr Example (comparative) 27after 15 min wt % NAD 0 25 Delta E CMC after 100 Strikes 3.13 3.18 onPrufbau Quartant Abrasion Testing Instrument

The data in Table 25 demonstrate that the substrate printed with thecoldset printing ink composition containing NAD (Example 27) has a rubresistance 15 minutes after printing that is similar to the rubresistance obtained using a comparative ink (without NAD) after 24hours. Thus, addition of NAD to a coldset printing ink can significantlyincrease the speed with which a printed ink sets and attains rubresistance.

Paper Types

Coldset printing inks generally only can be printed on porous paper,since the coldset printing inks dry by absorption of the solvents intothe paper substrate. Traditional coldset printing inks generally cannotbe printed on super calendered or coated papers because the pore size orcoating minimizes or prevents adequate absorption of the solvents intothe substrate. To demonstrate that coldset printing ink compositionscontaining NAD can be printed on various paper types using a coldsetlithographic printing process, coldset printing inks were printed onsuper calendered and low weight coated paper.

Super Calendered Paper

The coldset printing ink compositions of Examples 25 to 27 were printedon super calendered and coated paper to determine the effect of additionof NAD on printability of coldset printing ink compositions on differentpaper substrates. The results for the rub resistance of the coldsetprinting ink formulations printed on super calendered paper are providedin Tables 26 and 27. Table 26 provides the results of rub resistancetesting performed 15 minutes after printing the ink compositions onsuper calendered paper (Publipress 64 g/m² from Stora Enso).

TABLE 26 Results of the rub resistance performed after 15 minutes onsuper calendered paper Publipress 64 g/m² from Stora Enso. Example 25Example Example (comparative) 26 27 wt % NAD 0 10 25 Delta E CMC after100 Strikes 5.42 3.94 3.27 on Prufbau Quartant Abrasion TestingInstrument

The data indicate that adding NAD to a coldset printing ink compositionenhances short term rub resistance on super calendered paper, whichtypically cannot be printed with standard coldset printing inks. The rubresistance values obtained 15 minutes after printing show that thecomparative coldset printing inks containing no NAD have a Delta E CMCvalue well above 4 and, therefore, likely would be rejected by customersdue to poor rub resistance. The rub resistance values obtained 15minutes after printing show that the coldset printing inks containingNAD have a Delta E CMC value below 4 and, therefore, should be acceptedby customers. Thus, coldset printing ink compositions containing atleast 10 wt % NAD based on the weight of the ink composition can be usedto print on super calendered paper as evidenced by the exhibited shortterm rub resistance of the printed inks.

The coldset printing ink composition of Example 27 containing 25 wt %NAD based on the weight of the ink composition exhibits an increasingimprovement in rub resistance when compared to the ink composition ofExample 26, which contains only 10 wt % NAD based on the weight of theink composition. The trend of the data suggests that increasing theamount of the NAD in the coldset printing ink composition would yieldincreasing improvements in rub resistance on this substrate.Accordingly, coldset printing ink compositions containing NADdemonstrate rub resistance on a super calendered paper within 15 minutesof printing on this substrate.

Table 27 provides the results of rub resistance testing performed 24hours after printing the ink compositions on super calendered paper(Publipress 64 g/m² from Stora Enso).

TABLE 27 Results of the rub resistance performed after 24 hours on supercalendered paper Publipress 64 g/m² from Stora Enso. Example 25 ExampleExample (comparative) 26 27 wt % NAD 0 10 25 Delta E CMC after 100Strikes 20.66 16.56 3.68 on Prufbau Quartant Abrasion Testing Instrument

The data indicate that the comparative coldset printing ink of Example25, which contains no NAD, exhibits, on super calendered paper, a verypoor rub resistance after 24 hours. The coldset printing ink compositionof Example 26, which contains 10 wt % of NAD based on the weight of theink composition, exhibits improvement in rub resistance when compared tothe comparative coldset printing ink containing no NAD (Example 25). Thecoldset printing ink composition of Example 27, containing 25 wt % ofNAD based on the weight of the ink composition, exhibits a significantimprovement in rub resistance compared to the conventional coldsetprinting ink (Example 25). For the sample printed with the coldsetprinting ink of Example 27, the Delta E CMC was below the critical valueof 4. Hence, the data indicate that it should be possible to run such anink on super calendered paper using a coldset lithographic printingprocess. The sample printed with the coldset printing ink composition ofExample 27 containing 25 wt % NAD based on the weight of the inkcomposition exhibits an increasing improvement in rub resistance whencompared to the sample printed with the coldset printing ink compositionof Example 26, which contains only 10 wt % NAD based on the weight ofthe ink composition. Therefore, the trend of the data suggests thatincreasing the amount of the NAD in the exemplary coldset printing inkcomposition yields increasing improvements in rub resistance of thisformulation on this substrate. Accordingly, coldset printing inkcompositions containing NAD would be expected to be able to be used toprint on super calendered paper using a coldset lithographic printingprocess.

Low Weight Coated Paper

The coldset printing ink compositions of Examples 25 to 27 also wereprinted on low weight coated paper to determine the effect of additionof NAD on printability on this paper substrate. The results for the rubresistance of the coldset printing ink formulations printed on lowweight coated paper are provided in Table 28. Table 28 provides theresults of rub resistance testing performed 15 minutes after printingthe ink compositions on low weight coated paper (Bavaria 70 g/m² fromPapier Union).

TABLE 28 Results of the rub resistance performed after 15 minutes on lowweight coated paper (Bavaria 70 g/m² from Papier Union). Example 25Example Example (comparative) 26 27 wt % NAD 0 10 25 Delta E CMC after100 Strikes 23.18 16.88 4.99 on a Prufbau Quartant Abrasion TestingInstrument

The rub resistance data indicate that substrate printed with thecomparative coldset printing ink of Example 25, which contains no NAD,exhibits, on low weight coated paper, a very poor rub resistance after15 minutes. The substrate printed with the exemplary coldset printingink composition of Example 26, which contains 10 wt % NAD based on theweight of the ink composition, exhibits improvement in rub resistancewhen compared to the rub resistance of the comparative coldset printingink containing no NAD (Example 25). The substrate printed with thecoldset printing ink composition of Example 27, which contains 25 wt %NAD based on the weight of the ink composition, exhibits a significantimprovement in rub resistance compared to the comparative coldsetprinting ink containing no NAD (Example 25). For the exemplary sampleprinted with the coldset ink of Example 27, the Delta E CMC wasapproaching the critical value of 4.

The coldset printing ink composition of Example 27, which contains 25 wt% of NAD based on the weight of the ink composition, exhibits anincreasing improvement in short term rub resistance when compared to thecoldset printing ink composition of Example 26, which contains only 10wt % NAD based on the weight of the ink composition. The trend of thedata suggests that increasing the amount of the NAD in the coldsetprinting ink composition would yield increasing improvements in rubresistance on low weight coated paper.

The present invention has been described in detail, including thepreferred embodiments thereof, but is more broadly applicable as will beunderstood by those skilled in the art. It will be appreciated thatthose skilled in the art, upon consideration of the present disclosure,may make modifications and/or improvements on this invention that fallwithin the scope and spirit of the invention. Since modifications willbe apparent to those of skill in this art, it is intended that thisinvention be limited only by the scope of the following claims.

What is claimed is:
 1. A lithographic printing ink comprising from 15 to60 wt % of a non-aqueous dispersion (NAD) of an acrylic core/shellpolymer, comprising: an acrylic shell polymer; an acrylic core polymer;and a continuous phase of an essentially non-aqueous solvent.
 2. Thelithographic printing ink of claim 1, wherein the NAD is in an amountthat is 20 wt % to 35 wt. % based on the weight of the printing ink or25 wt % to 35 wt % based on the weight of the printing ink.
 3. Thelithographic printing ink of claim 1, wherein the acrylic shell polymeris soluble in the continuous phase of the essentially non-aqueoussolvent; and the acrylic core polymer is insoluble in the continuousphase of the essentially non-aqueous solvent but is soluble in theacrylic shell polymer.
 4. The lithographic printing ink of claim 1,wherein the continuous phase of essentially non-aqueous solvent contains0.001 wt % to 1.0 wt % water based on the weight of the dispersion. 5.The lithographic printing ink of claim 1, wherein the (NAD) comprises arheology adjusting component containing water, a C₁-C₆ alcohol, a metalhydroxide, an alkyl amine and/or a primary amine, a secondary amine,tertiary amine or a combination thereof.
 6. The lithographic printingink of claim 1, which is a sheetfed offset printing ink.
 7. Thelithographic printing ink of claim 1, which is a heat offset printingink.
 8. The lithographic printing ink of claim 1, which is a coldsetoffset printing ink.
 9. The lithographic printing ink of claim 6,wherein the sheetfed offset printing ink does not contain metal drier ormetal catalyst.
 10. The lithographic printing ink of claim 7, whereinthe rheology adjusting component contains a mixture of water, potassiumhydroxide, isopropanol and diethylamine.
 11. The lithographic printingink of claim 8, wherein the rheology adjusting component is present inan amount from 0.01 wt % to 2.0 wt % based on the weight of thedispersion.
 12. The lithographic printing ink of claim 1, wherein thecontinuous phase essentially non-aqueous solvent has a sulfur content ator below 1000 ppm.
 13. The lithographic printing ink of claim 1, whereinthe continuous phase essentially non-aqueous solvent has an anilinepoint between 45° C. and 90° C.
 14. The lithographic printing ink ofclaim 1, wherein the acrylic shell polymer contains isobutylmethacrylate and dodecyl methacrylate.
 15. The lithographic printing inkclaim 1, wherein the acrylic core polymer contains methylmethacrylateand N-butyl methacrylate.
 16. The lithographic printing ink of claim 1,wherein 90% of the acrylic core/shell polymer particles have a particlesize of less than 3 microns.
 17. The lithographic printing ink of claim1, wherein at least 50% of the acrylic core/shell polymer particles havea particle size of less than 1.5 microns.
 18. The lithographic printingink of claim 1, wherein the average particle size of the acryliccore/shell polymer particles is in the range of 300 nm to 1300 nm. 19.The lithographic printing ink of claim 1, wherein the acrylic core/shellpolymer particles contain from 15 wt % to 75 wt % acrylic core polymerbased on the weight of the acrylic core/shell polymer particle.
 20. Thelithographic printing ink of claim 1, wherein the acrylic core/shellpolymer particles contain from 15 wt % to 75 wt % acrylic shell polymerbased on the weight of the acrylic core/shell polymer particle.
 21. Thelithographic printing ink of claim 1, wherein the acrylic core/shellpolymer particles have an average core-to-shell ratio of from 0.60 to2.0.
 22. The lithographic printing ink of claim 1, wherein the amount ofacrylic core polymer in the dispersion is from 15 wt % to 35 wt % basedon the weight of the dispersion.
 23. The lithographic printing ink ofclaim 1, wherein the amount of acrylic shell polymer in the dispersionis from 15 wt % to 35 wt % based on the weight of the dispersion. 24.The lithographic printing ink of claim 2, wherein the amount of acryliccore/shell polymer particles in the dispersion is from 30 wt % to 70 wt% based on the weight of the dispersion.
 25. The lithographic printingink of claim 1, wherein the amount of essentially non-aqueous solvent inthe dispersion is from 30 wt % to 70 wt % based on the weight of thedispersion.
 26. The lithographic printing ink of claim 1 having aviscosity of 10 Pa·s to 150 Pa·s at a shear rate of 50 s⁻¹.
 27. Thelithographic printing ink of claim 1 having a viscosity of 40 Pa·s to100 Pa·s at a shear rate of 50 s⁻¹.
 28. The lithographic printing ink ofclaim 1, wherein the continuous phase essentially non-aqueous solvent isa hydrocarbon solvent.
 29. The lithographic printing ink of claim 1,wherein the continuous phase essentially non-aqueous solvent is a whitemineral or a hydrotreated light naphthenic distillate.
 30. Thelithographic printing ink of claim 1, wherein the continuous phaseessentially non-aqueous solvent is a vegetable oil.
 31. The lithographicprinting ink of claim 1, wherein the continuous phase essentiallynon-aqueous solvent is a fatty acid alkyl ester.
 32. The lithographicprinting ink of claim 1, wherein the continuous phase essentiallynon-aqueous solvent is a ethyl hexyl palmitate.
 33. The lithographicprinting ink of claim 1, wherein the acrylic shell polymer and/oracrylic core polymer contain a copolymer of monomers that contain afunctional group selected from the group consisting of a carboxyl group,a hydroxyl group and a vinyl group.
 34. The lithographic printing ink ofclaim 33, wherein the monomers containing a carboxyl group are selectedfrom the group consisting of acrylic acid, methacrylic acid, itaconicacid and maleic acid.
 35. The lithographic printing ink of claim 33,wherein the monomers containing a hydroxyl group are selected from thegroup consisting of 2-hydroxy ethyl acrylate, 2-hydroxy ethylmethacrylate, 2-hydroxy propyl acrylate and 2-hydroxy propylmethacrylate.
 36. The lithographic printing ink of claim 1, wherein theNAD is in an amount that is 25 wt. % to 35 wt. % based on the weight ofthe printing ink shell polymer.